Application of carbon material coated nickel nanoparticle catalyst in hydrogenation synthesis of m-aminobenzene sulfonic acid from sodium m-nitrobenzenesulfonate

A technology of sodium nitrobenzene sulfonate and nickel nanoparticles, which is applied in the preparation of organic compounds, catalysts for physical/chemical processes, metal/metal oxide/metal hydroxide catalysts, etc. Poor quality, poor sulfur resistance and other problems, to achieve the effect of easy operation, low production cost and good stability

Active Publication Date: 2021-12-17
ZHEJIANG UNIV OF TECH
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional preparation method: ① use iron powder to reduce sodium m-nitrobenzene sulfonate and acidify it, but the quality of the product produced by this method is poor and the pollution is serious; ② it is synthesized by electrochemical method, but the power consumption is large and the cost is too high; ③ The catalytic hydrogenation method has the advantages of less pollution and high product quality. It is a better production process at present. For example, the patent CN112371173A uses a Pt / C noble metal catalyst. Although the reaction activity is improved to a certain extent, the sulfur resistance performance is poor and stable. Sex is not strong

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Application of carbon material coated nickel nanoparticle catalyst in hydrogenation synthesis of m-aminobenzene sulfonic acid from sodium m-nitrobenzenesulfonate
  • Application of carbon material coated nickel nanoparticle catalyst in hydrogenation synthesis of m-aminobenzene sulfonic acid from sodium m-nitrobenzenesulfonate
  • Application of carbon material coated nickel nanoparticle catalyst in hydrogenation synthesis of m-aminobenzene sulfonic acid from sodium m-nitrobenzenesulfonate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0076] Weigh a certain amount of nickel nitrate hexahydrate and 4-pyridinecarboxylic acid and dissolve in a certain amount of absolute ethanol, the molar ratio of nickel to organic ligand is 1:2; the mass ratio of nickel to alcohol solution is 1:100. Heat at 25°C After stirring for 6 hours, add 1.0 mol / L sodium hydroxide aqueous solution dropwise to the mixed solution, adjust the pH of the solution to 4.0, and keep for 1 hour; add dropwise 98% triethanolamine solution, adjust the pH to 6.5, and keep for 2 hours; Add 25-28% ammonia water dropwise, adjust the pH to 8.5, and keep it for 2 hours. The resulting slurry is sealed and placed on a vibration table. The vibration program is set as follows: 1) Vibration frequency 10Hz, banner vibration for 2 minutes; 2) Vibration frequency 30Hz, banner vibration for 5 minutes; 3) Vibration frequency 40Hz, banner vibration for 1 minute; 4) The operation procedure 1)-3) is a vibration cycle; the entire crystallization, precipitation and agi...

Embodiment 16

[0118] Example 16 investigated the performance of different nickel nanoparticle catalysts prepared in Examples 1-15 and Comparative Examples 1-16 in catalytic hydrogenation synthesis of haloanilines.

[0119] In a 50ml stainless steel reaction kettle, add 25ml methanol, 1.0g p-chloronitrobenzene, 0.05g carbon material coated nickel nanoparticle catalyst prepared by different embodiments or comparative examples, close the reaction kettle, and replace the air in the reaction kettle with hydrogen for 10 The second time, the temperature was raised to 100°C, the hydrogen pressure was 1.0 MPa, stirring was started, and the stirring rate was 1800 r / min, and the reaction was carried out for 40 minutes. Stop the reaction, and after the temperature drops to room temperature, take the supernatant of the reaction solution, filter the catalyst, and analyze the filtrate by gas chromatography. The experimental results are shown in Table 3:

[0120] Table 3 Performance of different carbon ma...

Embodiment 17

[0124] Example 17 investigated the reaction performance of the carbon material-coated nickel nanoparticle catalyst prepared in Example 2 for the hydrogenation of different halogenated nitrobenzenes to prepare halogenated anilines.

[0125] In a 50ml stainless steel reactor, add 25ml of methanol, 1.0g of different halogenated nitrobenzenes, 0.05g of the carbon material coated nickel nanoparticle catalyst prepared in Example 2, close the reactor, and replace the air in the reactor with hydrogen for 10 times , the temperature was raised to 100° C., the hydrogen pressure was 1.0 MPa, stirring was started at a stirring rate of 1800 r / min, and the reaction was carried out for 1 h. Stop the reaction, and after the temperature drops to room temperature, take the supernatant of the reaction solution, filter the catalyst, and analyze the filtrate by gas chromatography. The experimental results are shown in Table 4:

[0126] Table 4 Reaction performance of nickel nanoparticle catalysts ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses an application of a carbon material coated nickel nanoparticle catalyst in hydrogenation synthesis of m-aminobenzene sulfonic acid from sodium m-nitrobenzenesulfonate. The carbon material coated nickel nanoparticle catalyst is high in conversion rate, high in selectivity, good in stability and long in service life when applied to synthesis of m-aminobenzene sulfonic acid through hydrogenation of sodium m-nitrobenzenesulfonate.

Description

technical field [0001] The invention belongs to the field of catalyst preparation technology and application, and relates to the application of a carbon material-coated nickel nanoparticle catalyst in the hydrogenation of sodium m-nitrobenzenesulfonate to synthesize m-aminobenzenesulfonic acid. Background technique [0002] Nickel nanoparticles have great application value in catalysis, lithium batteries, sensors and other fields. As a catalyst, nanoscale nickel particles have better catalytic activity than bulk or flake, but due to the high surface energy, nanoscale nickel particles are easy to agglomerate and limit its advantages. When exposed to the air, the metal nanoparticles are easily oxidized into metal oxides, and a layer of carbon material wrapped around the metal nanoparticles can prevent the metal nanoparticles from being oxidized. In addition to the characteristics of non-toxicity, high thermal stability and low price, the carbon layer-coated metal structure al...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C07C309/46C07C303/22B01J23/755C07C209/36C07C211/52C07C227/04C07C229/60C07C213/02C07C217/84C07C221/00C07C225/34
CPCC07C303/22B01J23/755C07C209/36C07C227/04C07C213/02C07C221/00C07C309/46C07C211/52C07C229/60C07C217/84C07C225/34
Inventor 卢春山杨园园李小年张群峰丰枫
Owner ZHEJIANG UNIV OF TECH
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com