A kind of lithium manganese oxide and its preparation method and application

A technology of lithium manganate and manganese metal, applied in the field of materials, can solve the problems of low capacity of lithium manganate, poor cycle performance, a large amount of ammonia-containing wastewater, etc., and achieve the effect of improving gram capacity and cycle stability.

Active Publication Date: 2022-05-17
XTC NEW ENERGY MATERIALS(XIAMEN) LTD
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the shortcomings of low capacity, poor cycle performance and a large amount of ammonia-containing waste water produced by the lithium manganate obtained by the existing method, and to provide a method that can obtain high capacity and cycle performance without generating waste water containing ammonia. Lithium manganate of ammonia wastewater and its preparation method and application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of lithium manganese oxide and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Add sodium chloride into the reactor to prepare an aqueous sodium chloride solution with a conductivity of 2000uS / cm. Manganese powder, tantalum powder, and aluminum powder are mixed in a molar ratio of 1:0.001:0.003, and the resulting metal mixture, nitric acid, and high-purity water are simultaneously added to the above reactor in a molar ratio of 10:2:2 to carry out chemical corrosion crystallization reaction, Under normal pressure conditions, the ORP value of the reaction system is controlled at -400mv, the concentration of complexing agent is controlled at 5g / L, the conductivity is controlled at 2000uS / cm, and the stirring input power is controlled at 0.4kw / m 3 h, the metal ion concentration is controlled at 16g / L, the pH value is controlled at 10.5, and the reaction temperature is controlled at 50°C. In order to control the shape of the material, 5L / h nitrogen is introduced to control oxidation, and the material stays in the reactor for corrosion crystallization re...

Embodiment 2

[0032] Add sodium sulfate into the reactor to prepare an aqueous sodium sulfate solution with a conductivity of 200uS / cm. Manganese powder, tantalum powder, and titanium powder are mixed in a molar ratio of 1:0.001:0.003, and the resulting metal mixture, oxygen, and high-purity water are simultaneously added to the above reactor in a molar ratio of 10:2:2 to carry out chemical corrosion crystallization reaction, At the same time, 50g / L ammonium sulfate was added, and under normal pressure conditions, the ORP value of the reaction system was controlled at -100mv, the conductivity was controlled at 200uS / cm, and the stirring input power was controlled at 0.4kw / m 3 h, the metal ion concentration is controlled at 16g / L, the pH value is controlled at 10.5, and the reaction temperature is controlled at 30°C. In order to control the shape of the material, 5L / h nitrogen is introduced to control oxidation, and the material stays in the reactor for corrosion crystallization reaction The...

Embodiment 3

[0036] Add sodium nitrate into the reactor to prepare an aqueous sodium nitrate solution with a conductivity of 1000uS / cm. Manganese powder, tantalum powder, and niobium powder are mixed in a molar ratio of 1:0.001:0.003, and the resulting metal mixture, nitric acid, and high-purity water are simultaneously added to the above reactor in a molar ratio of 10:2:2 to carry out chemical corrosion crystallization reaction, At the same time, 5g / L ammonium sulfate was added, and under normal pressure conditions, the ORP value of the reaction system was controlled at -100mv, the concentration of complexing agent was controlled at 15g / L, the conductivity was controlled at 1000uS / cm, and the stirring input power Controlled at 0.4kw / m 3 h, the metal ion concentration is controlled at 16g / L, the pH value is controlled at 10.5, and the reaction temperature is controlled at 30°C. In order to control the shape of the material, 5L / h nitrogen is introduced to control oxidation, and the material...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
retention rateaaaaaaaaaa
retention rateaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of materials, and relates to a lithium manganate and its preparation method and application. The preparation method of the lithium manganate comprises preparing a metal salt into a metal salt solution with a conductivity ≥ 200uS / cm, and then adding manganese metal element and / or manganese metal oxide, dopant, oxidant, water, ammonia solution, The metal salt solution undergoes chemical corrosion and crystallization reaction under the conditions of oxidation-reduction potential ORP value ≤-100mv, complexing agent concentration of 3-50g / L, and electrical conductivity ≥200uS / cm, followed by magnetic separation, solid-liquid separation, and washing Calcined after drying and mixing with lithium source. Adopt the method provided by the present invention to prepare lithium manganate, dissolving and crystallizing process does not produce waste water, and consumes water constantly, thereby can achieve the purpose of being friendly to the environment, and use lithium manganate thus obtained as lithium ion battery cathode material, can also improve The gram capacity and cycle stability of lithium-ion batteries have great industrial application prospects.

Description

technical field [0001] The invention belongs to the field of materials, and relates to a lithium manganate and its preparation method and application. Background technique [0002] Lithium-ion batteries are a new generation of green high-energy batteries. They have the advantages of high voltage, high energy density, good cycle performance, small self-discharge, no memory effect, and wide operating temperature range. They are widely used in various electronic equipment, especially power tools and electric The demand for lithium-ion batteries for scooters is increasing day by day. Lithium cobalt oxide material (LiCoO 2 ), multi-component materials, high-nickel materials, lithium manganese oxide materials (LiMn 2 o 4 ). Among them, lithium manganate is fully used in the 3C market due to its stable material and mature technology. LiMn 2 o 4 Considered as the most promising alternative LiCoO in the field of power tools 2 one of the materials. LiMn 2 o 4 As a cathode m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/505C01G45/12H01M10/0525
CPCC01G45/1242H01M4/505H01M10/0525C01P2004/03C01P2006/40Y02E60/10
Inventor 马跃飞李权洪礼训
Owner XTC NEW ENERGY MATERIALS(XIAMEN) LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com