Method for separating holocellulose in wood fibers by using choline deep-eutectic solvent

A technology of deep eutectic solvent and synthetic cellulose, which is applied in the field of biomass refining, can solve problems such as instrument corrosion, accelerated equipment aging, unfavorable interaction between deep eutectic solvent and fiber, etc., to achieve less environmental pollution and reduce equipment loss , Improve the effect of using value

Active Publication Date: 2020-02-18
QILU UNIV OF TECH
View PDF5 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the presence of chloride ions, the negative charge distribution is too concentrated, which is not conducive to the interaction between t

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for separating holocellulose in wood fibers by using choline deep-eutectic solvent
  • Method for separating holocellulose in wood fibers by using choline deep-eutectic solvent

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0089] Example 1:

[0090] The raw material of poplar wood is treated with choline lactate-lactic acid eutectic solvent to extract holocellulose.

[0091] (1) Raw material pretreatment: take relatively uniform wood chips, air-dry, crush, and sieving to obtain wood flour of 40-60 mesh.

[0092] (2) Phenyl alcohol extraction: The wood flour is extracted with a benzene-ethanol mixed solution with a volume ratio of 2:1 for 6 hours, dried and constant weight.

[0093] (3) Preparation of eutectic solvent: Mix choline chloride and potassium hydroxide according to the amount of the substance 1:1, in the ethanol solvent, heat and stir at the reaction temperature of 60 ℃ for 4 hours, filter, retain the supernatant, and follow the substance Add lactic acid in the amount of 1:1, after rotary evaporation and drying, mix with lactic acid in the amount of 1:10, heat at 60°C for 5h, and cool to room temperature to obtain choline lactate-lactic acid eutectic solvent.

[0094] (4) Eutectic solvent treat...

Example Embodiment

[0098] Example 2:

[0099] The raw materials of poplar wood are treated with choline formate-formic acid eutectic solvent to extract lignin.

[0100] (1) Raw material pretreatment: take relatively uniform wood chips, air-dry, crush, and then sieving to obtain wood flour of 40-60 mesh.

[0101] (2) Phenyl alcohol extraction: The wood flour is extracted with a benzene-ethanol mixed solution with a volume ratio of 2:1 for 6 hours, dried and constant weight.

[0102] (3) Preparation of eutectic solvent: Mix choline chloride and potassium hydroxide according to the amount of the substance 1:1, in the ethanol solvent, heat and stir at the reaction temperature of 60 ℃ for 4 hours, filter, retain the supernatant, and follow the substance Add formic acid in the amount of 1:1, after rotary evaporation and drying, mix with formic acid in the amount of 1:10, heat at 60°C for 5h, and cool to room temperature to obtain choline formate-formic acid eutectic solvent.

[0103] (4) Eutectic solvent treat...

Example Embodiment

[0107] Example 3:

[0108] The raw material of poplar wood is treated with choline propionate-propionic acid eutectic solvent to extract lignin.

[0109] (1) Raw material pretreatment: take relatively uniform wood chips, air-dry, crush, and then sieving to obtain wood flour of 40-60 mesh.

[0110] (2) Phenyl alcohol extraction: The wood flour is extracted with a benzene-ethanol mixed solution with a volume ratio of 2:1 for 6 hours, dried and constant weight.

[0111] (3) Preparation of eutectic solvent: Mix choline chloride and potassium hydroxide according to the amount of the substance 1:1, in the ethanol solvent, heat and stir at the reaction temperature of 60 ℃ for 4 hours, filter, retain the supernatant, and follow the substance Add propionic acid in the amount of 1:1, after rotary evaporation and drying, mix with propionic acid in the amount of 1:10, heat at 60°C for 5h, and cool to room temperature to obtain choline propionate-propionic acid eutectic solvent.

[0112] (4) Eutect...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a method for separating holocellulose in wood fibers by using a choline deep-eutectic solvent. The method comprises the following steps: pretreatment of raw materials, benzene-alcohol extraction, preparation of the deep-eutectic solvent, treatment of the deep-eutectic solvent, separation of the holocellulose and recovery of the solvent. The method is characterized in thatchloride ions in the choline deep-eutectic solvent are replaced under a mild condition, a non-toxic hydrogen bond donor is matched, and the deep-eutectic solvent with low halogen content is prepared and is used for separating holocellulose in the wood fibers. The method is high in holocellulose extraction rate, high in purity, simple to operate, obvious in effect, high in practicability, small inpollution and easy to popularize.

Description

technical field [0001] The invention belongs to the technical field of biomass refining, and in particular relates to a choline-based deep eutectic solvent and the application of the solvent system in extracting and separating cellulose. Background technique [0002] The information disclosed in this background section is only intended to increase the understanding of the general background of the present invention, and is not necessarily taken as an acknowledgment or any form of suggestion that the information constitutes the prior art already known to those skilled in the art. [0003] With the increasing shortage of petrochemical resources and the increasing pressure of environmental pollution, finding a renewable resource to replace petrochemical resources has become a top priority for sustainable development. Woody biomass resources are mainly composed of cellulose, hemicellulose, and lignin, and are the most widely available and abundant renewable resources on earth. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D21C3/20C08B37/00
CPCC08B37/0003D21C3/20
Inventor 杨桂花刘金科齐乐天陈嘉川薛玉
Owner QILU UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap