A kind of antistatic composite film

A composite film, anti-static technology, applied in the direction of synthetic resin layered products, chemical instruments and methods, layered products, etc., can solve the problems of anti-static film difficult to handle, to improve mechanical strength, protect the environment, improve tear resistance The effect of crack performance

Active Publication Date: 2019-04-30
SHANDONG ZHONGSU TAIFU TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The existing anti-static film basically needs to mix a large amount of conductive metal into the film material, which makes it difficult to handle the anti-static film during recycling.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Preparation of modified conductive polyaniline fibers: first soak polyester in 10wt% aniline hydrochloric acid-potassium dichromate solution for 1 hour to make the surface of the fibrils absorb aniline monomer, then add aniline hydrochloric acid-potassium dichromate solution 2wt% The hydrochloric acid-potassium dichromate solution of ammonium persulfate and aniline 1wt% nickel nitrate can obtain the modified polyaniline conductive fiber.

[0023] The preparation method of antistatic composite film comprises the following steps: mixing modified conductive polyaniline fiber, linear low-density polyethylene, silane coupling agent, solvent oil, and antioxidant to obtain a mixture; Extruded in the layer co-extrusion blown film machine, cooling promptly obtains described composite antistatic film; Described modified conductive polyaniline fiber is 10% of mixture quality, and described silane coupling agent is 5% of mixture quality, Solvent oil is 5% of the quality of the mixt...

Embodiment 2

[0025] Preparation of modified conductive polyaniline fibers: first soak polyester in 5wt% aniline hydrochloric acid-potassium dichromate solution for 3 hours to make the surface of the fibrils absorb aniline monomer, then add aniline hydrochloric acid-potassium dichromate solution 4wt% Sodium iodate and aniline hydrochloric acid-potassium dichromate solution 1wt% copper nitrate to obtain the modified polyaniline conductive fiber.

[0026] The preparation method of antistatic composite film comprises the following steps: mixing modified conductive polyaniline fiber, linear low-density polyethylene, silane coupling agent, solvent oil, and antioxidant to obtain a mixture; Extruded in the layer co-extrusion blown film machine, cooling promptly obtains described composite antistatic film; Described modified conductive polyaniline fiber is 10% of mixture quality, and described silane coupling agent is 5% of mixture quality, Solvent oil is 5% of the quality of the mixture, and the a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an anti-static composite film. The anti-static composite film comprises a polyurethane base layer, and an anti-static layer arranged on the polyurethane base layer; the anti-static layer is a linear low density polyethylene polymer layer containing modified conductive polyaniline fiber; and the content of the modified conductive polyaniline fiber in the linear low density polyethylene polymer layer is controlled to be 5 to 20wt%. According to a preparation method, low density polyethylene particles low in benzene series compound content and alkane compound content are taken as raw materials, and modified conductive polyaniline fiber capable of improving electrical conductivity and mechanical strength is added. The anti-static composite film prepared via the preparation method is capable of ensuring basic antistatic performance, and reducing adding amount of metal at the same time, and reducing the difficulty of environment pollution treatment and recycling, and is beneficial for environment protection. Adding of the modified conductive polyaniline fiber is capable of improving tear resistance of the anti-static composite film greatly, and increasing the mechanical strength of the anti-static composite film, and is beneficial for protection of electron components in packaging film from mechanical damage.

Description

technical field [0001] The invention relates to an antistatic composite film, in particular to an antistatic composite film suitable for wrapping electronic components. Background technique [0002] Static electricity is a common but complex physical phenomenon, it is invisible and ubiquitous. With the rapid development of science and technology, the improvement of high production efficiency and automation, and the widespread use of electronic equipment, the static and electromagnetic environment is getting worse and worse, which makes products sensitive to static electricity and electromagnetic radiation such as integrated circuits, electromagnetic Control systems, chemical agents, etc. pose a threat. Due to external electromagnetic radiation, failures and malfunctions of integrated circuits and electromagnetic control systems, and accidents of chemical product combustion and explosion occur from time to time. During the production, storage, transportation and use of chem...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L23/08C08L79/02C08L67/02C08L23/12C08L23/16B32B27/06B32B27/40B32B33/00B29C55/28B29C48/92D06M15/61D06M101/32D06M101/20
CPCB29C48/92B29C55/28B29C2948/92704B32B27/06B32B27/40B32B33/00B32B2307/21C08J5/18C08J2323/08C08J2479/02C08L23/0815C08L2201/04C08L2203/16C08L2203/20C08L2205/025C08L2205/03C08L2205/16C08L2207/066D06M15/61D06M2101/20D06M2101/32C08L79/02C08L67/02C08L23/12
Inventor 王震尹强
Owner SHANDONG ZHONGSU TAIFU TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products