Preparation method of silicon carbide composite material

A composite material and silicon carbide technology, which is applied in the field of composite material processing, can solve the problems of material uniformity, low repeatability index of Weibull modulus, reduced machinability and application reliability, and low room temperature strength of SiC ceramics, etc., to achieve improvement Effects of quality stability and strength, increased raw material cost, and shortened degreasing cycle

Inactive Publication Date: 2017-02-08
NINGBO DONGLIAN MECHANICAL SEAL
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Although reaction sintered silicon carbide has many advantages, the room temperature strength of SiC ceramics is relatively low, and the fracture toughness is poor. Silicon is essentially a brittle material, which is prone to brittle fracture, which reduces its machinability and application reliability to a certain extent. Therefore, the preparation of SiC-based composite ceramics with high density and high strength and fracture toughness has always been an important aspect of SiC ceramics. The main direction of research development

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of silicon carbide composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031]In this embodiment, the preparation method of silicon carbide composite material comprises the following steps:

[0032] 1), the main material is passed through a 70-mesh sieve after primary ball milling in water accounting for 22% of the total main material (add 0.3 parts by weight of a dispersant and perform secondary ball milling) to obtain a finished slurry, wherein the main material includes 50 parts by weight of SiC pellets and 0.4 parts by weight B 4 C pellets, B 4 C pellets are used as sintering aids, the particle size of SiC pellets is 0.8μm, B 4 The size of the C pellets was 3.0 μm.

[0033] 2), add auxiliary materials to the finished slurry product obtained in step 1) to prepare the slurry before casting (add methylenebisacrylamide first, then adjust the pH of the slurry to 10-11 with tetramethylammonium hydroxide, and then Add ammonium polyacrylate), keep stirring when adding, wherein the auxiliary materials include acrylamide, methylenebisacrylamide, ammo...

Embodiment 2

[0039] In this embodiment, the preparation method of silicon carbide composite material comprises the following steps:

[0040] 1), the main ingredient is passed through a 65-mesh sieve after primary ball milling in water accounting for 23% of the total amount of the main ingredient (add 0.3 parts by weight of a dispersant and perform secondary ball milling) to obtain a finished slurry, wherein the main ingredient includes 48 parts by weight of SiC pellets and 0.4 parts by weight B 4 C pellets, B 4 C pellets are used as sintering aids, the particle size of SiC pellets is 0.7μm, B 4 The size of the C pellets was 3.1 μm.

[0041] 2), add auxiliary materials to the finished slurry product obtained in step 1) to prepare the slurry before casting (add methylenebisacrylamide first, then adjust the pH of the slurry to 10-11 with tetramethylammonium hydroxide, and then Add ammonium polyacrylate), keep stirring when adding, wherein the auxiliary materials include acrylamide, methyle...

Embodiment 3

[0046] In this embodiment, the preparation method of silicon carbide composite material comprises the following steps:

[0047] 1), the main ingredient is passed through a 75-mesh sieve after a ball mill in water accounting for 24% of the total amount of the main ingredient (add 0.1-0.4 parts by weight of a dispersant and carry out secondary ball milling) to obtain a finished slurry, wherein the main ingredient includes 52 wt. Parts of SiC pellets and 0.6 parts by weight of B 4 C pellets, B 4 C pellets are used as sintering aids, the particle size of SiC pellets is 0.75 μm, B 4 The size of the C pellets was 2.9 μm.

[0048] 2), add auxiliary materials to the finished slurry product obtained in step 1) to prepare the slurry before casting (add methylenebisacrylamide first, then adjust the pH of the slurry to 10-11 with tetramethylammonium hydroxide, and then Add ammonium polyacrylate), keep stirring when adding, wherein the auxiliary materials include acrylamide, methylenebi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
sizeaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a silicon carbide composite material and belongs to the technical field of composite material processing. The preparation method comprises treating main materials to obtain a slurry finished product, wherein the main materials comprise SiC particles and B4C particles as sintering aids, adding auxiliary materials into the slurry finished product to obtain slurry before casting, wherein the auxiliary materials comprise acrylamide, methylene bisacrylamide and ammonium polyacrylate, adding ammonium persulfate into the slurry before casting, carrying out uniform stirring, carrying out injection molding to obtain a blank, degreasing the blank through a solvent, carrying out hot degreasing and sintering the degreased blank under oscillation pressure at a temperature of 2000-2100 DEG C to obtain the silicon carbide composite material finished product. The silicon carbide composite material has uniform and stable structure and quality, high density, good controllability and good toughness and strength.

Description

technical field [0001] The invention relates to a method for preparing a silicon carbide composite material, belonging to the technical field of composite material processing. Background technique [0002] Silicon carbide (SiC) ceramics, as a typical covalently bonded ceramic material, has high high-temperature strength, low high-temperature creep, high hardness, wear resistance, corrosion resistance, oxidation resistance, high thermal conductivity and high electrical conductivity. With the characteristics of high efficiency and good thermal stability, it has been widely used in high-tech fields such as machinery, chemical industry, energy, and military industry. At present, most of the ceramics that have been widely used are oxide ceramics, but they have disadvantages such as poor high temperature performance and insufficient corrosion resistance, and silicon carbide ceramics can just make up for these deficiencies. In addition, many special fields put forward higher requi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/565C04B35/632C04B35/634C04B35/638C04B35/645
CPCC04B35/565C04B35/632C04B35/63404C04B35/638C04B35/645C04B2235/3821C04B2235/6022C04B2235/6562C04B2235/6567C04B2235/96
Inventor 李友宝励永平叶传剑
Owner NINGBO DONGLIAN MECHANICAL SEAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More