High-stability UV adhesive

A shadowless adhesive and high-stable technology, applied in the direction of adhesives, polymer adhesive additives, non-polymer adhesive additives, etc., can solve the problems of shadowless adhesive stability and poor internal mechanical properties, and achieve Improve the internal mechanical properties, improve the connection force, and improve the effect of stability

Inactive Publication Date: 2019-08-23
陈习红
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is to provide a high-stable shadowless glue for the problems of poor stability and internal mechanical properties of commonly used shadowless glue

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0031] The preparation method of rubber matrix, comprises the steps:

[0032] (1) Mix polyethylene resin and petroleum ether in a reaction kettle according to a mass ratio of 1:20~40, add 2,6-di-tert-butyl-p-cresol with 8~12% polyethylene resin mass, and heat at 3~6°C / min rate program temperature rise to 160~180°C, stir and mix at 350~550r / min constant temperature for 2~4h to obtain polyethylene gel, take polyethylene gel and add epoxy resin at a mass ratio of 7~12:3:2, Mix the modified hydrotalcite and stir it magnetically at 500~800r / min for 40~60min to obtain the mixture;

[0033](2) In terms of parts by weight, take 10~20 parts of nano-silica, 3~7 parts of coupling agent, 30~55 parts of ethanol solution with a volume fraction of 70%, at 55~75°C, at 450~ Stir at a constant temperature of 700r / min for 2~4h, filter, take the filter cake and wash it with absolute ethanol for 2~4 times, then transfer it to a 70~90°C oven to dry to constant weight to obtain pretreated nano-sil...

Embodiment 1

[0042] Coupling agent: silane coupling agent KH-550.

[0043] Photosensitizer: 2,4,6-trimethylbenzoyl-diphenylphosphine oxide.

[0044] Anti-aging agent: anti-aging agent 264.

[0045] Reagent A: Mix sodium bicarbonate and 14% sodium hydroxide solution at a mass ratio of 3:18 to obtain reagent A.

[0046] Reagent B: Mix polyvinylpyrrolidone, polyethylene glycol, and water in a mass ratio of 5:1:18 to obtain Reagent B.

[0047] Modified hydrotalcite: mix magnesium aluminum hydrotalcite and water at a mass ratio of 1:25, and disperse ultrasonically at a frequency of 45 kHz for 20 minutes to obtain a dispersion. Take the dispersion and add hexadecyl trimethyl bromide at a mass ratio of 16:1 Mix ammonium, stir at 55°C for 3h at 400r / min constant temperature, filter, take the filter residue and wash it twice with water, then move to 65°C for oven drying for 2h to obtain modified hydrotalcite.

[0048] Additive: stannous octoate.

[0049] The preparation method of rubber matrix,...

Embodiment 2

[0060] Coupling agent: silane coupling agent KH-560.

[0061] Photosensitizer: Methyl benzoylformate.

[0062] Anti-aging agent: anti-aging agent 124.

[0063] Reagent A: Mix sodium bicarbonate and 14% sodium hydroxide solution at a mass ratio of 3:25 to obtain reagent A.

[0064] Reagent B: Mix polyvinylpyrrolidone, polyethylene glycol, and water in a mass ratio of 5:3:30 to obtain Reagent B.

[0065] Modified hydrotalcite: mix magnesium-aluminum hydrotalcite and water at a mass ratio of 1:50, and ultrasonically disperse at a frequency of 55 kHz for 35 minutes to obtain a dispersion. Take the dispersion and add hexadecyl trimethyl bromide at a mass ratio of 25:1 Mix ammonium, stir at 65°C and 600r / min constant temperature for 5h, filter, take the filter residue and wash it with water for 4 times, then move to 90°C oven to dry for 4h to obtain modified hydrotalcite.

[0066] Additive: stannous chloride.

[0067] The preparation method of rubber matrix, comprises the steps:...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
bond strengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to a high-stability UV adhesive, belonging to the adhesive field. As that brewer's grains are used as raw materials, the brewer's grains are mixed and soaked in alkali solution,so that the crude fibers in the brewer's grains are preliminarily defibrillated to form a support structure of a hollow shell layer. The production of the structure can improve the bite force betweenthe brewer's grains and the modified hydrotalcite component and the high molecular component, thereby achieving the effect of improving the internal mechanical properties; cetyltrimethyl ammonium bromide is used as modifier, the layered magnesium-aluminum hydrotalcite is modified, so as to be beneficial for high molecular viscous substances and other components to enter the interlayer structure, the interlayer structure of the hydrotalcite is spread out in the curing process to achieve the peeling effect, and the hydrotalcite is combined organically in the blending process of the gel made of polyethylene resin and the modified hydrotalcite, so as to effectively improve the stability and mechanical properties of the composite system. The invention solves the problems of poor stability and internal mechanical properties of the UV adhesive commonly used at present.

Description

technical field [0001] The invention belongs to the field of adhesives, in particular to a high-stable shadowless adhesive. Background technique [0002] We know that in the field of advertising, the general way of posting advertisements is to first spray the advertisement content on one layer of the inkjet film with an inkjet printer, and then paste it on the wall with ordinary latex or double-sided tape on the other layer of the inkjet film. On one hand, on advertising boards and other carriers, this method has complicated construction procedures on the one hand, and on the other hand, when removing advertisements, the latex or double-sided tape used tends to leave residual glue, is not easy to peel off, and can only be used once . In addition, the above method can only achieve single-sided inkjet painting, and for transparent glass windows, if it is used as a carrier for advertising, it needs to be constructed externally, which will have a certain impact on the advertisi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J4/02C09J4/06C09J11/08C09J11/06C09J11/04
CPCC09J4/06C09J11/04C09J11/06C09J11/08
Inventor 陈习红
Owner 陈习红
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap