A moisture-retaining heat-insulating cement concrete curing agent and preparation method thereof

A technology of cement concrete and curing agent, which is applied in the field of moisturizing and heat insulating cement concrete curing agent and its preparation, and cement concrete curing agent, can solve the problems of insufficient water retention rate, small spray thickness, and inability to form film, so as to improve water retention efficiency, Reduce the effect of high temperature water loss, not easy to peel off

Active Publication Date: 2017-05-24
建发合诚工程咨询股份有限公司 +1
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Resins usually contain volatile solvents, which pollute the environment and endanger human health; latex-type curing agents have problems such as high cost, difficulty in removing the film after curing, and affecting the progress of subsequent projects; emulsions have obvious advantages, but also have small spray thickness , poor film density, small spraying area per unit mass, etc.
Inorganic curing agents are mainly silicate solutions, which reduce the evaporation rate of water by enhancing the surface compactness, but they cannot form a film and the water retention rate is insufficient
[0005] Chinese patent CN 103253985 B discloses a composite cement concrete curing agent and its preparation method. Although the film is compact and has good water retention, it is complicated to clean up as a coating with water-based epoxy resin.
[0006] Chinese patent CN103058544 B discloses a two-component curing agent for concrete. Due to the use of two-component film formation, it is necessary to spray twice, which will increase the cost of manual spraying.
Although the core-shell structure is adopted, because it is a solid core-shell structure, it has no heat insulation effect and the cost is high
[0008] To sum up, although there are many types of concrete curing agents at present, and the water retention properties meet the requirements, they generally do not have heat insulation performance, resulting in a large amount of coating and high cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A moisture-retaining and heat-insulating cement concrete curing agent described in Example 1 is composed by mass percentage: 40% of core-shell hollow soft monomer, 2% of emulsion stabilizer, 3% of film-forming aid, leveling The agent is 2%, and the rest is water.

[0040] The composition of the core-shell hollow polymer particles is core-shell hollow polystyrene particles; the composition of the emulsion stabilizer is a liquid barium zinc stabilizer; the composition of the film-forming aid can be a strong solvent of propylene glycol butyl ether; The composition of described leveling agent is polyurethane type leveling agent;

[0041] The preparation method of a moisture-retaining and heat-insulating cement concrete curing agent described in Example 1 comprises the following steps:

[0042] 1) Preparation of air core emulsion

[0043] Add foaming agent rosin, emulsifier oleic acid soap and silicone resin polyether emulsion foam stabilizer in water; the addition of foam...

Embodiment 2

[0055] A moisture-retaining and heat-insulating cement concrete curing agent described in Example 2 is composed by mass percentage: 30% of core-shell hollow soft monomer, 2% of emulsion stabilizer, 2% of film-forming aid, leveling The agent is 1%, and the rest is water.

[0056] The composition of the core-shell hollow polymer particles is core-shell hollow polyvinyl chloride particles; the composition of the emulsion stabilizer is a liquid calcium zinc stabilizer; the composition of the film-forming aid can be a strong solvent for alcohol ester twelve ; The composition of the leveling agent is a polyurethane leveling agent;

[0057] The preparation method of a moisturizing and heat-insulating cement concrete curing agent described in Example 2 includes the following steps.

[0058] 1) Preparation of air core emulsion

[0059] Add foaming agent rosin, emulsifier oleic acid soap and silicone resin polyether emulsion foam stabilizer in water; the addition of foaming agent rosi...

Embodiment 3

[0071] A moisture-retaining and heat-insulating cement concrete curing agent described in Example 3 is composed by mass percentage: 50% of core-shell hollow soft monomer, 1.5% of emulsion stabilizer, 3.5% of film-forming aid, leveling The agent is 2.5%, and the rest is water.

[0072] The core-shell hollow polymer particles are core-shell hollow polymethyl methacrylate particles; the emulsion stabilizer is a liquid barium zinc stabilizer; the film-forming aid is a strong solvent of propylene glycol butyl ether; the leveling The agent is an acrylic acid leveling agent.

[0073] The preparation method of a moisture-retaining and heat-insulating cement concrete curing agent described in Example 3 comprises the following steps:

[0074] 1) Preparation of air core emulsion

[0075] Add foaming agent rosin, emulsifier oleic acid soap and silicone resin polyether emulsion foam stabilizer in water; the addition of foaming agent rosin, emulsifier oleic acid soap and silicone resin po...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a moisture preserving heat insulating cement concrete curing agent and a preparation method thereof, and relates to a cement concrete curing agent. The moisture preserving heat insulating cement concrete curing agent comprises the following components: 30%-60% of core shell hollow polymer particles, 1%-2% of an emulsion stabilizer, 2%-8% of a film forming assistant, 0-5% of a leveling agent, and balance of water. A foaming agent, an emulsifier and a foam stabilizer are added into the water, and stirred to obtain a foam inner core, the formed foam bubbles can be stable to suspend in the water, and an air inner core emulsion is obtained; hard monomers are added into the air inner core emulsion, so that the hard monomers are gathered on gas-liquid interface of foam, a water soluble initiator is added for emulsion polymerization, the foam stabilizer is added, an inner layer core shell hollow polymer particles emulsion is obtained, then soft hydrophilic monomers are added for polymerization to obtain a core shell hollow polymer particles emulsion with a soft outer shell, and the emulsion stabilizer, the film forming assistant and the leveling agent are added to obtain the moisture preserving heat insulating cement concrete curing agent with good moisture preserving heat insulating effect.

Description

technical field [0001] The invention belongs to the technical field of cement concrete maintenance, and relates to a cement concrete curing agent, in particular to a moisturizing and heat-insulating cement concrete curing agent and a preparation method thereof. Background technique [0002] As the most widely used material in the world, concrete plays an irreplaceable role in engineering. Concrete technology is a systematic project, which is closely related to all links from proportioning design, mixing, transportation, pouring, vibration to maintenance. Any problem in any link will have a serious impact on the quality of concrete. The early maintenance of concrete is an important part of concrete quality assurance. Improper early maintenance will lead to cracking due to drying shrinkage of concrete, surface dehydration and insufficient hydration will affect the strength and durability of concrete, and excessive internal and external temperature differences will also acceler...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B24/26
Inventor 程棋锋陈天培沈志献刘向东李建文康明旭李雪健林东明
Owner 建发合诚工程咨询股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products