Heat-resisting chlorinated polyvinyl chloride material for power cable
A chlorinated polyvinyl chloride and power cable technology, applied in the field of polyvinyl chloride, can solve the problems of poor heat resistance and impact resistance, high melt viscosity and processing temperature, and decreased physical and mechanical properties, and achieves improvement. Melt fluidity, good compatibility, and the effect of improving processability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0018]A heat-resistant chlorinated polyvinyl chloride material for power cables proposed by the present invention, its raw materials include the following components in parts by weight: 87.5 parts of chlorinated polyvinyl chloride, 19 parts of polyvinyl chloride, 1.86 parts of marble, and 3.8 parts of calcium carbonate , 5 parts of calcined kaolin, 2.6 parts of calcium stearate, 1.78 parts of zinc stearate, 0.75 parts of dibutyltin dilaurate, 2.23 parts of butyl stearate, 3.4 parts of oxidized polyethylene wax, 16.7 parts of aluminum hydroxide, hydrogen 11.3 parts of magnesium oxide, 2.3 parts of tricresyl phosphate, 4 parts of bis(2-ethylhexyl)phenyl phosphate, 1.35 parts of tris(2-ethylhexyl) phosphate, 2.38 parts of polystyrene, polyglutaryl 1.34 parts of amine, 1 part of stearyl alcohol, 1.86 parts of silane coupling agent, and 1.3 parts of antioxidant.
Embodiment 2
[0020] A heat-resistant chlorinated polyvinyl chloride material for power cables proposed by the present invention, its raw materials include the following components in parts by weight: 75 parts of chlorinated polyvinyl chloride, 25 parts of polyvinyl chloride, 0.5 part of marble, and 6 parts of calcium carbonate , 2 parts of calcined kaolin, 3 parts of calcium stearate, 0.8 parts of zinc stearate, 0.8 parts of dibutyltin dilaurate, 1 part of butyl stearate, 4 parts of oxidized polyethylene wax, 8 parts of aluminum hydroxide, hydrogen 3 parts of magnesium oxide, 1 part of tricresyl phosphate, 5 parts of bis(2-ethylhexyl)phenyl phosphate, 1.5 parts of tris(2-ethylhexyl) phosphate, 2.5 parts of polystyrene, polyglutaryl 0.3 parts of amine, 2 parts of stearyl alcohol, 0.3 parts of silane coupling agent KH-5500, 2 parts of n-octadecyl alcohol ester of β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionate; among them, The chlorinated polyvinyl chloride is a modified chlorinated polyviny...
Embodiment 3
[0022] A heat-resistant chlorinated polyvinyl chloride material for power cables proposed by the present invention, its raw materials include the following components in parts by weight: 90 parts of chlorinated polyvinyl chloride, 10 parts of polyvinyl chloride, 2 parts of marble, and 1 part of calcium carbonate , 8 parts of calcined kaolin, 1.5 parts of calcium stearate, 2 parts of zinc stearate, 0.2 parts of dibutyltin dilaurate, 2.3 parts of butyl stearate, 0.3 parts of oxidized polyethylene wax, 20 parts of aluminum hydroxide, hydrogen 15 parts of magnesium oxide, 2.8 parts of tricresyl phosphate, 0.3 parts of bis(2-ethylhexyl)phenyl phosphate, 0.3 parts of tris(2-ethylhexyl) phosphate, 1 part of polystyrene, polyglutaryl 1.5 parts of amine, 0.3 part of stearyl alcohol, 1 part of silane coupling agent KH-5601, 1 part of silane coupling agent A-1511, 0.3 part of N, N'-di-β-naphthyl-p-phenylenediamine; wherein, the Chlorinated polyvinyl chloride is modified chlorinated polyv...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com