Unbreakable PVC cable material

A technology of cable material and PVC resin, which is applied in the direction of circuits, electrical components, plastic/resin/wax insulators, etc., can solve the problems of poor thermal stability and easy breakage of PVC cable materials, and achieve low cost, not easy to break, and thermal stability good sex effect

Inactive Publication Date: 2018-11-06
ANHUI DUJIANG CABLE GROUP
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But at present, the thermal stability of PVC cable material is poor, and it is easy to break, which needs to be further improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A PVC cable material that is not easy to break, its raw materials include: SG3 type PVC resin 60kg, neoprene rubber 26kg, styrene-butadiene rubber 26kg, toughening agent 12kg, phytic acid compound 4kg, epoxy soybean oil 4kg, stearic acid 1kg , 16kg of fly ash, 14kg of hollow glass microspheres, 45kg of nano-montmorillonite, 2kg of diethoxydimethylsilane, 30kg of expanded perlite, 20kg of medical stone powder, 5kg of antioxidant, 2kg of tert-butyl peroxybenzoate .

[0015] The toughening agent is composed of rare earth calcium zinc composite stabilizer and chlorosulfonated polyethylene in a weight ratio of 2.6:4. The anti-aging agent is composed of anti-aging agent ODA and anti-aging agent DFC-34 in a weight ratio of 2.5:1.

[0016] The phytic acid complex is prepared by the following process: mix 8kg silk fibroin fiber, 1kg sodium alginate, 2kg aniline, and 80kg water, heat up to 95°C and stir for 30 minutes, add 16kg phytic acid and continue stirring for 30 minutes to...

Embodiment 2

[0018] A PVC cable material that is not easy to break, its raw materials include: SG3 type PVC resin 70kg, neoprene rubber 18kg, styrene-butadiene rubber 34kg, toughening agent 6kg, phytic acid compound 8kg, epoxy soybean oil 2kg, stearic acid 2kg , fly ash 8kg, hollow glass microspheres 20kg, nano-montmorillonite 35kg, diethoxydimethylsilane 3kg, expanded perlite 20kg, medical stone powder 30kg, anti-aging agent 2.5kg, tert-butyl peroxybenzoate 4kg.

[0019] The toughening agent is composed of rare earth calcium zinc composite stabilizer and chlorosulfonated polyethylene in a weight ratio of 2:8. The anti-aging agent is composed of anti-aging agent ODA and anti-aging agent DFC-34 in a weight ratio of 1.5:2.

[0020] The phytic acid complex is prepared by the following process: mix 4kg silk fibroin fiber, 3kg sodium alginate, 1kg aniline, and 120kg water, heat up to 85°C and stir for 50 minutes, add 10kg phytic acid and continue stirring for 50 minutes to obtain a premix; Mi...

Embodiment 3

[0022] A PVC cable material that is not easy to break, its raw materials include: SG3 type PVC resin 64kg, neoprene rubber 24kg, styrene-butadiene rubber 28kg, toughening agent 10kg, phytic acid compound 5kg, epoxy soybean oil 3.5kg, stearic acid 1.2kg, fly ash 14kg, hollow glass microspheres 16kg, nano-montmorillonite 42kg, diethoxydimethylsilane 2.2kg, expanded perlite 28kg, medical stone powder 22kg, anti-aging agent 4kg, tertiary benzoic acid peroxide Butyl ester 2.5kg.

[0023] The toughening agent is composed of rare earth calcium zinc composite stabilizer and chlorosulfonated polyethylene in a weight ratio of 2.4:5. The anti-aging agent is composed of anti-aging agent ODA and anti-aging agent DFC-34 in a weight ratio of 2.2:1.3.

[0024] The phytic acid compound is prepared by the following process: mix 7kg silk fibroin fiber, 1.5kg sodium alginate, 1.8kg aniline, and 90kg water, heat up to 92°C and stir for 35-45min, add 14kg phytic acid and continue stirring for 35mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an unbreakable PVC cable material. The PVC cable material comprises the following raw materials: 60-70 parts of SG3 PVC resin, 18-26 parts of neoprene, 26-34 parts of styrene-butadiene rubber, 6-12 parts of a flexibilizer, 4-8 parts of a phytic acid complex, 2-4 parts of epoxidized soybean oil, 1-2 parts of stearic acid, 8-16 parts of fly ash, 14-20 parts of hollow glass microspheres, 35-45 parts of nano-montmorillonite, 2-3 parts of diethoxydimethylsilane, 20-30 parts of expanded perlite, 20-30 parts of medical stone powder, 2.5-5 parts of antioxidant and 2-4 parts oftert-butyl peroxybenzoate, wherein the phytic acid complex is prepared with the following process: mixing silk fibroin fiber, sodium alginate, aniline and water, performing heating and stirring, adding phytic acid and continuously stirring the mixture to obtain a premixed solution; mixing ammonium persulfate and a hydrochloric acid solution uniformly, dropwise adding the mixed solution to the premixed solution for stirring, adding polyethylene glycol diglycidyl ether for stirring, leaving the mixture to stand for defoaming, adding a calcium chloride aqueous solution, and performing stirring uniformly and grinding to obtain the phytic acid complex.

Description

technical field [0001] The invention relates to the technical field of cable materials, in particular to an unbreakable PVC cable material. Background technique [0002] In the existing technology, PVC cable material is based on PVC resin, adding plasticizer (reducing the resin processing temperature, lowering the softening point of the product), lubricant (improving product processing performance, making the material easier to demould and flow), etc. Products that are mixed together after being extruded and plasticized by an appropriate ratio. But at present, the thermal stability of PVC cable material is poor, and it is easy to break, which needs to be further improved. Contents of the invention [0003] Based on the technical problems in the background technology, the present invention proposes a PVC cable material that is not easy to break, has good mechanical properties, is not easy to break, has excellent thermal stability and aging resistance, and is extremely low ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08L11/00C08L9/06C08L91/00C08L23/34C08L89/00C08L5/04C08K13/04C08K5/09C08K7/28C08K3/34C08K7/26C08K5/5419H01B3/44
CPCC08L27/06C08K2201/011C08L2201/08C08L2203/202C08L2205/035H01B3/443C08L11/00C08L9/06C08L91/00C08L23/34C08L89/00C08L5/04C08K13/04C08K5/09C08K7/28C08K3/346C08K7/26C08K5/5419
Inventor 巫春生张家文徐志敏
Owner ANHUI DUJIANG CABLE GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com