Environment-friendly water-based nail polish and preparation method thereof

A nail polish, water-based technology, applied in manicure, pedicure, pharmaceutical formulations, etc., can solve problems such as polluting the environment and harming human health, and achieve the effects of simple preparation process, high gloss uniformity, and good hand feel

Active Publication Date: 2015-04-29
上海高庄生物科技有限公司
View PDF3 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to overcome the problems of polluting the environment and harming human health in the prior art, and provide a kind of environmental protection water-based nail polish and its preparation method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0037] A kind of preparation method of environmental protection water-based nail polish of the present invention comprises the following steps:

[0038] 1) First, add 4 to 18 parts of inert vinyl monomer, 9.48 to 13.35 parts of polymer polyol, 8.5 to 14 parts of diisocyanate compound, 0.8 to 2 parts of chain extender, 1.66 to 2.95 parts of Water chain extender, 0.15-0.3 parts of cross-linking agent and 0-0.095 parts of catalyst, the reaction temperature is 70-90°C, and the reaction time is 1-4 hours;

[0039] 2) Then, add 0.5-2 parts of vinyl monomers containing active hydrogen for capping, react for 0.5-1 hour, then cool the system temperature to 30-50°C, then add 1.3-3.2 parts of volatile base, and And react for 20-30 minutes, then add 60-100 parts of water, stir and disperse at high speed for 10-30 minutes, then raise the temperature to 70-90°C;

[0040] 3) Finally, at a temperature of 70-90°C, add an initiator solution (0.2-0.8 parts of initiator dissolved in 10-40 parts ...

Embodiment 1

[0044] 1) First, add 4 parts of methyl methacrylate, 9.9 parts of polycaprolactone diol, 8.5 parts of isophorone diisocyanate, 0.8 parts of 1,4-butanediol, 1.66 parts of dihydroxy Methylpropionic acid, 0.15 parts of trimethylolpropane and 0.01 part of catalyst dibutyltin dilaurate, the reaction temperature is 70 ° C, and the reaction time is 1 hour;

[0045] 2) Then, add 0.5 parts of hydroxyethyl acrylate for capping, react for 0.5 hours, then cool the system temperature to 30°C, then add 1.3 parts of ammonia water, neutralize and react for 20 minutes, then add 60 parts of water, stir and disperse at high speed 10 minutes, then heat up to 80°C;

[0046] 3) Finally, at a temperature of 80°C, add hydrogen peroxide solution (0.2 parts of initiator dissolved in 10 parts of water) to the reactor and drop it evenly into the reactor within 1 hour. After the addition is completed, continue to keep warm React for 1 hour to obtain an aqueous polyurethane emulsion;

[0047] 4) Add BYK-...

Embodiment 2

[0049] 1) First, add 4 parts of methyl acrylate and 5 parts of butyl acrylate, 11.5 parts of polycarbonate diol, 10.1 parts of hexamethylene diisocyanate, 1.3 parts of diethylene glycol chain extender into the dry reactor , 2.16 parts of dimethylolbutyric acid, 0.22 parts of glucose and 0.05 part of catalyst dibutyltin diacetate, the reaction temperature is 80 ° C, and the reaction time is 2.5 hours;

[0050]2) Then, add 1.2 parts of hydroxypropyl acrylate for capping, react for 0.6 hours, then cool the system temperature to 40°C, then add 1.9 parts of triethylamine, neutralize for 25 minutes, then add 75 parts of water, high-speed Stir and disperse for 20 minutes, then raise the temperature to 70°C;

[0051] 3) Finally, under the condition that the temperature is 70°C, add potassium persulfate solution (0.4 parts of initiator dissolved in 21 parts of water) to the reactor and drop it evenly into the reactor within 2 hours. After the dropwise addition, Continue the heat prese...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glossaaaaaaaaaa
Login to View More

Abstract

The invention discloses environment-friendly water-based nail polish and a preparation method thereof. The nail polish comprises waterborne polyurethane emulsion, an antifoaming agent, an accelerant, a thickening agent and pigments, wherein the waterborne polyurethane emulsion comprises the following components in parts by weight: 4-18 parts of an inert vinyl monomer, 9.48-13.35 parts of polymer polyol, 8.5-14 parts of a diisocyanate compound, 0.8-2 parts of a chain extender, 1.66-2.95 parts of a hydrophilic chain extender, 0.15-0.3 part of a cross-linking agent, 0-0.095 part of a catalyst, 0.5-2 parts of a vinyl monomer containing activated hydrogen, 1.3-3.2 parts of volatile alkali, 60-100 parts of water and initiator solution; and the initiator solution is prepared by dissolving 0.2-0.8 part of an initiator in 10-40 parts of water. The water-based nail polish disclosed by the invention is simple in preparation process, environmentally friendly and pollution-free and has environmental-friendly, non-toxicity and odorless performances.

Description

technical field [0001] The invention relates to a nail polish, in particular to an environment-friendly water-based nail polish and a preparation method thereof. Background technique [0002] Nail varnishes in use today are almost all manufactured based on binders containing organic solvents. Nail polishes produced by major international companies in the market are almost all composed of nitrocellulose, modified resins, and various mixed solvents. However, the solvents that can dissolve nitrocellulose are generally esters, ketones, benzenes, alcohols, etc. Ether and other volatile, irritating and toxic organic solvents can affect human health and cause environmental pollution. Therefore, reducing or even completely avoiding organic solvent components in conventional nail polishes has attracted great interest. Contents of the invention [0003] The object of the present invention is to overcome the problems of polluting the environment and harming human health existing in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61K8/87A61Q3/02C08G18/67C08G18/66C08G18/42C08G18/48C08G18/44
Inventor 赖小娟王磊付建萍宫米娜
Owner 上海高庄生物科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com