Environment-friendly medium-density fiber board excellent in fireproofing performance and preparation method thereof

An environmentally friendly, medium-density technology, applied in the field of materials, to achieve good application prospects, cheap raw materials, and simple processes

Inactive Publication Date: 2017-02-15
苏州佰思科节能环保科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

So now we have developed a composite fiberboard with good fire resistance, environmental protection and no pollution, which can effectively make up for the shortcomings of traditional wood materials such as flammability and low density, and play a certain role in promoting the development of the industry.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] (1) Weigh 10 parts of wood scraps, 5 parts of crop straws, 5 parts of coconut fiber, 4 parts of silicon carbide, 5 parts of polyurethane, 3 parts of petroleum ether, and 4 parts of polyethylene glycol-p-toluenesulfonate according to parts by weight. , 4 parts of carbonic acid fiber, 1 part of magnesium hydroxide, 1 part of zinc borate, 3 parts of o-hydroxymethyl benzoic acid lactone, 1 part of trichloroisocyanuric acid, 1 part of diethylthiocarbamoyl chloride, 3-urea 1 part of propyl propyltrimethoxysilane, 2 parts of ethyl 3,4-dihydroxybenzoate, 2 parts of dibutyl phthalate;

[0025] (2) Add wood scraps, crop stalks, and coconut fiber into 0.5% sodium hypochlorite solution for soaking, softening and disinfection, soaking time is 3 hours;

[0026] (3) Dry the softened mixture for stirring and cutting, and then pour it into a hot mill, while adding silicon carbide and ethyl 3,4-dihydroxybenzoate. The heating temperature of the hot mill is 450°C and the stirring speed is 1000 ...

Embodiment 2

[0033] (1) Weigh 13 parts of wood scraps, 7 parts of crop straws, 7 parts of coconut fiber, 5 parts of silicon carbide, 9 parts of polyurethane, 4 parts of petroleum ether, and 5 parts of polyethylene glycol-p-toluenesulfonate according to parts by weight. , Carbonate fiber 5 parts, magnesium hydroxide 1 part, zinc borate 1 part, o-hydroxymethyl benzoic acid lactone 4 parts, trichloroisocyanuric acid 1 part, diethyl thiocarbamoyl chloride 2 parts, triethoxy 2 parts of methylsilyl-1-propylamine, 2 parts of tert-butyl p-hydroxyanisole, 3 parts of triphenyl phosphite;

[0034] (2) Add wood scraps, crop stalks, and coconut fiber into 0.5% sodium hypochlorite solution for soaking, softening and disinfection, soaking time is 4 hours;

[0035] (3) Dry the softened mixture for stirring and cutting, and then pour it into a hot mill, while adding silicon carbide and tert-butyl p-hydroxyanisole. The heating temperature of the hot mill is 500°C, and the stirring speed is 1100 revolutions per m...

Embodiment 3

[0042] (1) Weigh 16 parts of wood scraps, 8 parts of crop straws, 9 parts of coconut fiber, 6 parts of silicon carbide, 12 parts of polyurethane, 5 parts of petroleum ether, and 8 parts of polyethylene glycol-p-toluenesulfonate according to parts by weight. , Carbonate fiber 8 parts, magnesium hydroxide 2 parts, zinc borate 2 parts, o-hydroxymethyl benzoic acid lactone 4 parts, trichloroisocyanuric acid 2 parts, diethyl thiocarbamoyl chloride 2 parts, vinyl- 3 parts of tris(2-methoxyethoxy)silane, 3 parts of cyclohexanol phosphate, 4 parts of polythiol;

[0043] (2) Add wood scraps, crop stalks, and coconut fiber into 0.5% sodium hypochlorite solution for soaking, softening and disinfection, soaking time is 5 hours;

[0044] (3) Dry the softened mixture for stirring and cutting, and then pour it into a hot mill, while adding silicon carbide and cyclohexanol phosphate. The heating temperature of the hot mill is 550°C, the stirring speed is 1200 rpm, and the heat The grinding time i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environment-friendly medium-density fiber board excellent in fireproofing performance and a preparation method thereof. The environment-friendly medium-density fiber board excellent in the fireproofing performance is prepared from the following raw materials in parts by weight: 10 to 18 parts of wood scrap, 5 to 9 parts of crop straw, 5 to 10 parts of coconut shred fiber, 4 to 7 parts of silicon carbide, 5 to 15 parts of polyurethane, 3 to 6 parts of petroleum ether, 4 to 9 parts of polyethylene glycol-p-tosylate, 4 to 9 parts of carbonic acid fiber, 1 to 2 parts of magnesium hydroxide, 1 to 3 parts of zinc borate, 3 to 5 parts of o-hydroxymethylbenzoic acid lactone, 1 to 2 parts of symclosene, 1 to 3 parts of diethylthiocarbamoyl chloride, 1 to 4 parts of silane coupling agent, 2 to 3 parts of antioxidant and 2 to 5 parts of adhesive. The prepared environment-friendly medium-density fiber board excellent in the fireproofing performance has the fireproofing performance, and is environmentally friendly and free from pollution.

Description

Technical field [0001] The invention relates to the field of materials, in particular to an environmentally-friendly medium-density fiberboard with excellent fireproof performance and a preparation method thereof. Background technique [0002] Wood is a natural composite material with the widest application range and the longest history. It is composed of 50-55% cellulose, 15-25% hemicellulose and 20-30% lignin as main components. Composite materials. According to its structural characteristics, wood can be regarded as an aggregate of oriented fibers in an amorphous substrate, and the unique chemical and organizational structure of wood can be used to modify the wood to achieve the purpose of improving its performance and imparting new functions. Wood composite material is a new type of material with special microstructure and performance composed of wood materials and other materials. Through the use of the composite effect of wood and other materials, the inherent shortcoming...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L97/02C08L75/04C08L71/02C08K13/04C08K7/08C08K3/34C08K3/22C08K3/38C08K5/134C08K5/3492B29C47/92B29C48/92
CPCC08L97/02B29C48/92B29C2948/9258B29C2948/92704C08L2201/02C08L2205/025C08L2205/035C08L2205/16C08L75/04C08L71/02C08K13/04C08K7/08C08K3/34C08K2003/2224C08K2003/387C08K5/1345C08K5/34924
Inventor 费根华
Owner 苏州佰思科节能环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com