High-elasticity vibration-resistant expanded polyethylene plate and method for manufacturing same

A foamed polyethylene and high-elasticity technology, applied in the field of high-elasticity and shock-resistant foamed polyethylene sheets and their preparation, can solve the problems of poor bending strength, compressive strength and heat resistance, low rigidity and hardness, and improve mechanical properties. , Increase the effect of flame retardant, improve strength and aging resistance

Inactive Publication Date: 2015-09-09
周诗慧
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present, polyethylene foam materials still have deficiencies such as poor bending strength, compressive strength and heat resistance, low rigidity and hardness, which limit its application.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A highly elastic and shock-resistant foamed polyethylene sheet, prepared from the following raw materials in parts by weight (kg): polyethylene 120, ethylene-vinyl acetate copolymer 20, p-toluenesulfonyl hydrazide 10, dichlorotetrafluoroethane 5 , Dicumyl peroxide 3, Zinc oxide 7, Titanate modified calcium carbonate 40, Leucite powder 8, Isobutyltriethoxysilane 5, Magnesium stearate 6, Butyl stearate 4, Hexamethylenetetramine 4, polycarbonate 3, aluminum hydroxide 10, titanium nitride whisker 7, dioctyl adipate 6, 2-aminoethanol 3, dicyclohexyl phthalate 8, di Magnesium boride 7, jade powder 4.

[0016] A method for preparing a high-elastic shock-resistant foamed polyethylene sheet, comprising the following steps:

[0017] (1) Put polyethylene and ethylene-vinyl acetate copolymer in a mixer for 5-6 minutes, then add zinc oxide, titanate modified calcium carbonate, leucite powder, isobutyltriethoxysilane, Magnesium stearate, aluminum hydroxide, titanium nitride whi...

Embodiment 2

[0022] A highly elastic and shock-resistant foamed polyethylene sheet, prepared from the following raw materials in parts by weight (kg): polyethylene 130, ethylene-vinyl acetate copolymer 25, p-toluenesulfonyl hydrazide 12, dichlorotetrafluoroethane 6.5 , Dicumyl peroxide 4, Zinc oxide 8, Titanate modified calcium carbonate 45, Leucite powder 9, Isobutyltriethoxysilane 6, Magnesium stearate 7.5, Butyl stearate 5, Hexamethylenetetramine 4.5, polycarbonate 4, aluminum hydroxide 12, titanium nitride whisker 8, dioctyl adipate 7, 2-aminoethanol 4, dicyclohexyl phthalate 8.5, di Magnesium boride 8, jade powder 5.

[0023] The preparation method is the same as in Example 1.

Embodiment 3

[0025] A high-elastic shock-resistant foamed polyethylene sheet, characterized in that it is prepared from the following raw materials in parts by weight (kg): polyethylene 140, ethylene-vinyl acetate copolymer 30, p-toluenesulfonyl hydrazide 14, dichlorotetra Fluoroethane 8, dicumyl peroxide 5, zinc oxide 9, titanate modified calcium carbonate 50, leucite powder 10, isobutyltriethoxysilane 7, magnesium stearate 9, stearic acid Butyl ester 6, hexamethylenetetramine 5, polycarbonate 5, aluminum hydroxide 14, titanium nitride whisker 9, dioctyl adipate 8, 2-aminoethanol 5, dicyclohexyl phthalate Ester 9, magnesium diboride 9, jade powder 6.

[0026] The preparation method is the same as in Example 1.

[0027] The performance test results of the highly elastic anti-shock foamed polyethylene sheet made by above-mentioned embodiment 1-3 are shown in the following table:

[0028] Example 1 Example 2 Example 3 Tensile strength, Mpa 12.5 11.8 12.3 Impact...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-elasticity vibration-resistant expanded polyethylene plate and a method for manufacturing the same. The high-elasticity vibration-resistant expanded polyethylene plate comprises, by weight, 120-140 parts of polyethylene, 20-30 parts of ethylene-vinyl acetate copolymers, 10-14 parts of p-toluenesulfonhydrazide, 5-8 parts of dichlorotetrafluoroethane, 3-5 parts of dicumyl peroxide, 7-9 parts of zinc oxide, 40-50 parts of titanate-modified calcium carbonate, 8-10 parts of leucite powder, 5-7 parts of dynasylan ibteo, 6-9 parts of magnesium stearate, 4-6 parts of butyl stearate, 4-5 parts of hexamethylenetetramine, 3-5 parts of polycarbonate, 10-14 parts of aluminum hydroxide, 7-9 parts of titanium nitride whiskers, 6-8 parts of dioctyl adipate, 3-5 parts of 2-aminoethanol, 8-9 parts of dicyclohexyl phthalate, 7-9 parts of magnesium diboride and 4-6 parts of jade powder. The high-elasticity vibration-resistant expanded polyethylene plate and the method have the advantages that the polyethylene plate manufactured by the aid of the method not only is excellent in vibration-resistant and buffer performance, but also is high in mechanical strength and good in ageing resistant, and good flame-retardant effects can be realized.

Description

technical field [0001] The invention relates to a polyethylene sheet, in particular to a high-elasticity shock-resistant foamed polyethylene sheet and a preparation method thereof. Background technique [0002] Foamed polyethylene, commonly known as pearl cotton, is a new type of environmentally friendly packaging material with high-strength cushioning, shock-absorbing and shock-resistant capabilities. It is flexible, light, elastic, and has good resilience. It can absorb and disperse external impact by bending to achieve a cushioning effect. At the same time, foamed polyethylene has a series of superior performance characteristics such as heat preservation, moisture resistance, friction resistance and corrosion resistance. At present, it is widely used in the packaging of IT, electronics, electrical appliances, hardware and electromechanical, advanced audio-visual, precision instruments, high-end furniture, life jackets and other products. However, polyethylene foam mate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L23/08C08L69/00C08K13/06C08K9/04C08K5/14C08K3/22C08K3/34C08K5/5415C08K5/098C08K5/101C08K5/17C08K7/00C08K5/11C08K5/12C08K3/38C08J9/10C08J9/14
CPCC08L23/06C08J2323/06C08K2201/014C08L2205/025C08L2205/03C08L23/0853C08L69/00C08K13/06C08K9/04C08K5/14C08K2003/2296C08K3/34C08K5/5415C08K5/098C08K5/101C08K5/17C08K2003/2227C08K7/00C08K5/11C08K5/12C08K3/38C08J9/104C08J9/144
Inventor 周诗慧任浩楠陈逸涵李子健
Owner 周诗慧
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap