Illuminant ceramic mud composition for mud extruding process and preparation method thereof

A technology of luminescent ceramics and composites, applied in the field of ceramic materials, can solve the problems of low value, lack of fluorescence characteristics and light transmission properties, lack of individuality of ceramics, etc.

Inactive Publication Date: 2017-12-15
JINGDEZHEN CERAMIC INSTITUTE
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, ceramics printed by rapid prototyping technology lack individuality, so their value is not high, and there are no ceramics with fluorescent and light-transmitting properties on the market

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0068] Take kaolin 360g, bentonite 30g, potassium feldspar 110g, albite 70g, anorthite 80g, quartz 70g, pyrochlore 60g, fluorite 70g, talcum powder 10g, mullite 60g, waste porcelain powder 50g, Jiepai Mud 30g, sintering aid 55g and fluorescent powder 100g.

[0069] Put the above raw materials into the mixing bucket, use a mixer to mix the raw materials evenly, and stir for about five minutes. After mixing evenly, add 600g of water to the raw materials being stirred, and slowly add water while stirring, which can increase the mixing uniformity of the mud raw materials. After stirring, add 14g of plasticizer sodium humate, 8g of soluble starch, 6g of polyvinyl alcohol and 12g of carboxymethyl cellulose, and continue stirring for 3 minutes. After completion, the water content of the mud is about 26%. After the stirring is completed, add 7 g of decoagulant sodium silicate, 6 g of sodium carbonate and 12 g of tannic acid, and continue stirring until the water content is about 25%....

Embodiment 2

[0072] Embodiment 2: get kaolin 360g, bentonite 30g, potassium feldspar 110g, albite 70g, anorthite 80g, quartz 70g, pyrochlore 60g, fluorite 70g, talcum powder 10g, mullite 60g, waste porcelain powder 50g, Jiepai mud 30g, sintering aid 55g and fluorescent powder 125g. Put the above raw materials into the mixing bucket, use a mixer to mix the raw materials evenly, and stir for about five minutes. After mixing evenly, add 600g of water to the raw materials being stirred, and slowly add water while stirring, which can increase the mixing uniformity of the mud raw materials. After stirring, add 14g of plasticizer sodium humate, 8g of soluble starch, 6g of polyvinyl alcohol and 12g of carboxymethyl cellulose, and continue stirring for 5 minutes. The water content after completion is about 25%. After the stirring is completed, add 7 g of decoagulant sodium silicate, 6 g of sodium carbonate and 12 g of tannic acid, and continue stirring for 5 minutes. Finally, add 4.5g of floccula...

Embodiment 3

[0073] Embodiment 3: get kaolin 360g, bentonite 30g, potassium feldspar 110g, albite 70g, anorthite 80g, quartz 70g, pyrochlore 60g, fluorite 70g, talcum powder 10g, mullite 60g, waste porcelain powder 50g, Jiepai mud 30g, sintering aid 55g and fluorescent powder 150g. Put the above raw materials into the mixing bucket, use a mixer to mix the raw materials evenly, and stir for about five minutes. After mixing evenly, add 600g of water to the raw materials being stirred, and slowly add water while stirring, which can increase the mixing uniformity of the mud raw materials. After stirring, add 14g of plasticizer sodium humate, 8g of soluble starch, 6g of polyvinyl alcohol and 12g of carboxymethyl cellulose, and continue stirring for 3 minutes. The water content after completion is about 26%. After the stirring is completed, add 7 g of decoagulant sodium silicate, 6 g of sodium carbonate and 12 g of tannic acid, and continue stirring for 7 minutes. Finally, add 4.5g of floccula...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
luminous intensityaaaaaaaaaa
luminous intensityaaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of a ceramic material and especially relates to an illuminant ceramic mud composition for a mud extruding process. The illuminant ceramic mud composition comprises the following components in a weight ratio: kaoline, bentonite, potassium feldspar, albite, anorthite, quartz, pyrochlore, fluorite, talcum powder, mullite, waste ceramic powder, Jiepai mud, a plasticizer, a liquefaclent, a flocculant, a brightening agent, a high temperature protective agent, an anti-cracking agent, a wetting agent, a tackifier, a rare earth trichromatic phosphor, a sintering additive and water. The illuminant ceramic mud composition prepared according the formula and preparation method provided by the invention has magnificent fluorescence characteristic and light transmittance performance. The illuminant ceramic mud has higher liquidity than that of common mud, difficultly blocks a sprayer in a forming process and has higher plasticity than that of common mud, and meanwhile, a green body is difficult to deform in the forming process.

Description

technical field [0001] The invention relates to the field of ceramic materials, in particular to a luminescent ceramic mud material composition for mud extrusion and a preparation method thereof. Background technique [0002] Nowadays, individual ceramics cover a wide range. However, ceramics printed by rapid prototyping technology lack individuality, so their value is not high, and there are no ceramics with fluorescent and light-transmitting properties on the market. Contents of the invention [0003] The invention provides a luminous ceramic mud composition for mud extrusion method and a preparation method thereof, so as to solve the above-mentioned technical problems. [0004] In order to achieve the above object, the technical solution of the present invention is achieved in that: [0005] A luminescent ceramic mud composition for the mud extrusion method, by weight ratio, comprising: [0006] Kaolin 16.8-18.5% [0007] Bentonite 1.1-1.6% [0008] Potassium felds...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/13C04B33/132B33Y70/00
CPCB33Y70/00C04B33/13C04B33/131C04B33/1324C04B2235/3201C04B2235/3222C04B2235/3224C04B2235/3225C04B2235/3229C04B2235/3232C04B2235/3255C04B2235/3296C04B2235/3418C04B2235/3427C04B2235/3445C04B2235/3463C04B2235/3472C04B2235/3481C04B2235/3826C04B2235/3843C04B2235/444C04B2235/445C04B2235/656Y02P40/60
Inventor 廖达海吴南星余冬玲汪伟江毅陈涛江竹亭程章云赵增怡花拥斌刘玉涛朱祚祥徐佳杰宁翔
Owner JINGDEZHEN CERAMIC INSTITUTE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap