Modified anticorrosive chlorosulfonated polyethylene coating with polyaniline loaded on surfaces of zeolite molecular sieves

A technology of chlorosulfonated polyethylene and zeolite molecular sieve, which is applied to anti-corrosion coatings, fire-retardant coatings, chloroprene homopolymer coatings, etc., can solve the problem of reducing anti-corrosion performance and cannot effectively improve the comprehensive performance of chlorosulfonated polyethylene and other problems, to achieve the effect of improving quick-drying, excellent adhesion, quick-drying and anti-corrosion performance

Inactive Publication Date: 2017-04-19
闻承岳
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the addition of water-based epoxy resin, the adhesion of the coating is improved while the anti-corrosion performance is reduced, and the comprehensive performance of chlorosulfonated polyethylene cannot be effectively improved. It is necessary to further improve the water-based chlorosulfonated polyethylene coating. To meet the needs of industry development

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] A zeolite molecular sieve-modified chlorosulfonated polyethylene anti-corrosion coating loaded with polyaniline on the surface, made of the following raw materials in parts by weight (kg): chlorosulfonated polyethylene latex 60, neoprene latex 35, polyoxyethylene fatty alcohol Ether 7, appropriate amount of deionized water, silane coupling agent KH5602.5, lanthanum oxide 2, cerium oxide 1.5, an appropriate amount of nitric acid solution with a concentration of 65wt%, ammonium bicarbonate solution with a concentration of 50wt%, and rutile titanium dioxide 10 , Emulsified silicone oil 1, aniline 2, ammonium persulfate 0.1, zeolite molecular sieve 4, sodium dodecylbenzene sulfonate 0.3, an appropriate amount of ethanol.

[0015] According to claim 1, a zeolite molecular sieve-modified chlorosulfonated polyethylene anti-corrosion coating loaded with polyaniline on the surface is prepared by the following specific method:

[0016] (1) Mix chlorosulfonated polyethylene latex ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a modified anticorrosive chlorosulfonated polyethylene coating with polyaniline loaded on the surfaces of zeolite molecular sieves. The coating is made of, by weight, 60-65 parts of chlorosulfonated polyethylene latex, 35-40 parts of neoprene latex, 7-8 parts of polyoxyethylene fatty alcohol ether, an appropriate amount of deionized water, 2.5-3 parts of silane coupling agents KH560, 2-3 parts of lanthanum oxides, 1.5-2 parts of cerous oxides, an appropriate amount of nitric acid solutions with the concentration being 65wt%, an appropriate amount of ammonium bicarbonate solutions with the concentration being 50wt%, 10-12 parts of rutile titanium dioxides, 1-1.2 parts of silicone emulsion, 2-3 parts of aniline, 0.1-0.12 part of ammonium persulfate, 4-5 parts of the zeolite molecular sieves, 0.3-0.4 part of sodium dodecyl benzene sulfonate and an appropriate amount of absolute ethyl alcohol. The manufactured coating has the advantages that an technology and equipment are simple, industrial production is easy, product construction is convenient, and the adhesive force and the quick-drying performance are excellent. The coating can be used on the surface of steel body structure and chemical pipeline equipment and has good preservative effect.

Description

technical field [0001] The invention relates to the technical field, in particular to a polyaniline-loaded zeolite molecular sieve-modified chlorosulfonated polyethylene anticorrosion coating. Background technique [0002] Corrosion and anticorrosion are prominent problems in chemical industry, light industry, metallurgy, electric power, textile, printing and dyeing, shipbuilding, construction and other industries. Corrosion causes huge losses every year, so anti-corrosion work is particularly important. Chlorosulfonated polyethylene anti-corrosion coatings are widely used for their excellent corrosion resistance, especially excellent flexibility, and the price is not high. Once favored by the industry. With the rapid development of modern industrial level, higher and stricter ability to withstand environmental corrosion has been put forward for anti-corrosion coatings. The anti-corrosion performance of chlorosulfonated polyethylene coatings produced by traditional formula...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D123/34C09D111/02C09D5/18C09D5/08C09D7/12
CPCC08L2201/02C08L2205/035C09D5/08C09D5/18C09D7/62C09D7/65C09D7/70C09D123/34C08L11/02C08L71/02C08L83/04C08K13/06C08K9/12C08K3/34C08K9/06C08K2003/2213C08K2003/221
Inventor 闻承岳
Owner 闻承岳
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products