Preparation process of low-grade laterite nickel ore oxidized pellet

A technology of lateritic nickel ore and oxidized pellets, which is applied in the field of preparation of low-grade laterite nickel ore oxidized pellets. It can solve the problems of high-yield impact of blast furnace, low output of sintering machine, and short construction period, so as to solve the problem of pressure resistance Low strength, increase specific surface area, and promote the effect of liquid phase bonding

Active Publication Date: 2011-11-16
北京中宏联工程技术有限公司
View PDF3 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the processing methods of lateritic nickel ore put into production in the world are as follows: the most important process used in the pyrotechnic process is the reduction smelting nickel-iron process, and the reactors used include electric furnace and blast furnace. Other major pyrotechnic processes include Krupp process, rotary kiln-electric furnace smelting, reduction smelting ferronickel outside the furnace and other processes, but lateritic nickel ore is required to have a higher grade, and is required to be lump ore or sintered ore; the ammonia leaching process in the wet process is only suitable for treating the surface layer For laterite nickel ore, although the high-pressure acid leaching (HPAL) process has been industrialized and industrialized, it is difficult to popularize because it operates under high-pressure conditions and has high requirements for equipment, scale, investment, operation control and ore grade; The fire-wet method combined process is relatively simple, the investment is small and the construction period is short, which is suitable for small and medium-sized enterprises, but the technical difficulties lie in high energy consumption and comprehensive recovery of metals
Some domestic enterprises use the method of blast furnace smelting to prepare nickel-containing molten iron to utilize laterite nickel ore, but the blast furnace charge is mainly prepared by sintering, the output of the sintering machine is low, and the strength of the sinter is low, which seriously affects the smooth operation and high production of the blast furnace
At present, there is no precedent in the world where laterite nickel ore is prepared into pellets and supplied to the blast furnace for ferronickel smelting

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation process of low-grade laterite nickel ore oxidized pellet
  • Preparation process of low-grade laterite nickel ore oxidized pellet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] See figure 1 , The low-grade laterite nickel ore is dried to a moisture content of 12%, and crushed to -3mm with a pair of roller crusher; laterite nickel ore 45%, iron concentrate 34.3%, chromite 15%, calcium additives 5.7% Under the condition of raw material ratio, when the moisture content of the mixture is 10%, the pressure is 0.67N / mm 2 After pretreatment by high-pressure roller mill, pellets are pelletized on a disc pelletizer. The pelletizing water content is 12.2%, pelletizing time is 12min, and the pellet size is controlled at 12mm; the green pellet drop strength is 13.3 times / 0.5m. Additive formula: limestone : Quartz sand: borax=58%:27%:15%, the particle size is less than 0.074mm and the content reaches 85% or more; under the conditions of pellet preheating temperature 1100, preheating time 13min, roasting temperature 1220, roasting time 13min, prepare The finished pellets have a compressive strength of 1915N / piece.

Embodiment 2

[0018] See figure 1 , Dry the low-grade laterite nickel ore to a moisture content of 13%, and use a roller crusher to crush it to -3mm; laterite nickel ore 45%, iron concentrate 32.3%, chromite 15%, calcium-containing additives 7.7% Under the condition of raw material ratio, the moisture content of the mixture is 10%, and the pressure is 0.77N / mm 2 After the high-pressure roller mill pretreatment, pelletize on a disc pelletizer with a pelletizing water content of 12.5%, pelletizing time of 14min, and a pellet size of 14mm; the falling strength of the pellets is >20 times / 0.5m. Additive formula: limestone: quartz sand: borax = 62%: 23%: 15%, the particle size is less than 0.074mm and the content is more than 85%; the pellet preheating temperature is 1000, preheating time 15min, roasting temperature 1280, roasting time 15min Under the conditions, the finished pellets were prepared with a compressive strength of 2326N / piece.

Embodiment 3

[0020] See figure 1 , Dry the low-grade laterite nickel ore to a moisture content of 11%, and use a roller crusher to crush it to -3mm; laterite nickel ore 45%, iron concentrate 35%, chromite 15%, calcium additive 5.0% Under the condition of raw material ratio, the moisture content of the mixture is 10%, and the pressure is 0.57N / mm 2 After pretreatment by high-pressure roller mill, pellets are pelletized on a disc pelletizer. The pelletizing water content is 12.3%, pelletizing time is 10 minutes, and the pellet size is controlled at 15mm; the green pellet drop strength is 13.3 times / 0.5m. Additive formula: limestone : Quartz sand: borax=60%:27%:13%, the particle size is less than 0.074mm and the content reaches 85% or more; under the conditions of pellet preheating temperature 1050, preheating time 12min, roasting temperature 1240, roasting time 12min, prepare The finished pellets have a compressive strength of 1900N / piece.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation process of a low-grade laterite nickel ore oxidized pellet. The preparation method comprises the following steps: drying low-grade laterite nickel ore until the moisture content of the laterite nickel ore is 11-13%, and crushing the laterite nickel ore with a double-roll crushing mill until the grain size of the laterite nickel ore is minus 3mm; evenly mixinglaterite nickel ore, iron ore concentrate, chromite and a calcium-containing additive in a mass proportion of (45-50%):(30-35%):15%:(5.0-7.7%); carrying out high-pressure rolling pretreatment on the mixed material; pelletizing on a disk pelletizing machine, wherein the moisture content of fresh pellet is 12-12.5%, and the grain size of the fresh pellet is controlled to 12-16mm; and carrying out drying preheating and roasting on the fresh pellet in a chain gate and a rotary kiln or a belt type roasting machine so as to obtain the finished product oxidized pellet, wherein the preheating temperature is 1000-1100 DEG C, the preheating time is 12-15 minutes, the roasting temperature is 1220-1280 DEG C, and the roasting time is 12-15 minutes. The invention relates to the preparation process of the low-grade laterite nickel ore oxidized pellet with high finished product pellet compression strength and wide roasting temperature range when the laterite nickel ore is used for production of pellets.

Description

Technical field [0001] The invention relates to a process for preparing oxidized pellets of laterite nickel ore, in particular to a process for preparing oxidized pellets of laterite nickel ore. Background technique [0002] Nickel and chromium are the main alloying elements for smelting stainless steel. About 63% of the world’s nickel is used in the production of stainless steel, so the stainless steel industry has the largest impact on nickel consumption. Currently, the only nickel resources available for human development and utilization are land-based nickel sulfide ore and laterite nickel ore, of which about 30% are 70% of sulfide ore is oxide ore, while nickel sulfide ore provides 60% of the total nickel metal output. Laterite nickel ore resources are surface weathered crust deposits formed by weathering-leaching-sedimentation of nickel sulfide rock masses, which are loose clay-like ore composed of hydrous oxides such as iron, aluminum, and silicon. Although the reserves ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22B1/243
Inventor 潘建朱德庆李启厚周仙霖张金良
Owner 北京中宏联工程技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com