Single-component acrylic acid modified wrinkle paint and resin preparation method

An acrylic, one-component technology, applied in the field of coatings, can solve the problems of difficult to control the size of the wrinkle pattern, slow increase in the hardness of the coating film, and inconsistent finished product effects, and achieve improved moisture resistance, defoaming performance, and good scrub resistance. , The surface pattern is clear and uniform

Inactive Publication Date: 2021-11-12
宁夏星邦豹丰涂料科技有限公司
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The wrinkle paint in the traditional sense has: the size of the wrinkle pattern is not easy to control due to factors such as the level of construction personnel and the shape of the workpiece; due to the presence of tung oil in the existing product sink, the paint has poor weather resistance and is not suitable for outdoor products; construction technology Complicated and cumbersome process, resulting in inconsistent effects of the finished product; slow increase in coating film hardness, not suitable for assembly line operation, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] A one-component acrylic modified wrinkle paint is characterized in that it mainly includes the following raw material components in parts by weight: 28 parts of acrylic modified wrinkle resin, 6 parts of BF305 auxiliary resin, 6 parts of BF902 crosslinking agent, 12 parts of light Calcium, 6 parts of titanium dioxide, 2 parts of carbon black, 0.4 parts of white carbon black, 0.6 parts of vanadium drier, 0.8 parts of zirconium drier, 25 parts of ethyl acetate.

[0037] A one-component acrylic modified wrinkle paint, the preparation method of the single-component acrylic modified wrinkle paint and resin mainly includes the following preparation steps:

[0038] (1) Drop the hydroxy-terminated siloxane solution into an equimolar amount of the initiator intermediate solution at a rate of 20 drops / min, raise the temperature to 78°C, and react to the end point under the condition of reflux of ethyl acetate to obtain a crude product; After the reaction, the crude product was wa...

Embodiment 2

[0047] A one-component acrylic modified wrinkle paint is characterized in that it mainly includes the following raw material components in parts by weight: 28 parts of acrylic modified wrinkle resin, 6 parts of BF305 auxiliary resin, 6 parts of BF902 crosslinking agent, 12 parts of light Calcium, 6 parts of titanium dioxide, 2 parts of carbon black, 0.4 parts of white carbon black, 0.6 parts of vanadium drier, 0.8 parts of zirconium drier, 25 parts of ethyl acetate.

[0048] A one-component acrylic modified wrinkle paint, the preparation method of the single-component acrylic modified wrinkle paint and resin mainly includes the following preparation steps:

[0049] (1) Add phenyl-substituted cyclopropene dimethyl ester, isobornyl acrylate, and azobisisobutyronitrile to the reactor at a molar ratio of 1:3:0.008. Add a modified phosphazene base of 0.06 times the total mass of acrylate to the atmosphere, react at 500 rpm and 60°C for 8 hours, and finally end the reaction with 0.0...

Embodiment 3

[0055] A one-component acrylic modified wrinkle paint is characterized in that it mainly includes the following raw material components in parts by weight: 28 parts of acrylic modified wrinkle resin, 6 parts of BF305 auxiliary resin, 6 parts of BF902 crosslinking agent, 12 parts of light Calcium, 6 parts of titanium dioxide, 2 parts of carbon black, 0.4 parts of white carbon black, 0.6 parts of vanadium drier, 0.8 parts of zirconium drier, 25 parts of ethyl acetate.

[0056] A one-component acrylic modified wrinkle paint, the preparation method of the single-component acrylic modified wrinkle paint and resin mainly includes the following preparation steps:

[0057] (1) Drop the hydroxy-terminated siloxane solution into an equimolar amount of the initiator intermediate solution at a rate of 20 drops / min, raise the temperature to 78°C, and react to the end point under the condition of reflux of ethyl acetate to obtain a crude product; After the reaction, the crude product was wa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a single-component acrylic acid modified wrinkle paint and a resin preparation method, and relates to the technical field of coatings. The specific method comprises the steps of under the catalysis of a modified phosphazene base, initiating phenyl-substituted cyclopropene dimethyl ester and isobornyl acrylate to carry out anionic copolymerization by using a prepared short-chain silicon initiator so as to prepare carboxyl-terminated acrylic resin; sequentially adding n-butyl acetate, ethyl acetate, carboxyl-terminated acrylic resin, soya oil acid, linoleic acid, pentaerythritol, terephthalic acid, benzoic acid and dibutyltin dilaurate into a reactor for a heating reaction, and preparing acrylic acid modified wrinkle resin; and mixing the acrylic acid modified wrinkle resin with each auxiliary agent, and adjusting the viscosity to obtain the single-component acrylic acid modified wrinkle paint. The prepared single-component acrylic acid modified wrinkle paint is clear in pattern, simple to construct and good in weather resistance and mechanical strength.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a single-component acrylic modified wrinkle paint and a resin preparation method. Background technique [0002] At present, the wrinkle paint used more on the market is a kind of decorative baking paint with phenolic resin and alkyd resin as the main film-forming substances. Manufactured from phenolic or alkyd resins, pigments, drying oils, catalysts and organic solvents. Through the adjustment of the pigment-base ratio, the amount of the flower-adjusting resin and the auxiliary alkyd resin, different patterns can be formed; through the adjustment of the diluent and drier, the pattern shape and film performance can be improved. [0003] The wrinkle paint in the traditional sense has: the size of the wrinkle pattern is not easy to control due to factors such as the level of construction personnel and the shape of the workpiece; due to the presence of tung oil in the existing pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/08C09D7/61C09D5/28
CPCC09D167/08C09D7/61C09D5/28C08K2003/265C08K2003/2241C08K3/26C08K3/22C08K3/04C08K7/26
Inventor 王鸿忠
Owner 宁夏星邦豹丰涂料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka