Medical dressing capable of resisting bacteria and promoting wound healing
A technology for wound healing and chitosanization, applied in medical science, bandages, etc., can solve the problem of not finding soluble chitosan, and achieve the effect of promoting wound healing, good antibacterial properties, and antibacterial wound healing
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Synthetic example 1
[0044] Synthetic methoxy PEG chitosan
[0045] It is weighed with a chitosan of 0.16 g of a molecular weight of 2 × 10 ^ 5dA, and a deththyacetin is 95%, and a 10 ml MES buffer (25 mM, pH = 4.90), and stirred at 0.1 ml of HCl at room temperature for half an hour, The chitosan is completely dissolved, thereby obtaining a uniform solution having a mass volume percent concentration of 1.6%; then activated at room temperature for 1 hour carboxy polyethylene glycol monomethyl ether, NHS and EDC · HCl mixed solution (solvent is 25 mm pH) = 4.90 MES buffer solution) 20 mL of the reaction solution, continuously stirred at room temperature for 24 hours, wherein the ratio of chitosan, carboxy polyethylene glycol monomethyl ether, NHS, EDC · HCl is 1 ratio of 1 : 1: 2: 2; After the reaction is completed, the hydroxylamine is added to the amount of hydroxylamine having a substance of carboxyl polyethylene glycol monomethyl ether and then transferred to a dialysis bag with the reaction solutio...
Synthetic example 2
[0047] Synthesis azide-based PEG chitosan
[0048] It is weighed with a chitosan of 0.16 g of a molecular weight of 5 × 10 × 10 × 10 × 4 DA, and the dethritis is 98% is added to 10 ml MeS buffer (25 mM, pH = 4.80), and stirred with 0.1 ml of HCl at room temperature for half an hour, so that the shell The glycan is completely dissolved, thereby obtaining a uniform solution having a mass volume percent concentration of 1.6%; then a carboxy-polyethylene glycol-azide group, NHS-polyethylene glycol-azide group, NHS and EDC · HCl, which activates 1 hour at room temperature 1 hour, NHS and EDC · HCl mixed solution (MES cushioning solution having a solvent of 25 mM pH = 4.80) 20 mL was added to the above-mentioned reaction solution, and the reaction was continuously stirred at room temperature for 24 hours, including chitosan, carboxy-polyethylene glycol-azide, NHS, EDC · HCl The ratio of the substance is 1: 2: 4: 4; the reaction is added to the end of the amount of hydrochloride hydroxyl...
Embodiment 1
[0051] Experiments were prepared by red blood cell suspension: Take 1 volume rabbit whole blood in 50 ml of centrifuge tube, add 4 volume Tris buffer (10 mm Tris, 150 mM NaCl, pH = 7.2), 1000 × g from centrifugation for 10 minutes, and be careful Decorate, and add 5 volume Tris buffer in the lower red blood cell precipitation, and 1000 × g was centrifuged again for 10 minutes. Washed to colorlessness to be washed with the supernatant, dilute the resulting red blood cell precipitate to 5% (v / v) to 5% (v / v) to obtain a red blood cell suspension.
[0052] Soluble chitosan aqueous solution of soluble chitosan: Samples of PEG chitosan in Synthesis Example 2 were dissolved and diluted with the above Tris buffer, and the concentration of 20 mg / ml, 30 mg / ml, 40 mg / ml and 50 mg / ml sample, respectively. Solution. To 0.5 ml of 5% (v / v) red blood cell suspension, the equivalent sample solution, the like Tris buffer is a negative control, and the like 0.1% Triton X-100 (Tris buff...
PUM
Property | Measurement | Unit |
---|---|---|
molecular weight | aaaaa | aaaaa |
molecular weight | aaaaa | aaaaa |
molecular weight | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com