Preparation method of tissue engineering porous extracellular matrix scaffold

A technology of tissue engineering and extracellular matrix, which is applied in the field of preparation of porous extracellular matrix scaffolds for tissue engineering, can solve problems such as limiting the application of decellularized scaffolds, and achieve the effect of broadening the scope of application

Active Publication Date: 2016-05-11
NANKAI UNIV
View PDF3 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The existence of these problems also limits the further application of decellularized scaffolds

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0011] Example 1: Preparation of nanopore cell matrix scaffold material

[0012] Preparation of PCL nanofiber scaffold: Weigh 1.0 g of PCL with a molecular weight of 80,000, add it to 10 ml of dichloromethane, stir and dissolve at room temperature until clear, and prepare a PCL solution with a concentration fraction of 10% (m / v). Electrospinning was performed at room temperature with a relative humidity of 60%. Cover the electrospinning drum receiving device with aluminum foil and ground it, fill the 10% (m / v) PCL spinning solution into a disposable syringe with a diameter of about 14.95 mm, and connect the high voltage DC power supply to the syringe needle. Adjust the syringe needle to the center of the cylindrical receiver, set the distance between the needle and the receiver to 12 cm, the solution flow rate to 1 ml / h, the DC voltage to 16 kV, and the spinning time to 40 min. After the preparation is completed, the obtained membrane scaffold material is vacuum-dried at room...

Embodiment 2

[0017] Example 2: Preparation of cell matrix scaffold material with micron pore size

[0018] Preparation of PLA microfiber scaffold: The scaffold was prepared in a fume hood at room temperature by wet spinning. Dissolve 1 gram of polylactic acid in 10 ml of hexafluoroisopropanol, and stir at room temperature until the solution is clear. Connect a cylinder with a diameter of 3 cm to a rotating motor. The polylactic acid spinning solution was sucked into the syringe, and the needle of the syringe was placed in the ethanol coagulation bath at a position 1 cm away from the receiving cylinder. Set the flow rate of the solution to 2ml / h, the rotational speed of the receiving rod to 500rpm, and the spinning time to 40min. After the preparation is completed, the micron fiber scaffold is vacuum-dried for future use.

[0019] Subcutaneous implantation of the PLA microfiber scaffold: cut the PLA microfiber scaffold obtained above into strips of 4 cm×2 cm, sterilize with 75% medical a...

Embodiment 3

[0023] Example 3: Preparation of cell matrix scaffold material with large pore size

[0024] Preparation of PCL crude fiber scaffold: the scaffold was prepared at room temperature by melt spinning. 20 grams of PCL was added to the barrel. Raise the temperature of the barrel to 90°C for 5 hours, adjust the distance between the needle of the barrel and the receiving plate, set the advancing speed of the barrel to 6ml / h, the moving speed of the x-axis and y-axis of the receiving plate to 1mm / s, and the moving distance It is 15cm, and the spinning time is 60min. After the preparation is completed, the crude fiber scaffold is vacuum-dried for future use.

[0025] Subcutaneous implantation of the PCL crude fiber scaffold: cut the PCL crude fiber scaffold obtained above into a rectangle of 10 cm×8 cm, and sterilize it with ethylene oxide before use. After the sheep were anesthetized, the two sides of the back were shaved with a size of 12 cm × 2 cm, and an 11 cm long incision was ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a preparation method of a tissue engineering porous extracellular matrix scaffold. The method is characterized in that a nano or micron polymer scaffold is implanted under the skin of or in the abdomen of a host, the polymer scaffold is used as a template to prepare the tissue engineering porous extracellular matrix scaffold with a controllable pore structure and free of immunogenicity after in-vivo implantation by using a host immunoprotection mechanism. The preparation method has the advantages that the problem of hole forming of extracellular matrix scaffold materials is solved; the porous scaffold is animal-source, is used for repairing self-injured tissue or organs, and is free of immunological rejection; since self-repair has no complex decellularization step, the scaffold has significantly better mechanical strength than a decelluarized scaffold material; the extracellular matrix scaffold may be further decelluarized for repairing foreign tissue or organs and has a promising application prospect in the field of organ repairing.

Description

technical field [0001] The invention relates to a method for preparing a porous scaffold in the field of tissue engineering, in particular to a method for preparing a porous extracellular matrix scaffold for tissue engineering. Background technique [0002] The development of tissue engineering has opened up a new path for the repair of human tissue and organ defects. At present, scientists have developed a variety of tissue engineering products and used them clinically, and achieved good results. Tissue engineering mainly includes three aspects: scaffolds, cells and signaling factors. Tissue engineering scaffold materials can be implanted in the body to match the corresponding tissues and organs, including tissue scaffold materials for bone, cartilage, nerves, blood vessels, skin and artificial organs, such as liver, kidney, spleen, urethra, etc. Scaffold materials need to meet the following conditions: good biocompatibility; controllable degradation rate; high porosity; s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L27/56A61L27/38A61L27/36A61L27/50
Inventor 朱美峰孔德领王恺王淑芳李雯
Owner NANKAI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com