Fluorinated plastic and preparation method thereof

A technology of fluorinated plastics and fluorinated graphene, which is applied in the field of plastic preparation and can solve problems such as poor barrier properties and poor bondability

Inactive Publication Date: 2018-09-28
长沙小新新能源科技有限公司
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This invention has good hydrophobicity, weather resistance and toughness, and high impact strength, but there are problems of poor barrier property and bondability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fluorinated plastic and preparation method thereof
  • Fluorinated plastic and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] The preparation method of the fluorinated plastic comprises the following steps:

[0030] S1: Take sodium alkylbenzene sulfonate, add deionized water 12-15 times its weight, stir evenly, raise the temperature to 56-58°C, stir for 3-6min, add calcium fluoride, stir to room temperature, and obtain fluorine chemical dispersion;

[0031]S2: Mix titanium tetrachloride, ammonium aluminum sulfate and potassium perfluorobutane sulfonate evenly to obtain mixed material A, add deionized water 40-50 times the weight of mixed material A, stir evenly, and the dropwise concentration is 5.4% - 5.6% ammonia solution, adjust the pH to 8-9, filter with suction, add the precipitate into deionized water 40-50 times its weight, sonicate for 6-10min, add antioxidant, stir for 10-20min, then add step S1 Stir the prepared fluorinated dispersion liquid and surfactant evenly, raise the temperature to 95-100°C, heat-preserve and stir for 2-3h, send it into an oven at 57-60°C, and dry it to obtai...

Embodiment 1

[0037] A fluorinated plastic, in parts by weight, comprising the following raw materials: 13 parts of phenolic resin, 8 parts of talcum powder, 6 parts of sodium alkylbenzenesulfonate, 3 parts of titanium tetrachloride, 12 parts of ferric chloride, methyl 11 parts of methyl acrylate, 2 parts of azobisisobutyronitrile, 9 parts of polyvinyl chloride, 0.2 parts of silane coupling agent, 6 parts of trimethylolpropane, 5 parts of ammonium aluminum sulfate, 1 part of potassium perfluorobutyl sulfonate 4 parts of calcium fluoride, 5 parts of nitrogen derivatives of perfluoropolyoxyalkylcarbonic acid, 3 parts of fluorinated graphene, 2 parts of acrylic resin, 1 part of antioxidant, and 0.8 parts of surfactant.

[0038] The antioxidant is 2,8-di-tert-butyl-4-methylphenol.

[0039] The surfactant is citrate.

[0040] The preparation method of the fluorinated plastic comprises the following steps:

[0041] S1: Take sodium alkylbenzene sulfonate, add deionized water 15 times its weight,...

Embodiment 2

[0048] A fluorinated plastic, in parts by weight, comprising the following raw materials: 15 parts of phenolic resin, 9 parts of talcum powder, 3 parts of sodium alkylbenzenesulfonate, 4 parts of titanium tetrachloride, 14 parts of ferric chloride, methyl 12 parts of methyl acrylate, 6 parts of azobisisobutyronitrile, 6 parts of polyvinyl chloride, 0.4 parts of silane coupling agent, 3 parts of trimethylolpropane, 2 parts of ammonium aluminum sulfate, 2 parts of potassium perfluorobutyl sulfonate 6 parts of calcium fluoride, 8 parts of nitrogen derivatives of perfluoropolyoxyalkylcarbonic acid, 5 parts of fluorinated graphene, 3 parts of acrylic resin, 1.5 parts of antioxidant, and 0.5 parts of surfactant.

[0049] The antioxidant is 2,6-di-tert-butylphenol.

[0050] The surfactant is ethylene bis stearamide.

[0051] The preparation method of the fluorinated plastic comprises the following steps:

[0052] S1: Take sodium alkylbenzene sulfonate, add 12 times its weight in de...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses fluorinated plastic and a preparation method thereof, belonging to the technical field of plastic preparation. The fluorinated plastic comprises the following raw materials: phenolic resin, talcum powder, sodium alkyl benzene sulfonate, titanium tetrachloride, iron chloride, methyl methacrylate, azobisisobutyronitrile, polyvinyl chloride, a silane coupling agent, trimethylolpropane, ammonium aluminum sulfate, potassium perfluorobutyl sulfonate, calcium fluoride, a nitrogen derivative of perfluoropolyoxyalkyl carbonate, fluorinated graphene, acrylic resin, an antioxidantand a surfactant. The fluorinated plastic is prepared through the steps of mixing, stirring, ultrasonic treatment, drying, injection molding, etc. According to the invention, by adoption of the nitrogen derivative of the perfluoropolyoxyalkyl carbonate, the fluorinated graphene and the acrylic resin as reinforcing systems, barrier properties and cohesiveness of the fluorinated plastic are improved.

Description

technical field [0001] The invention belongs to the technical field of plastic preparation, and in particular relates to a fluorinated plastic and a preparation method thereof. Background technique [0002] So far, polytetrafluoroethylene still ranks first among plastics with its excellent performance, but polytetrafluoroethylene is difficult to process and expensive, thus limiting its application range. In practical applications, it is often only required that the plastic surface layer has the properties of polytetrafluoroethylene. Therefore, if the surface layer of the molded polyethylene sheet, pipe and film can be fluorinated, their performance can be greatly improved, and the cost can be greatly reduced. Fluoropolymers have been widely used and developed in many fields due to their excellent properties such as high thermal stability and chemical stability. At present, the fluorinated polymer materials used are mainly prepared by the following methods: one is to prepar...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L61/06C08L33/04C08L51/10C08L101/06C08K13/02C08K3/04C08F292/00C08F220/14
CPCC08F292/00C08L61/06C08L2205/035C08F220/14C08L33/04C08L51/10C08L101/025C08K13/02C08K3/042
Inventor 不公告发明人
Owner 长沙小新新能源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap