Vanadium iron slag-corundum slag coating for lost foam casting and manufacturing method thereof

A technology of lost foam casting and corundum slag, which is applied to casting molding equipment, coatings, casting molds, etc. It can solve the problems of environmental hazards and other problems, and achieve the effects of improving fire resistance limit, improving cohesiveness and dispersion, and stabilizing the structure

Inactive Publication Date: 2015-11-11
张燕
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the traditional production process of vanadium products, a large amount of waste slag is produced, such as vanadium extraction tailings, vanadium iron slag, waste sodium sulfate, etc. The stacking treatment will cause great harm to the surrounding environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A vanadium iron slag-corundum slag lost foam casting coating is characterized in that, the lost foam casting coating is composed of the following raw materials in parts by weight:

[0045] 25 parts vanadium iron slag

[0046] 22 parts corundum slag

[0047] 11 parts magnesia

[0048] 6 parts kaolin

[0049] Silicon carbide 6 parts

[0050] Zinc-aluminum spinel fine powder 2 parts

[0051] brucite 2 parts

[0052] 2 parts glass powder

[0053] 2 parts meerschaum powder

[0054] 2 parts siliceous shale powder

[0055] 4 parts of isocyanate propyl triethoxysilane

[0056] 6 parts of isopropoxy tris(dodecylbenzenesulfonyl) titanate

[0057] 2 parts of isobutanol etherified melamine methyl ether resin

[0058] Dicumyl peroxide 0.3 parts

[0059] 0.4 parts of polyvinyl alkyl alcohol ether

[0060] Tertiary vinegar emulsion 0.3 parts

[0061] 2 parts asbestos fiber

[0062] 1 part starch

[0063] Sodium dodecyl sulfonate 2 parts

[0064] 1 part pentaerythritol

...

Embodiment 2

[0073] A vanadium iron slag-corundum slag lost foam casting coating is characterized in that, the lost foam casting coating is composed of the following raw materials in parts by weight:

[0074] 33 parts of ferrovanadium slag

[0075] 28 parts corundum slag

[0076] 13 parts magnesia

[0077] 9 parts kaolin

[0078] Silicon carbide 8 parts

[0079] Zinc-aluminum spinel fine powder 5 parts

[0080] brucite 5 parts

[0081] 4 parts glass powder

[0082] 3 parts meerschaum powder

[0083] 4 parts siliceous shale powder

[0084] 6 parts of isocyanate propyltriethoxysilane

[0085] 8 parts of isopropoxy tris(dodecylbenzenesulfonyl) titanate

[0086] 4 parts of isobutanol etherified melamine methyl ether resin

[0087] Dicumyl peroxide 0.4 parts

[0088] 0.5 parts of polyvinyl alkyl alcohol ether

[0089] Tertiary vinegar emulsion 0.5 parts

[0090] 3 parts asbestos fiber

[0091] 3 parts starch

[0092] Sodium dodecyl sulfonate 3 parts

[0093] 3 parts pentaerythri...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Mohs hardnessaaaaaaaaaa
Login to View More

Abstract

Vanadium iron slags, corundum slags, magnesite, kaoline, silicon carbide, zinc-aluminum oxide spinel fine powder, brucite, glass powder, sea-foam stone powder, siliceous shale powder, isocyanate propyl group triethoxy silane, isopropoxy tri-(dodecylbenzene) titanate, isobutanol etherified melamine methyl ether resin, dicumyl peroxide, polyethylene alcohol ether, tert-acetic emulsion, asbestos fiber, starch, sodium dodecyl sulfate, pentaerythritol, sodium benzoate, ethanol and water are used as raw materials, and a coating with the good using performance and low production cost for lost foam casting is obtained. The purposes of comprehensively recycling the vanadium iron slags and the corundum slags and lowering the production cost are achieved.

Description

technical field [0001] The invention belongs to the field of lost foam casting coatings, and in particular relates to a vanadium iron slag-corundum slag lost foam casting coating and a preparation method thereof. Background technique [0002] Lost foam casting technology is a new casting process in the foundry industry. The lost foam casting process refers to making foam plastic (EPS, ETMMA or EPMMA) into the shape, structure and size of the required castings. After the refractory coating is dried, it is embedded in a special sand box with dry sand (usually quartz sand) for molding, and then poured under a certain negative pressure. Lost foam casting is mainly called dry sand solid mold casting and negative pressure solid mold casting in China, and it is referred to as EPC casting abroad. [0003] At present, the most mature lost foam casting process is used in the mass production of automotive castings. The products produced include aluminum alloy castings (such as intake ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22C3/00
Inventor 张燕
Owner 张燕
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com