Method for preparing nano multiple films on surface of glass

A glass surface, nano-multi-layer technology, applied in the field of glass surface film preparation, can solve the problems of poor effect and efficiency, affecting sight line, unable to use front windshield, etc.

Inactive Publication Date: 2005-10-26
西安陆通科技发展有限公司 +1
View PDF0 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because this method affects the line of sight, it is mainly used on the rear windshield of the car and cannot be used on the front windshield
The defogging of the front windshield mainly depends on blowing, which is less effective and efficient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] Embodiment 1: common glass surface coating

[0010] 1) Preparation of silica sol: first mix ethyl orthosilicate, short-carbon chain alcohols with a carbon chain length of less than 4, and deionized water, then add organic acid or inorganic acid as a catalyst, and stir and mix in a closed container at room temperature , make it carry out hydrolysis and polymerization reaction to make silica sol; orthosilicate, short carbon chain alcohol with carbon chain length less than 4, deionized water and organic acid or inorganic acid as catalyst at 1:15: 4: 0.05 molar ratio mixing;

[0011] 2) Preparation of antimony-fluorine composite doped tin dioxide sol: Dissolve stannous chloride dihydrate and deionized water in ethanol at a molar ratio of 1:2:40, stir in a constant temperature reactor at 80°C After 20 hours, add trifluoroacetic acid and antimony trichloride absolute ethanol solution with a molar ratio of 0.1:0.03:40 respectively, continue stirring at a constant temperature ...

Embodiment 2

[0019] Example 2: Coating on the surface of tempered glass

[0020] The preparation of silica sol: first mix ethyl orthosilicate, short carbon chain alcohol with carbon chain length less than 4 and deionized water, then add organic acid or inorganic acid as catalyst, stir and mix in a closed container at room temperature, make It undergoes hydrolysis and polymerization reaction to produce silica sol; tetraethyl orthosilicate, short carbon chain alcohol with a carbon chain length less than 4, deionized water and organic acid or inorganic acid are used as catalysts at a ratio of 1:20:4: Mixed at a molar ratio of 0.05;

[0021] 2) Preparation of antimony-fluorine compound-doped tin dioxide sol: Dissolve tin chloride tetrahydrate and deionized water in ethylene-propanol at a molar ratio of 1:2:40, and heat in a constant temperature reactor at 70° C. Stir for 23 hours, then add hydrofluorosilicic acid with a molar ratio of 0.3:0.02:80, antimony pentachloride in ethylene-propanol s...

Embodiment 3

[0029] Example 3: Coated tempered glass tempered after pre-coating

[0030] The preparation of silica sol: first mix ethyl orthosilicate, short carbon chain alcohol with carbon chain length less than 4 and deionized water, then add organic acid or inorganic acid as catalyst, stir and mix in a closed container at room temperature, make It undergoes hydrolysis and polymerization to produce silica sol; orthosilicate, short carbon chain alcohols with a carbon chain length of less than 4, deionized water and organic acids or inorganic acids as catalysts at a ratio of 1:25:4: Mixed at a molar ratio of 0.05;

[0031]2) Preparation of antimony-fluorine compound-doped tin dioxide sol: Dissolve stannous chloride dihydrate and deionized water in n-butanol at a molar ratio of 1:2:80, and dissolve them in n-butanol in a constant temperature reactor at 60 Stir at ℃ for 22 hours, then add the n-butanol solution of ammonium fluoride and antimony trichloride with a molar ratio of 0.2:0.04:40 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to view more

Abstract

The present invention relates to a method for preparing nano multilayer film on glass surface. Said invention utilizes the combination of sol-gel method and spray pyrolysis method to prepare first layer silicon dioxide film, second layer antimony-fluorine combination doped tin dioxide film and third layer composite film using silicon dioxide and titanium dioxide as main component. Said invention also provides the concrete function of the above-mentioned energy layer film, and said glass has the hydrophobic and bacteriostatic characteristics.

Description

technical field [0001] The invention relates to a preparation method of a glass surface film, in particular to a preparation method of a glass surface nanometer multilayer film. Background of the invention [0002] The transparent conductive substrate used in liquid crystal, plasma and other flat panel display devices in the optoelectronics industry is to prepare a layer of oxide transparent conductive film on the glass surface. There are many types of oxide transparent conductive films, such as: doped tin oxide, Doped zinc oxide and tin-doped indium oxide (ITO), etc. In industrial applications, taking into account both electrical conductivity and light transmission, this type of thin film is currently mainly made of tin-doped indium oxide (ITO). Due to the rare element indium, the cost is relatively high. Its preparation methods mainly adopt magnetron sputtering, chemical vapor deposition, sol-gel method, spray pyrolysis method, etc., among which: magnetron sputtering and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C17/34
Inventor 赵高扬张卫华庄耀山何善溪
Owner 西安陆通科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap