Light cement foam insulation plate and production method thereof

A cement foaming and insulation board technology, applied in the field of building materials, can solve the problems of poor insulation performance, large strength attenuation, high water absorption, etc., and achieve good bonding effect, strong negative wind pressure resistance, and good weather resistance.

Active Publication Date: 2013-07-03
新疆青创建材有限公司
View PDF7 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the cement foam boards currently on the market use sulphoaluminate cement as the main raw material, which makes the product have relatively high early strength, large strength attenuation in the later stage, and relatively high capacity (mostly 250kg / m 3 -300kg / m 3 ), relatively poor thermal insulation performance, relatively high water absorption, high brittleness, relatively poor durability, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] A lightweight cement foam insulation board, which is composed of the following raw materials in parts by weight: 52.5 parts of ordinary Portland cement 76 parts, fly ash 44 parts, silicon fume 36 parts, river sand 18 parts, fluorite slag 12 parts, clay 8 parts, 16 parts of plant straw powder, 24 parts of water glass, 25 parts of vermiculite, 10 parts of foaming agent, 1.5 parts of foam stabilizer, 1.5 parts of hydroxyethyl cellulose, 4 parts of modified tree ash, high performance polycarboxylate 1 part of water reducer, 320 parts of water.

[0016] Wherein, the modified tree ashes are prepared by the following method: first soak the tree ashes with 15% hydrogen peroxide for 1.5 hours, then wash with distilled water, dehydrate, and add titanate coupling agent TMC equivalent to 1.5% of the weight of the tree ashes -TTS, 2.5% Ping Pingjia O, 3% sodium lauryl sulfate, 5% nano sepiolite powder, disperse at high speed for 25 minutes, dry, crush and grind into ultrafine powder...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
compressive strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
water absorptionaaaaaaaaaa
Login to View More

Abstract

The invention discloses a light cement foam insulation plate which comprises the following raw materials in parts by weight: 70-80 parts of 52.5 general silicate cement, 40-50 parts of coal ash, 30-40 parts of silicon powder, 15-20 parts of river sand, 10-15 parts of fluorite slag, 5-10 parts of argil, 15-20 parts of plant straw powder, 18-25 parts of water glass, 20-30 parts of vermiculite, 8-12 parts of foaming agent, 1-2 parts of foam stabilizing agent, 1-2 parts of hydroxyethyl cellulose, 3-5 parts of modified tree ash, 1-2 parts of polycarboxylate high-performance water-reducing agent and 300-360 parts of water. The cement foam plate produced with the method has the advantages of excellent insulation and construction performances, good bonding effect, no empty drum cracking phenomenon, strong negative air pressure resistance, high strength, light weight, pressure resistance, good weather resistance, environmental protection, energy saving, non-toxicity, harmlessness and the like, and has very wide market space and development prospect in the field of building energy-saving applications in our country.

Description

technical field [0001] The invention relates to a lightweight cement foam insulation board and a preparation method thereof, belonging to the field of building materials. Background technique [0002] With the popularization of building energy saving and the continuous improvement of people's demand for the comfort of living environment, thermal insulation materials have been paid more and more attention by people. The previously used organic and flammable insulation materials quickly withdraw from the market, such as polyurethane and polystyrene board. Inorganic non-combustible insulation materials have become the mainstream of building energy-saving insulation, such as rock wool boards, vitrified microbeads, and foamed cement insulation boards. However, the output of inorganic rock wool board and vitrified microbeads is low, which cannot meet the needs of the society. At the same time, the production of rock wool board consumes a lot of energy and pollutes the environment...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/02C04B28/04C04B18/24
CPCY02W30/91
Inventor 陈廷武
Owner 新疆青创建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products