Wear-resisting enhancement polyurethane polystyrene foam for switch cabinet sealing

Abstract

The invention discloses wear-resisting enhancement polyurethane polystyrene foam for switch cabinet sealing. The wear-resisting enhancement polyurethane polystyrene foam is prepared from, by weight, 150-160 parts of diphenyl-methane-diisocyanate, 100-105 parts of propoxylated glycerin, 100-110 parts of castor oil, 5-6 parts of glycerin, 40-43 parts of diethyl phosphate, a proper amount of 1 mol/L sodium hydroxide solution, 13-15 parts of kieselguhr, 5-6 parts of distilled water, 2-3 parts of triethanolamine, 3-4 parts of dibutyltin dilaurate, 3-4 parts of sorbitan ester, 3-4 parts of silicon resin polyether emulsion, 3-4 parts of silicon carbide, 2-3 parts of fumed silica, 2-3 parts of EVA emulsion, 2-3 parts of polyvinyl alcohol, 1-1.5 parts of nickel powder and a proper amount of deionized water. The wear-resisting enhancement polyurethane polystyrene foam is used for switch cabinet sealing, on-site foaming can be conducted, foam cells are dense, sealing performance is high, wear resistance is high, and service life is long.

Description

technical field [0001] The invention relates to the technical field of styrofoam, in particular to a wear-resistant reinforced polyurethane styrofoam used for sealing switch cabinets. Background technique [0002] Two-component polyurethane adhesive is the most important type of polyurethane adhesive, usually composed of A component (main agent) and B component (curing agent), where A component is a hydroxyl component, B component For components containing free isocyanate groups, the two are packaged separately and can be formulated and used in a certain proportion. In our country, the research on foaming two-component polyurethane adhesives began in 1995 and was gradually put into use in the late 1990s. The foaming two-component polyurethane adhesive has the characteristics of porosity, low relative density, and high specific strength. According to different raw materials and formulas, it can be made into ordinary soft foam, hard foam, high-resilience foam and slow-rebound...

AI Technical Summary

Problems solved by technology

The traditional sealing process is to use the physical bonding method to bond the standard seal to the sealing position. This method has many defects such as low production efficiency, poor reliability, and unsightly appearance.

[0003] In the article "Preparation of Foaming Two-Component Polyurethane Adhesive", trihydroxypolyoxypropylene ether, castor oil and diphenylmethane diisocyanate are used as the main raw materials, glycerol is used as the chain extender, and water is used as the foaming agent. , through a suitable proportion, a foaming two-component polyurethane adhesive was synthesized by pre-polymerization method. The foamed adhesive foam was uniform and delicate, with high tensile and shear strength and excellent comprehensive performance. , but its heat resistance is poor and it is easy to burn. When it is used as the seal of a switch cabinet or a cabinet, it cannot meet the safety of use. This requires strengthening and modifying its thermal stability to improve its flame retardant performance.