Silicone rubber for sealing two ends of heater

A heater and silicone rubber technology, applied in the field of rubber, can solve the problems of poor physical and mechanical properties, poor oil resistance, solvent resistance, poor mechanical properties such as tensile strength and tear resistance, and achieve long service life, Good sealing effect, effect of improving mechanical properties and surface resistance

Inactive Publication Date: 2015-02-25
滁州君越高分子新材料有限公司
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the mechanical properties of silicone rubber such as tensile strength and tear resistance are poor, and its physical and mechanical properties are not as good as most synthetic rubbers at room temperature. Poor, so silicone rubber is not suitable for ordinary conditions, so adding various additives to silicone rubber to improve its inherent properties can improve its overall quality and improve its applicability in various fields

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A kind of heater two ends sealing silicon rubber is characterized in that it is made up of the raw material of following weight part:

[0021] 1,4-cyclohexanedimethanol 1, vanadium diboride 0.4, polypropylene powder 3, accelerator TT2, thiocyanic acid 0.4, 2-mercaptobenzimidazole 0.7, 1-hydroxycyclohexylphenyl Methanone 2, superfine barium sulfate 17, dioctyl sebacate 13, calcium fluoride 3, butyl tin mercaptide 0.5, rare earth additive 4, methyl vinyl phenyl silicone rubber 110, sulfur 2, tetrahydrofuran 0.5 ;

[0022] Described rare earth additive is made up of the following raw materials of weight part:

[0023] Aluminum magnesium silicate 2, polyvinyl acetal 16, dodecanedioic acid 1-2, lanthanum chloride 6, methyl nylon acid 0.4, urea 0.6, formaldehyde 2, deionized water 130, ethylenediamine 0.3, calcium Zeolite 50;

[0024] Mix dodecanedioic acid and lanthanum chloride, add 30% of the weight of the above-mentioned deionized water, stir and mix for 40 minutes, ad...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strength at breakaaaaaaaaaa
elongationaaaaaaaaaa
rate of change of tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses silicone rubber for sealing two ends of a heater. The silicone rubber comprises the following raw materials in parts by weight: 1-2 parts of 1,4-cyclohexanedimethanol, 0.4-1 parts of vanadium diboride, 3-4 parts of polypropylene powder, 1-2 parts of accelerant TT, 0.4-1 part of trithiocyanuric acid, 0.7-1 part of 2-mercaptobenzimidazole, 1-2 parts of 1-hydroxycyclohexyl phenyl ketone, 10-17 parts of superfine barium sulfate, 10-13 parts of bis(2-ethylhexyl)sebacate, 2-3 parts of calcium fluoride, 0.5-1 part of butyltin mercaptide, 3-4 parts of rare earth auxiliaries, 100-110 parts of methyl vinyl phenyl siloxane rubber, 1-2 parts of sulfur, and 0.2-0.5 part of tetrahydrofuran, wherein the rare earth auxiliaries are prepared by the following steps: fully melting magnesium-aluminum silicate and colloid formed by polyvinyl acetal under the condition of taking deionized water as a solvent, so as to form stable and high-viscosity colloidal state, adding the treated acidified rare earth into the high-viscosity colloidal state system to form stable rare earth colloidal liquid, and then mixing and modifying with the esterified zeolite. By adopting the rare earth auxiliaries, not only can the mechanical performance and surface resistance of the finished products be effectively improved, but also the compatibility of materials can be enhanced, the stability of the finished products can be improved, the volume wear can be reduced by rare earth, and the wear resistance of the rubber can be improved.

Description

technical field [0001] The invention mainly relates to the field of rubber, in particular to a silicone rubber for sealing both ends of a heater. Background technique [0002] Silicone rubber has excellent heat resistance, cold resistance, dielectric properties, ozone resistance and atmospheric aging resistance. The outstanding performance of silicone rubber is that it can be used in a wide temperature range, which can be used at -60°C (or lower temperature) to +250°C. °C (or higher temperature) for long-term use. However, the mechanical properties of silicone rubber such as tensile strength and tear resistance are poor, and its physical and mechanical properties are not as good as most synthetic rubbers at room temperature. Therefore, silicone rubber is not suitable for use in ordinary conditions. Therefore, adding various additives to silicone rubber to improve its inherent properties can improve its overall quality and improve its applicability in various fields. C...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L83/07C08L23/12C08L29/14C08K13/06C08K9/04C08K3/16C08K3/34C08K3/30C08K5/11C08K3/38
Inventor 任兆军
Owner 滁州君越高分子新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products