Insulating mortar for buildings and preparation method thereof
A technology for thermal insulation mortar and construction, applied in the field of thermal insulation mortar for construction and its preparation, can solve the problems affecting the reliability, durability and safety of building structures, poor impact resistance, low mechanical strength, etc. Freeze resistance, high compressive strength, excellent waterproof and frost resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0022] Example 1
[0023] An insulation mortar for construction, prepared with the following raw materials: 100kg of calcium carbide slag, 60kg of boron mud, 25kg of modified shale ceramic sand, 10kg of left cloud clay, 8kg of sepiolite fiber, 3kg of microclimate powder, 3kg of analcite powder, 1kg of calcium nitrate, 0.4kg of polydimethylsiloxane, 0.3kg of dimethylsulfoxide, 0.8kg of sodium lignocarbonate, 0.6kg of dehydrated acetic acid, 4kg of polyacrylate copolymer emulsion, 1kg of higher fatty acid waterproofing agent, 1kg of antifreeze agent (Two mixtures of calcium chloride and sodium acetate, the mass ratio is 1:1), barium chloride coagulant 1kg and sodium azobisisobutyronitrile air-entraining agent 1kg;
[0024] Preparation of modified shale ceramic sand: take 25kg of raw shale ceramic sand and place it in a calciner, calcinate it at 680℃ for 1.5h, take out the ground powder after natural cooling, pass through a 60 mesh sieve, and add 1.5kg Lignin and 75kg of deionized wa...
Example Embodiment
[0028] Example 2
[0029] A building insulation mortar, prepared with the following raw materials: 110kg of calcium carbide slag, 70kg of boron mud, 30kg of modified shale clay, 11kg of left cloud clay, 10kg of sepiolite fiber, 4kg of plagioclase powder, 4kg of analcite powder, 1.5 kg of calcium nitrate, 0.5 kg of polydimethylsiloxane, 0.4 kg of dimethyl sulfoxide, 1 kg of sodium carbonate, 0.8 kg of dehydrated acetic acid, 5 kg of polyacrylate copolymer emulsion, 1.5 kg of inorganic aluminum salt waterproofing agent, two 1.5kg of methyl sulfoxide antifreeze, 2kg of borax coagulant and 3kg of azodicarbonamide air-entraining agent;
[0030] Preparation of modified shale ceramic sand: take 30kg of raw shale ceramic sand and place it in a calciner, calcinate it at 700℃ for 2h, take out the ground powder after natural cooling, pass through 70 mesh sieve, and add 2.1kg wood After mixing with 120kg deionized water at 80℃, soak for 9h, then centrifuge at high speed and take it out for dr...
Example Embodiment
[0034] Example 3
[0035] A thermal insulation mortar for construction, prepared with the following raw materials: 120kg of calcium carbide slag, 80kg of boron mud, 35kg of modified shale clay, 12kg of left cloud clay, 12kg of sepiolite fiber, 5kg of microclimate powder, 5kg of analcite powder, and Calcium nitrate 2kg, polydimethylsiloxane 0.6kg, dimethyl sulfoxide 0.5kg, lignocarbonate 1.2kg, dehydrated acetic acid 1kg, polyacrylate copolymer emulsion 6kg, silane waterproofing agent 2kg, antifreeze 2kg (former Two mixtures of amide and magnesium chloride, the mass ratio is 1:3), 3kg of barium hydroxide coagulant and 5kg of triethoxybutane air-entraining agent;
[0036] Preparation of modified shale ceramic sand: take 35kg of raw shale ceramic sand and place it in a calcining furnace, and calcinate it at 720℃ for 2.5 hours. After it is naturally cooled, the ground powder is taken out, passed through an 80 mesh sieve, and then added 2.8kg Lignin and 175kg of deionized water, stir w...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap