Method for preparing denitrification catalyst with metatitanic acid as raw material in one step
A denitration catalyst, metatitanic acid technology, applied in chemical instruments and methods, catalyst activation/preparation, physical/chemical process catalysts, etc. High temperature activity, simplified preparation process and high catalytic activity
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0026] Example 1
[0027] Ammonia washing treatment of metatitanic acid
[0028] Put 300g of metatitanic acid in a beaker, add 500mL of water and stir, then add 70mL of 25% concentrated ammonia to adjust the pH to about 9.5. The mixture was transferred to a three-necked flask and stirred at 95°C under reflux for 3 hours. The mixture was subjected to liquid-solid separation by filtration, and the filter cake was washed three times with 500 mL of deionized water each time, and then the filter cake was dried in an oven at 120° C. for 12 hours to obtain metatitanic acid after ammonia washing treatment.
Example Embodiment
[0029] Example 2
[0030] Take 3.2 g of ammonium metavanadate, 1.16 g of ethanolamine, and 4.4 g of ammonium paratungstate to dissolve in water to prepare a 45 mL solution, mix with 30 g of metatitanic acid after ammonia washing treatment, and add to a ball mill tank for ball milling for 3 hours to obtain catalyst slurry. Cut 400cpsi cordierite honeycomb ceramic into small pieces of Φ1.4×2.2cm, weigh and immerse in the obtained catalyst slurry, take out after 30 seconds, blow off the remaining slurry in the pores with hot air, and then dry it in a microwave oven For 3 minutes, this process was repeated once to obtain the coated catalyst twice, and the catalyst was heated to 500°C at a rate of 2°C / min in a muffle furnace for 2 hours to obtain an overall denitration catalyst. The weight of the catalyst coating measured after being taken out and weighed was 0.631 g.
[0031] The denitration activity test method of the prepared catalyst is as follows: the integrally coated catalyst is...
Example Embodiment
[0032] Example 3
[0033] The preparation of the catalyst slurry was the same as in Example 2. Cut 400cpsi cordierite honeycomb ceramic into small pieces of Φ1.4×2.2cm, weigh and immerse in the obtained catalyst slurry, take out after 30 seconds, blow off the remaining slurry in the pores with hot air, and then dry it in a microwave oven For 3 minutes, this process was repeated twice to obtain a coated catalyst for three times, and it was heated in a muffle furnace at a rate of 2° C. / min to 500° C. and calcined for 2 hours to obtain an overall denitration catalyst. After being taken out and weighed, the weight of the catalyst coating measured was 1.1938 g.
[0034] The denitration activity test method of the prepared catalyst is as follows: the integrally coated catalyst is put into a quartz tube, and the reaction atmosphere is: 500ppm NO+500ppm NH 3 +5%O 2 +N 2 , Adjust the feed gas flow so that the reaction space velocity is 30000hr -1 . Separately detect NO and NO at import an...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap