External wall applied water-based low temperature ultraviolet-curing coating

A curing coating, water-based technology, applied in coatings and other directions, can solve the problems of difficult popularization and application, low fluorine content, difficult processing, etc., and achieve the effects of convenient manufacturing, improved aging resistance and high production efficiency

Inactive Publication Date: 2015-09-30
CHENGDU NASHUO TECH
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although fluorine materials have the above advantages, the difficulty of processing has always been a difficulty that plagues the promotion of fluorine materials. For example, tetrafluoro compounds are insoluble in conventional solvents. As coatings, they must be sintered to form thin polymers. This m

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A water-based UV low-temperature curing coating for exterior walls, which is composed of the following raw materials in parts by mass: 90 parts of film-forming substance, 40 parts of ethyl acetate, 5 parts of stearic acid monoglyceride (GMS), 15 parts of talcum powder, and acrylic acid 2 parts of resin, 1 part of benzoin dimethyl ether, 2 parts of white carbon black.

Embodiment 2

[0024] A water-based ultraviolet low-temperature curing coating for exterior walls, which is composed of the following raw materials in parts by mass: 100 parts of film-forming substance, 10 parts of ethyl acetate, 40 parts of propylene glycol methyl ether acetate, and stearic acid monoglyceride (GMS) 5 Parts, 17 parts of talc, 1 part of polyethylene glycol, 1 part of acrylic resin, 1 part of urea-formaldehyde resin, 1 part of melamine formaldehyde resin, 1 part of benzoin dimethyl ether, 2-hydroxy-2-methyl-1-phenyl One part of acetone (UV-1173) and 2 parts of white carbon black.

Embodiment 3

[0026] A water-based ultraviolet light low-temperature curing coating for exterior walls, which is composed of the following raw materials in parts by mass: 110 parts of film-forming substance, 10 parts of ethyl acetate, 20 parts of ethanol, 20 parts of propylene glycol methyl ether acetate, and monoglyceride stearate ( GMS) 5 parts, talc 4 parts, polyethylene glycol 3 parts, acrylic resin 2 parts, urea-formaldehyde resin 1 part, melamine formaldehyde resin 1 part, benzoin dimethyl ether 1 part, 2,4,6-trimethylbenzene 2 parts of formyl-diphenyl phosphine oxide (TPO), 1 part of methyl benzoylformate (MBF), 3 parts of white carbon black.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an external wall applied water-based low temperature ultraviolet-curing coating, and belongs to the field of coatings, in particular to the field of ultraviolet-curing water-based coatings. The external wall applied water-based low temperature ultraviolet-curing coating consists of the following raw materials: a film-forming substance, a solvent, talcum powder, a dispersant, a leveling agent, a photoinitiator and white carbon black. The cured product of the fluorine-containing coating is good in performance, and samples obtained after curing are excellent in adhesion, scratch resistance and stain resistance.

Description

Technical field [0001] The invention belongs to the field of coatings, in particular to the field of water-based coatings cured by ultraviolet light. Background technique [0002] Light-curing water-based coatings combine the advantages of water-based coatings and light-curing solvent coatings, and have developed rapidly in recent years. Light-curing water-based coatings solve the inherent disadvantages of water-based paints such as low hardness, high energy consumption, and high requirements for the cleanliness of the construction process and the surface of the material; it solves the problems of unsafe light-curing solvent coatings and curing shrinkage, and realizes water-based environmental protection. Low cost and high efficiency application. With the further development of the research on light-curing hydrophilic coatings, the application range of light-curing hydrophilic coatings is becoming more and more extensive. It can be coated on metal, wood, plastic, leather, glass,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D4/02C09D4/06C09D7/12
Inventor 黄波
Owner CHENGDU NASHUO TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap