Method for preparing bleeding stopping oxidized celluloses in ramie oxidation degumming procedures

A technology of oxidizing cellulose and oxidizing degumming, which is applied in the fields of application, pharmaceutical formulation, and medical science, and can solve problems such as combination of other products, complex production process, waste of oxidizing solution, etc., and achieve simple process, good chemical stability, and short reaction time. The effect of shortening

Active Publication Date: 2017-03-08
DONGHUA UNIV
View PDF1 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the commercial product of oxidized cellulose clinically used as hemostatic gauze is "SURGICEL" of Johnson & Johnson, but the current form of the product is not conducive to combining with other products, and the production process is relatively complicated, the cost is high, and the price is high. Expensive, serious waste of oxidizing solution in the production process, it is urgent to develop better alternative products, exploring a better preparation process of medical hemostatic oxidized cellulose is an urgent proposition

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A method for preparing oxidized cellulose for hemostasis in the process of oxidative degumming of ramie is as follows:

[0027] The raw ramie is crushed into short fibers with a fineness of 40 meshes with a pulverizer, put into a container with a sealing ring to balance the moisture, and measure the moisture regain of the short fibers to be 9.2%. The weighed short fiber quality is 21.10g, and its fiber dry weight is calculated according to the moisture regain to be 19.16g. Add deionized water so that the mass concentration of raw hemp cellulose is 6%, soak for 48 hours, and make it fully wet. Sodium chlorate 0.4g, resorcinol 0.1g, 4-methylmorpholine-N-oxide 0.1g, polyvinyl alcohol 0.1g, aminotriacetic acid 0.1g, add 199.2g water to make degumming liquid; Raw hemp short fibers of ramie and the degumming reaction solution were mixed in a mass ratio of 1:10, and a 1000mL brown Erlenmeyer flask was used as a reactor. The pH value of the degumming solution was adjusted to ...

Embodiment 2

[0032] A method for preparing oxidized cellulose for hemostasis in the process of oxidative degumming of ramie is as follows:

[0033] The raw ramie is crushed into short fibers with a fineness of 20 meshes with a pulverizer, put into a container with a sealing ring to balance the moisture, and measure the moisture regain of the short fibers to be 9.2%. The weighed short fiber quality is 21.20g, and its fiber dry weight is calculated according to the moisture regain to be 19.25g. Add deionized water to make the mass concentration of raw hemp cellulose at 1%, and soak for 24 hours to make it fully wet. Add 1g of tetramethylpiperidine oxide-sodium hypochlorite-sodium bromide ternary composite oxidation system, 0.5g of sodium benzoate, 0.4g of urea, 0.3g of sodium dodecylsulfonate, 0.3g of sodium polyacrylate, and add 197.5g of water Prepare a degumming solution; mix the ramie raw hemp short fiber and the degumming reaction solution at a mass ratio of 1:10, and use a 1000mL brow...

Embodiment 3

[0038] A method for preparing oxidized cellulose for hemostasis in the process of oxidative degumming of ramie is as follows:

[0039] Raw ramie is crushed into short fibers with a fineness of 60 meshes with a pulverizer, put into a container with a sealing ring to balance the moisture, and measure the moisture regain of the short fibers to be 8.9%. The weighed short fiber quality is 22.02g, and its fiber dry weight is calculated according to the moisture regain to be 20.06g. Add deionized water to make the mass concentration of raw hemp cellulose at 3%, soak for 36 hours, and make it fully wet. Add 2.0g of nitric acid-phosphoric acid-sodium nitrite oxidation system, 1.0g of water glass, 0.8g of thiourea, 0.6g of sodium dodecylbenzenesulfonate, 0.6g of diethylenetriaminepentamethylenephosphonic acid, and add 195.0g of water Prepare a degumming solution; mix the ramie raw hemp short fiber and the degumming reaction solution at a mass ratio of 1:10, and use a 1000mL brown Erlen...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
crystallinityaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to view more

Abstract

The invention provides a method for preparing bleeding stopping oxidized celluloses in ramie oxidation degumming procedures. The method includes smashing raw ramie to obtain short fibers and soaking the short fibers to sufficiently moisten the short fibers and allow the short fibers to sufficiently swell; mixing the pretreated raw ramie short fibers and degumming solution with one another to obtain mixtures, heating the mixtures, then preserving heat, sufficiently removing colloid in the raw ramie by the aid of oxidability of specific oxidizing agents and simultaneously oxidizing celluloses with active hydroxyl to obtain oxidized celluloses with a large quantity of carboxyl; soaking oxidized and treated fibers by the aid of organic solvent aqueous solution and removing the unreacted oxidizing agents; separating the oxidized celluloses from water and carrying out drying treatment on the oxidized celluloses to ultimately obtain the powdery bleeding stopping oxidized celluloses. The method has the advantages that processes are simple, the original two working procedures are combined into a single working procedure, accordingly, the total reaction time can be shortened, medicines and the cost can be saved, and the efficiency can be greatly improved; the bleeding stopping oxidized celluloses which are products prepared by the aid of the method are high in bleeding stopping speed and bleeding stopping efficiency and can be widely applied to quickly stopping bleeding under conditions of war wound, trauma and the like, and stable effects can be realized.

Description

technical field [0001] The invention relates to a method for preparing oxidized cellulose for hemostasis in the oxidative degumming process of ramie, and belongs to the technical field of natural fiber preparation and application of oxidized cellulose for hemostasis in the textile field. Background technique [0002] In recent years, medical absorbable hemostatic materials have attracted great attention from the medical and industrial circles of various countries. With the improvement of performance requirements for hemostatic materials, the development of hemostatic materials with better hemostatic effect, green, environmental protection, degradable, non-toxic, no side effects, no stimulation It is imperative to develop a medical absorbable hemostatic material with high biocompatibility and good biocompatibility. At present, medical hemostatic materials mainly include fibrin glue, gelatin sponge, oxidized cellulose, microfibrous collagen, chitosan and calcium alginate fiber...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08B15/02A61L24/00A61L24/08
CPCA61L24/0042A61L24/08A61L2400/04C08B15/02C08L1/04
Inventor 李召岭沈家力丁彬俞建勇
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap