Automotive nylon plastic part processing technology

A nylon plastic and processing technology, applied in the field of auto parts production, can solve the problems of high temperature oxidation resistance and low corrosion resistance, and achieve the effects of good dimensional stability, strong impact resistance, and easy molding and processing

Inactive Publication Date: 2017-11-07
ANHUI CAREMIC CONSULTING CO LTD
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Chinese invention patent with application number 201310616017.5, EVA modified polyphenylene sulfide material for automotive plastic parts, which is made of the following raw materials in parts by weight: polyphenylene sulfide 100, nano-carbon 2-3, EVA12-15, polyphenylene sulfide Butylene succinate 4-6, coupling agent KH-5502-3, resorcinol tetraphenyl diphosphate 2-5, ammonium polyphosphate 1-2, zinc cyanurate 2-3, zinc oxide 3-4, alum powder 7-9, bentonite 10-12, accelerator TETD1-2, auxiliary agent 12-15; the present invention combines the advantages of polyphenylene sulfide, EVA and other raw materials, and improves the traditional polyphenylene sulfide material The performance of the obtained material has good processing performance and mechanical performance, high strength, wear resistance, easy processing and molding, but low resistance to high temperature oxidation and corrosion resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A process for processing nylon plastic parts for automobiles, the process steps are as follows:

[0024] (1) Preparation of raw materials: 100 parts of polystyrene resin, 4 parts of heat stabilizer, 5 parts of modifier, 0.5 parts of triphenyl polyphosphate, 7 parts of titanium dioxide, 3 parts of lubricant, diphthalate 10 parts of isononyl ester, 3 parts of polydihydropyridine, 7 parts of epoxy soybean oil, 15 parts of calcium carbonate powder;

[0025] (2) mix, put raw material into reaction container, under the condition of reaction temperature 250 ℃ and reaction pressure 2.5MPa, adopt zinc oxide to be catalyst;

[0026] (3) For smelting, the temperature is raised to 420° C., and the smelting is repeated, and the time is controlled at 45 minutes;

[0027] (4) into the material, the reaction product of step (3) is introduced into the polycondensation kettle, and the reaction temperature is controlled to be 370° C., carried out under high vacuum and strong stirring, to...

Embodiment 2

[0037] A process for processing nylon plastic parts for automobiles, the process steps are as follows:

[0038] (1) Preparation of raw materials: 100 parts of polystyrene resin, 5 parts of heat stabilizer, 10 parts of modifier, 0.5 parts of triphenyl polyphosphate, 9 parts of titanium dioxide, 5 parts of lubricant, diphthalate 30 parts of isononyl ester, 3 parts of polydihydropyridine, 7 parts of epoxy soybean oil, 15 parts of calcium carbonate powder;

[0039] (2) mix, put raw material into reaction container, under reaction temperature 300 ℃ and reaction pressure 2MPa condition, adopt zinc oxide as catalyst;

[0040] (3) For smelting, the temperature is raised to 580°C, and the smelting is repeated, and the time is controlled at 30 minutes;

[0041] (4) into materials, the reaction product of step (3) is introduced into the polycondensation tank, and the reaction temperature is controlled to be 380° C., carried out under high vacuum and strong stirring, to obtain high molec...

Embodiment 3

[0051] A process for processing nylon plastic parts for automobiles, the process steps are as follows:

[0052] (1) Preparation of raw materials: 100 parts of polystyrene resin, 5 parts of heat stabilizer, 8 parts of modifier, 0.5 parts of triphenyl polyphosphate, 8 parts of titanium dioxide, 4 parts of lubricant, diphthalate 20 parts of isononyl ester, 3 parts of polydihydropyridine, 7 parts of epoxy soybean oil, 15 parts of calcium carbonate powder;

[0053] (2) mix, put raw material into reaction container, under reaction temperature 275 ℃ and reaction pressure 2.3MPa condition, adopt zinc oxide to be catalyst;

[0054](3) For smelting, the temperature is raised to 500° C., and the smelting is repeated, and the time is controlled at 38 minutes;

[0055] (4) into the material, the reaction product of step (3) is introduced into the polycondensation tank, and the reaction temperature is controlled to be 375° C., carried out under high vacuum and strong stirring, to obtain hi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an automotive nylon plastic part processing technology which comprises the following process steps: (1) preparing raw materials; (2) mixing; (3) smelting; (4) molding materials; (5) modifying; (6) crystallizing and separating; and (7) cleaning the surface. The performances of high-temperature oxidation and corrosion resistance are improved, the crystallization rate is high, and the nylon plastic part is easy to mold and process and has the characteristics of high impact resistance and the like.

Description

technical field [0001] The invention relates to the field of auto parts production, in particular to a processing technology for auto nylon plastic parts. Background technique [0002] The plastic extrusion molding process in the prior art involves material distribution, stirring, granulation, and molding. Among them, the formula in the batching process selects resin, plasticizer, heat stabilizer, lubricant, filler and other additives. Because the plasticizer is relatively soft, it is easy to affect the banburying of the product during the smelting process. After molding, the continuous volatilization of the plasticizer will accelerate the aging of the product. Even if plastic products adopt secondary processing to improve the surface finish, they can only be painted and polished. Since the main component of varnish is resin and contains extremely volatile thinners, it is easy to fade and fade. The color of the product is monotonous, dull, the cost of secondary processing ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L25/06C08L27/06C08L9/06C08L85/02C08L75/14C08K13/02C08K3/22C08K5/101C08K5/12C08K5/098
CPCC08L25/06C08K2003/2241C08L2201/08C08L2205/035C08L27/06C08L9/06C08L85/02C08L75/14C08K13/02C08K3/22C08K5/101C08K5/12C08K5/098
Inventor 徐忠丁瑞
Owner ANHUI CAREMIC CONSULTING CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com