Acidic ammonium salt vanadium precipitation waste water recycling method
A technology for acidic ammonium salt vanadium precipitation and resource utilization, which is applied in the field of resource utilization of acidic ammonium salt vanadium precipitation wastewater, can solve the problems of high cost, complicated operation, and increased production cost of vanadium oxide, achieve qualified quality, and improve system yield , The clinker dipping process is smooth
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0035] Example 1
[0036] Take 500g of vanadium extraction residue as sand filter medium, 10L of wastewater is pretreated by sand filter and mixed with 150L of condensed water, and 1L of mixed solution is heated to 90℃; 475g of vanadium slag powder containing 8% vanadium, 120g of sodium carbonate, sand 470g of the filtered vanadium extraction residue is mixed uniformly, the temperature is programmed (6°C / min), the highest roasting temperature is 780°C, and the roasting time is 150min. The clinker obtained by roasting is immersed in the prepared mixture for 30 minutes soaking time. The vanadium-containing leaching solution is added with 1.5g of calcium chloride to remove P, and 50g of ammonium sulfate is added for vanadium precipitation, and the end point pH of the precipitation is 2.0. After testing, the TV of the residue is 1.02%, SV is 0.08%, and the conversion rate of vanadium is 88.0%; TV content in APV is 49.2%, Na content is 0.36%, and S content is 0.24%, all of which meet ...
Example Embodiment
[0037] Example 2
[0038] Take 500g of vanadium extraction residue as sand filter medium, 10L of wastewater is pretreated by sand filter and mixed with 100L of condensed water, and 1L of mixed solution is heated to 90℃; 475g of vanadium slag powder containing 8.3% vanadium, 120g of sodium carbonate, sand 470g of the filtered vanadium extraction residue is mixed uniformly, the temperature is programmed (7°C / min), the maximum roasting temperature is 780°C, and the roasting time is 150min. The clinker obtained by roasting is immersed in the prepared mixture and the soaking time is 30min. The vanadium-containing leaching solution was added with 1.7g calcium chloride to remove P, and 45 ammonium sulfate was added for vanadium precipitation. The end point pH of the precipitation was 2.0. After testing, the TV of the residue is 1.01%, SV is 0.09%, and the conversion rate of vanadium is 88.3%. The TV content of APV is 48.8%, Na content is 0.41%, and S content is 0.26%, which all meet the...
Example Embodiment
[0039] Example 3
[0040] Take 500g of vanadium extraction residue as sand filter medium, 10L of wastewater is pretreated by sand filter and mixed with 70L of condensed water, and 1L of mixed solution is heated to 90℃; 475g of vanadium slag powder containing 8.4% vanadium, 120g of sodium carbonate, sand 470g of the filtered vanadium extraction residue is mixed uniformly, the temperature is programmed (7°C / min), the maximum roasting temperature is 780°C, and the roasting time is 150min. The clinker obtained by roasting is immersed in the prepared mixture and the soaking time is 30min. The vanadium-containing leaching solution was added with 1.8g calcium chloride to remove P, and 47 ammonium sulfate was added for vanadium precipitation. The pH value of the precipitation end point was 2.0. After testing, the TV of the residue was 1.02%, SV was 0.09%, and the conversion rate of vanadium was 87.8%. The TV content in APV is 48.6%, Na content is 0.49%, and S content is 0.28%, all of whi...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap