Low-temperature-resistant solvent-free and thick-film type epoxy anticorrosive paint
An epoxy anti-corrosion coating, solvent-free technology, applied in the direction of anti-corrosion coatings, epoxy resin coatings, polyurea/polyurethane coatings, etc., can solve the problems of coating peeling, small film thickness at one time, and large solvent content, etc., to achieve anti-corrosion Good crystallinity at low temperature, enhanced thixotropic stability, low viscosity and no solvation effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0025] Example 1
[0026] The epoxy anticorrosive coating of this embodiment is made by uniformly mixing component A and component B in a weight ratio of 3:1.
[0027] The A component contains the following ingredients: 100kg of composite toughened epoxy resin, 30kg of anti-sagging gel, 35kg of precipitated barium sulfate, 5kg of iron oxide red, 40kg of talc, 40kg of sericite, BYK-A530 defoamer 2kg, Germany BYK BYK-3550 leveling agent 2kg, Germany BYK-R605 thixotropic agent 3kg; the composite toughened epoxy resin is pre-blocked by the composite epoxy resin and the toughening agent polymerized phenolic phenol The polymer (Bayer XP2540) is mixed according to the weight ratio of 100:30; the anti-sag gel is made of silane coupling agent KH560, fumed silica, nano titanium dioxide and composite epoxy resin according to 8:8:20:100 The composite epoxy resin is made of bisphenol A epoxy resin E51, bisphenol F epoxy resin 170, 1,4-butanediol diglycidyl ether and polypropylene glycol diglyc...
Example Embodiment
[0040] Example 2
[0041] The epoxy anticorrosive coating of this embodiment is made by uniformly mixing component A and component B in a weight ratio of 4:1.
[0042] The A component contains the following components by weight: 100kg of composite toughened epoxy resin, 20kg of anti-sagging gel, 50kg of precipitated barium sulfate, 10kg of iron oxide red, 40kg of sericite, 30kg of talc, BYK-A530 4kg of defoamer, 4kg of BYK-3550 leveling agent in Germany; the composite toughened epoxy resin is a polypropylene glycol ether polyurethane prepolymer (Bayer XP2540) capped by a composite epoxy resin and a toughening agent polymerized phenol according to 100 : 10 by weight ratio; the anti-sagging gel is made by mixing silane coupling agent KH550, fumed silica, nano titanium dioxide and composite epoxy resin in a weight ratio of 8:5:30:100; The composite epoxy resins are all made by mixing bisphenol A epoxy resin E51 and bisphenol F epoxy resin 170 at a weight ratio of 70:30.
[0043] The B...
Example Embodiment
[0054] Example 3
[0055] The epoxy anticorrosive coating of this embodiment is made by uniformly mixing component A and component B in a weight ratio of 3:1.
[0056] The A component contains the following components by weight: 100kg of composite toughened epoxy resin, 50kg of anti-sagging gel, 50kg of precipitated barium sulfate, 50kg of talc, and 5kg of BYK-A530 defoamer from Germany; The tough epoxy resin is made by mixing a composite epoxy resin and a polypropylene glycol ether polyurethane prepolymer (Bayer XP2540) terminated by a toughening agent polymerized phenol according to a weight ratio of 100:50; the anti-sag gel is made of a silane coupling agent KH560, fumed silica, nano titanium dioxide and composite epoxy resin are mixed in a weight ratio of 10:10:5:100; the composite epoxy resin is made of bisphenol A type epoxy resin E44, bisphenol F type Epoxy resin 170 and polypropylene glycol diglycidyl ether are mixed uniformly according to the weight ratio of 50:30:30.
[0...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap