Preparing method for high abrasion resistance and high heat resistance automobile clutch surface patch

Abstract

The invention discloses a preparing method for a high abrasion resistance and high heat resistance automobile clutch surface patch. The method comprises the following steps that oxidized graphene and nano-diamond modified composite fiber cloth is immersed in nano aluminum titanate / phosphorus boron molybdenum silicon composite modified water soluble phenol-formaldehyde resin to be dipped, and after dipping is finished, the composite fiber cloth is dried in a drying tower; then, the dried composite fiber cloth is subjected to strip tearing, and winding and forming are conducted on a winding machine; a mold blank obtained after winding is arranged in a die to be subjected to hot press forming, the mold blank obtained after hot press is placed in an oven to be subjected to heat treatment, and after heat treatment is finished, a product is cut, the surface is ground, and the automobile clutch surface patch with the needed specification is manufactured. According to the preparing method, filling particles and other components are not needed, in other words, the pulp dipping step is removed in the technology, the modified composite fiber cloth is directly immersed in the modified water soluble phenol-formaldehyde resin, and then the high abrasion resistance and high heat resistance automobile clutch surface patch can be prepared. Heat treatment is adopted in the method, the method is scientific and reasonable, inner stress of products can be completely eliminated, and the mechanical performance of the products is improved.

Description

technical field [0001] The invention relates to a preparation method of an automobile clutch face, in particular to a preparation method of a highly wear-resistant and high heat-resistant automobile clutch face. Background technique [0002] The automobile clutch face is a component material that the vehicle relies on friction to perform the transmission function. It is a kind of friction material and a very important safety part in the automobile. It has an important impact on the realization of the functionality, safety and comfort of the automobile. . The commonly used automobile clutch face is mainly composed of three parts: binder, reinforcing fiber and filler particles. The role of the binder is to connect the reinforcing fiber and filler particles into a whole, that is, the clutch face product; The mechanical properties of the product ensure that the product has sufficient mechanical strength to withstand the impact force, shear force, and high-speed rotation of the ...

AI Technical Summary

Problems solved by technology

However, with the development of automobiles towards high speed, heavy load, comfort and safety, the performance requirements of clutch faces used in automobiles are getting higher and higher, which requires stronger wear resistance and better wear resistance of clutch faces. At the same time, the reinforcing fiber needs to be impregnated with slurry in the process of the above literature, which greatly increases the production strength and production cost, and the heat treatment process is unreasonable, and the internal stress of the product cannot be completely eliminated.