Environment-friendly polyaniline modified aluminium powder anti-corrosive coating and preparation method thereof
A technology of anti-corrosion coatings and polyaniline, which is applied in the field of coatings and can solve problems such as poor anti-corrosion performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0061] Example 1
[0062] Prepare polyaniline modified aluminum powder as follows:
[0063] (a) Prepare a mixed aqueous solution of phosphoric acid and phytic acid: phosphoric acid is 1.5 mol / liter; phytic acid is 0.5 mol / liter.
[0064] (b) Adding aniline to the mixed aqueous solution of phosphoric acid and phytic acid, the concentration of aniline after mixing is 0.5 mol / L. Continue stirring for 0.5 hour. Take 500ml of a mixed aqueous solution of phosphoric acid, phytic acid and aniline, add 70g of 325 mesh aluminum powder, and stir for 10 minutes, then pre-cool to 8°C.
[0065] (c) Preparation of oxidant aqueous solution: benzoyl peroxide is selected as the oxidant, and the concentration of benzoyl peroxide is 1.5 mol / L. The aqueous solution of benzoyl peroxide is pre-cooled to 8°C.
[0066] (d) Add 500ml of (c) solution slowly to 500ml of mixed aqueous solution of phosphoric acid, phytic acid and aniline (b) containing aluminum powder within 10-30 minutes, react at 5°C for 3 hour...
Example Embodiment
[0069] Example 2
[0070] Dispersing agent (Disperbyk190) 0.4 parts, leveling agent (Perenol F40) 1.2 parts, defoaming agent (BYK-066N) 1.1 parts, anti-sagging agent (bentonite) 0.5 parts, pigment (titanium dioxide) 3 parts, filler ( 2 parts of barite powder), 25 parts of 325 mesh polyaniline modified aluminum powder prepared according to the method of Example 1, added to 92 parts of alkyd resin (60% oil linseed oil alkyd resin) and 20 parts of solvent (toluene) It is stirred for 20 minutes, and then ground in a sand mill. After the fineness is less than 45 microns, the material is discharged to make an environmentally friendly polyaniline modified aluminum powder alkyd anticorrosive coating.
[0071] Spray two coats of the coating on the surface of four 150mm×75mm×2mm 45# steel plates treated by conventional sandblasting to Sa2.5 grade, dry at room temperature for 15 days, and then seal with a 60℃ liquid with a weight ratio of rosin: paraffin wax = 1:1 At the same time, conduct c...
Example Embodiment
[0072] Example 3
[0073] Dispersing agent (Disperbyk180) 0.7 parts, leveling agent (BYK-359) 0.8 parts, defoaming agent (Defom 5300) 0.5 parts, anti-sagging agent (bentonite) 0.6 parts, pigment (zinc oxide) 2 parts, filler (talc) Powder) 2 parts, 25 parts of 325 mesh polyaniline modified aluminum powder prepared according to the method of Example 1, added to 50 parts of 2123 phenolic resin (produced by Shanghai Daowang Adhesive Technology Co., Ltd.) and 20 parts of solvent (toluene) , Stir for 20 minutes, and then grind in a sand mill. After the fineness is less than 45 microns, the material is discharged to make an environmentally friendly polyaniline modified aluminum powder phenolic anticorrosive coating.
[0074] Spray the coating twice on the surface of four 150mm×75mm×2mm 45# steel plates treated by conventional sandblasting to Sa2.5 grade, dry for 15 days at room temperature, and then seal with a 60℃ liquid with a weight ratio of rosin: paraffin wax = 1:1 At the same time,...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap