Bioactive carbon fiber preparation method

A bioactive carbon fiber technology, applied in fiber treatment, fiber chemical characteristics, heat treatment of artificial filaments, etc., can solve the problems of low surface energy of bioactive carbon fiber, low strength of bioactive carbon fiber, unsuitable for a large amount of sewage, etc., to achieve good The effect of fiber diameter and pore size uniformity, good regeneration performance, and excellent catalytic degradation activity

Inactive Publication Date: 2013-07-31
LIYANG ZHUXI ACTIVATED CARBON
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In recent years, the production technology of activated carbon fiber has developed rapidly, and it also has related applications in water pollution control, biochemical reaction, food fermentation, etc. as a carrier of microorganisms. The surface energy of the bioactive carbon fiber prepared by this method is still not high, and further improvement is needed; at the same time, the bioactive carbon fiber prepared by this method has low strength and poor impact resistance, and is not suitable for the treatment of a large amount of sewage
[0005] Based on some deficiencies of the current bioactive carbon fiber, there is no report on its application as a biofilm carrier in water treatment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] (1) Dissolve 1.3g of bisphenol AF-aniline benzoxazine monomer (reagent model P8423) and 0.1g of benzylamine in 25.3g of N,N-dimethylformamide in a stirred tank at room temperature , the stirring speed is 100rpm, and the stirring time is 10min to obtain a benzoxazine solution with a mass concentration of 4.1%;

[0024] (2) At room temperature, add 2.1g of nylon 6 (molecular weight: 70,000) into the benzoxazine solution, stir at a speed of 500rpm, stir for 3h, and mix evenly to obtain a solution with a mass concentration of the blended material of 5.9%. ;

[0025] (3) Under the conditions of room temperature and relative humidity of 30%, the obtained mixed solution was input to the spinneret of the electrospinning equipment at a flow rate of 0.3mL / h, and the spinneret was connected to a 10kV power supply for electrostatic The benzoxazine composite nanofiber membrane is prepared by spinning, the receiving device is a copper mesh, and the distance between the receiving dev...

Embodiment 2

[0030] (1) Dissolve 8.1g of naphthol-aniline type benzoxazine monomer (reagent model P8417) and 1.4g of imidazole in 67.2g of tetrahydrofuran in a stirred tank at room temperature, the stirring speed is 150rpm, and the stirring time is 15min , to obtain a mass concentration of 12.4% benzoxazine solution;

[0031] (2) At room temperature, 17.3g of polyacrylonitrile (molecular weight: 90,000) was added to the benzoxazine solution, the stirring speed was 600rpm, and the stirring time was 5h. solution;

[0032] (3) Under the conditions of room temperature and relative humidity of 45%, the resulting blended solution was input to the spinneret of the electrospinning equipment at a flow rate of 1mL / h, and the spinneret was connected to an 18kV power supply for electrospinning Silk preparation of benzoxazine composite nanofiber membrane, the receiving device is aluminum foil, the distance between the receiving device and the spinneret is 15cm;

[0033](4) Put the obtained benzoxazin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention discloses a bioactive carbon fiber preparation method. The preparation method comprises the following steps: obtaining a benzoxazine solution; obtaining a mixed solution of blending polymers; obtaining a composite nanofiber; and preparing the bioactive carbon fiber. The preparation method is simple, the kinds and the application amounts of reaction reagents required by the method are less, and the cost is low. The bioactive carbon fiber prepared through the method has the advantages of extremely-high specific surface area, good fiber diameter and aperture uniformity, excellent mechanical performances and excellent heat stability.

Description

technical field [0001] The invention relates to a preparation method of bioactive carbon fiber. Background technique [0002] Bioactive carbon fiber is a new type of adsorption material prepared by combining carbon fiber and activated carbon technology. It has ultra-high specific surface area, micro-mesoporous multi-level structure, small pore size distribution, large adsorption capacity, fast adsorption and desorption speed, and easy regeneration. Features. At present, the raw materials of activated carbon fiber precursors are generally pitch, viscose fiber, polyacrylonitrile and phenolic resin, among which phenolic activated carbon fiber has higher carbonization yield, specific surface area and electrical conductivity than other activated carbon fibers received widespread attention. Bioactive carbon fiber is mainly used for environmental purification, and is mostly used as an excellent adsorbent for air purification, which can absorb hydrogen sulfide in gas and remove un...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F9/14D01F9/28D01F9/22D01D5/00D01D10/02
Inventor 陈静葛华林
Owner LIYANG ZHUXI ACTIVATED CARBON
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com