Chromium-free passivation solution and hot-dip galvanized metal material

A chromium-free passivation, hot-dip galvanizing technology, applied in metal material coating process, hot-dip plating process, coating and other directions, can solve the problems of poor corrosion resistance, heat resistance and fingerprint resistance, and achieve good resistance. Corrosive, easy to use, save the effect of oiling process

Inactive Publication Date: 2012-03-14
PANGANG GROUP VANADIUM TITANIUM & RESOURCES +3
View PDF6 Cites 30 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to solve the defects of the poor corrosion resistance, heat resistance and fingerprint resistance of the chromium-free passivation solution in the prior art, and provide a kind of corrosion resistance, water resistance, heat resistance and fingerprint resistance. Good chrome-free passivation solution

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Chromium-free passivation solution and hot-dip galvanized metal material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] This embodiment is used to illustrate the chromium-free passivation solution provided by the present invention and its preparation method.

[0043] Put 20g of tannic acid in the container, add 100mL of distilled water to dissolve it completely; slowly drop 20mL of silane coupling agent KH550 into the above container within 2 minutes, stir for 5 minutes until the reaction is complete; add 0.5g of dispersing Agent (boric acid), 0.005g defoamer (polyether modified polydimethylsiloxane, Guangzhou Silok, silok2243) and 0.005g stabilizer (isopropanol), stir until completely dissolved; add 25 grams of H 2 TiF 6 Aqueous solution (30% by weight), stirred for 5 minutes until uniform; Added 10g nanometer SiO 2 powder (purchased from GE Company of the United States, RNS-E, average particle size 20nm), stirred for 10 minutes until the solution was in a uniform and stable phase; added 180mL silicon acrylic emulsion (purchased from Nantong Shengda, SD-5281), and then distilled water ...

Embodiment 2

[0045] This embodiment is used to illustrate the chromium-free passivation solution provided by the present invention and its preparation method.

[0046] Put 24g of phytic acid in the container, add 100mL of distilled water to dissolve it completely; slowly drop 15mL of silane coupling agent KH560 into the above container within 2 minutes, stir for 5 minutes until the reaction is complete; add 0.5g of dispersant (boric acid), 0.005g defoamer (polyether modified polydimethylsiloxane, Guangzhou Silok, silok2243) and 0.010g stabilizer (isopropanol), stir until completely dissolved; add 25 grams of sulfuric acid oxygen Titanium solution (40% by weight), stirred for 5 minutes until uniform; added 30g of silica sol (30% by weight), stirred for 10 minutes until the solution was in a uniform and stable phase; added 180mL of acrylic resin film-forming agent (purchased from A-3418), then the volume is fixed to 1L with distilled water to obtain the chromium-free passivation solution S2 pr...

Embodiment 3

[0048] This embodiment is used to illustrate the chromium-free passivation solution provided by the present invention and its preparation method.

[0049] Put 15g of tannic acid in the container, add 100mL of distilled water to dissolve it completely; slowly drop 10mL of silane coupling agent KH570 into the above container within 2 minutes, stir for 5 minutes until the reaction is complete; add 0.5g of dispersing Agent (boric acid), 0.010g defoamer (polyether modified polydimethylsiloxane, Guangzhou Silok, silok2243) and 0.010g stabilizer (isopropanol), stirred until completely dissolved; add 20 grams of sulfuric acid Aqueous titanyl oxide solution (40% by weight), stirred for 5 minutes until uniform; adding 30 g of sodium silicate aqueous solution with a modulus of 2 at a concentration of 30% by weight, stirred for 10 minutes until the solution was a uniform and stable phase; added 180 mL of polyurethane resistant Yellow resin (purchased from Jinjiang Jianhua, Fujian, 812), a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a chromium-free passivation solution and a hot-dip galvanized metal material. The chromium-free passivation solution is prepared from a raw material mixture through uniform mixing. The raw material mixture contains one or more silane coupling agents and water. The chromium-free passivation solution is characterized in that the raw material mixture also contains one or more titanium compounds, one or more inorganic silicon compounds, one or more water-soluble film-forming agents and tannic acid or phytic acid, wherein the one or more titanium compounds are selected from hexafluorotitanic acid, ammonium hexafluorotitanate, potassium hexafluorotitanate, metatitanic acid and titanyl sulfate and the one or more inorganic silicon compounds are selected from nanoscale silica powder, silica sol and sodium silicate. The chromium-free passivation solution has good corrosion resistance, good water resistance, good heat resistance, good fingerprint resistance and excellent roller coating performances. A passivation method adopting the chromium-free passivation solution can greatly shorten treatment time, can be utilized for passivation plate production in a spray mode or a roller coating mode, and also can avoid an oiling process in galvanized plate production.

Description

technical field [0001] The invention relates to a chrome-free passivation solution and a hot-dip galvanized metal material. Background technique [0002] In order to prevent the galvanized sheet from rusting during transportation, the hot-dip galvanized sheet factory will coat a layer of anti-rust oil film on the surface of the galvanized sheet before leaving the factory. However, when users use hot-dip galvanized sheets, they require bare parts to have excellent anti-corrosion properties to prevent corrosion and rust and reduce their service life. Therefore, users must use galvanized sheets that use passivation liquid for surface anti-rust treatment. [0003] The most widely used method to improve the corrosion resistance of galvanized coatings is chromate passivation. This passivation method has simple process, low cost and good corrosion resistance. However, since this passivation method involves Pb, Cd, Hg, Cr 6+ The use and release of many substances that seriously po...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23C22/34C23C22/53C23C2/06
CPCC23C2222/20
Inventor 梅东生许哲峰郭太雄徐权陈永娄燕周一林
Owner PANGANG GROUP VANADIUM TITANIUM & RESOURCES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com