Temperature adjusting humidity adjusting coating and preparation method thereof

A temperature-adjusting-humidity-adjusting coating technology, which is applied in the preparation of temperature-humidity-adjusting coatings, can solve the problems of excessive harmful components, harmful to human body, easy to burn, etc., and achieve excellent fire prevention and energy saving effects

Inactive Publication Date: 2013-06-19
LUNAN RES INST OF COAL CHEM
View PDF8 Cites 134 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, there are harmful components in temperature-adjusting and heat-insulating coatings exceeding the standard, and the noise reduction, heat insulation, temperature adjustment, humidity adjustment, high strength, and fire resistance performance cannot meet the quality standards. For example, coatings containing organic polymer materials are not fireproof, and coatings containing asbestos Harmful to the human body, can not meet the technical requirements of energy saving and environmental protection
Chinese patent CN 100528998C uses attapulgite, plant fiber, rock wool, modified emulsified asphalt, polyvinyl alcohol and sodium hydroxymethyl cellulose as raw materials to prepare a temperature-adjusting waterproof coating, but the modified emulsified asphalt and polyvinyl alcohol are easy to burn , and polyvinyl alcohol is harmful to the human body, which limits its application
[0004] At present, there is no literature report on the method of adjusting the indoor temperature with a coating consisting of a heat-insulating primer, a phase-change energy storage intermediate paint and a heat-conducting topcoat.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Temperature adjusting humidity adjusting coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] 1. Preparation of primer: In parts by mass, 100 parts of aluminum dihydrogen phosphate, 10 parts of perlite, 10 parts of calcium carbonate, 0.02 part of methyl silicone oil, 0.04 part of sodium tripolyphosphate, 0.04 part of methyl trimethoxy Silane, 50 parts of deionized water, stirred and dispersed to obtain a thermal insulation primer.

[0030] 2. Preparation of intermediate paint: in parts by mass, 100 parts of aluminum dihydrogen phosphate, 10 parts of Na 2 SO 4 10H 2 O, 10 parts of calcium carbonate, 0.02 part of methyl silicone oil, 0.04 part of sodium tripolyphosphate, 0.04 part of methyltrimethoxysilane, 50 parts of deionized water, stirred and dispersed to obtain a phase change energy storage intermediate paint.

[0031] 3. Preparation of topcoat: In parts by mass, 100 parts of aluminum dihydrogen phosphate, 5 parts of graphite flakes, 20 parts of diatomaceous earth, 20 parts of calcium carbonate, 2 parts of zinc powder, 0.02 parts of methyl silicone oil, 0....

Embodiment 2

[0033] 1. Preparation of primer: In parts by mass, 100 parts of silica sol, 100 parts of mineral wool, 100 parts of gypsum, 1 part of simethicone, 2 parts of hydroxymethyl cellulose, 2 parts of vinyl dimethyl ethane Oxysilane, 800 parts of deionized water, stirred and dispersed to obtain a thermal insulation primer.

[0034]2. Preparation of intermediate paint: in parts by mass, 100 parts of silica sol, 100 parts of paraffin, 100 parts of gypsum, 1 part of simethicone, 2 parts of hydroxymethyl cellulose, 2 parts of vinyl dimethyl ethoxylate base silane, 800 parts of deionized water, stirred and dispersed to obtain a phase change energy storage intermediate paint.

[0035] 3. Preparation of topcoat: In parts by mass, 100 parts of silica sol, 100 parts of pure acrylic emulsion, 100 parts of aluminum nitride, 100 parts of molecular sieve, 100 parts of gypsum, 20 parts of copper chloride, and 1 part of dimethyl silicone oil , 2 parts of hydroxymethyl cellulose, 2 parts of vinyl d...

Embodiment 3

[0037] 1. Preparation of primer: In parts by mass, 100 parts of geopolymer, 50 parts of hollow glass microspheres, 50 parts of gypsum, 0.5 part of hydrophilic silicone oil, 1 part of sodium polyacrylate, 1 part of polyacrylic acid, 400 parts Deionized water, stirring and dispersing to obtain a thermal insulation primer.

[0038] 2. Preparation of intermediate paint: in parts by mass, 100 parts of geopolymer, 50 parts of polyol, 50 parts of talcum powder, 0.5 part of hydrophilic silicone oil, 1 part of sodium polyacrylate, 1 part of polyacrylic acid, 400 parts of Ionized water, stirring and dispersing to obtain a phase change energy storage medium paint.

[0039] 3. Preparation of topcoat: in parts by mass, 100 parts of geopolymer, 50 parts of organic silicon modified pure acrylic emulsion, 50 parts of magnesium oxide, 50 parts of activated carbon, 50 parts of attapulgite, 10 parts of anatase type Titanium oxide, 0.5 parts of hydrophilic silicone oil, 1 part of sodium polyacry...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to temperature adjusting humidity adjusting coating and a preparation method thereof. The temperature adjusting and humidity adjusting coating comprises thermal insulation undercoat, phase transition energy storage intermediate coat and heat conduction humidity adjusting finish. The undercoat insulates heat, and the phase transition energy storage intermediate coat transmits indoor energy through the finish and stores energy through the phase transition, and thereby effectively adjusting indoor temperature. The phase transition energy storage intermediate coat and the humidity adjusting function of the finish impart the whole coating temperature adjusting and humidity adjusting function. In addition, the temperature adjusting and humidity adjusting coating has the advantages of being fireproof, waterproof, antifouling, mechanical, capable of eliminating peculiar smell, sterilizing, insulating heat, removing sound, protecting environment and the like. The temperature adjusting and humidity adjusting coating is applicable to various kinds of constructional coating.

Description

technical field [0001] The invention relates to the field of preparation of temperature-regulating and humidity-regulating coatings, in particular to a method for preparing a heat-insulating primer, a phase-change energy storage intermediate paint and a heat-conducting and humidity-regulating topcoat. Background technique [0002] With the rapid development of the construction industry, more and more attention has been paid to the performance of coatings such as temperature regulation, humidity regulation, fire prevention, waterproof, antifouling, deodorization, sterilization, heat insulation, noise reduction, mechanics and environmental protection. In particular, the temperature and humidity regulation performance of the paint can shorten the use time of the air conditioner, and even replace the air conditioner, effectively saving energy and alleviating the energy crisis. [0003] At present, there are harmful components in temperature-adjusting and heat-insulating coatings...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00
Inventor 张国庆尹振燕张庆杰李秀娟商春锋刘其鹏彭艳菲姚超
Owner LUNAN RES INST OF COAL CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap