Upconversion transparent ceramic and application thereof in improvement of photoelectric conversion efficiency of crystalline silicon solar cells
A technology of photoelectric conversion efficiency and solar cells, applied in circuits, photovoltaic power generation, electrical components, etc., can solve problems such as no research reports, achieve good transparency, high conversion efficiency, and increase absorption and utilization
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
preparation example Construction
[0031]The up-conversion erbium ion-doped yttrium oxide-based transparent ceramics of the present invention can be prepared by a variety of ceramic preparation methods, such as coprecipitation, sol-gel method, combustion method, gel injection molding, tape casting, atmosphere sintering, thermal Pressing and sintering, etc., the present invention provides a specific process for the preparation of up-conversion erbium ion doped yttrium oxide-based transparent ceramics, but is not limited thereto.
[0032] The preparation method of the up-conversion erbium ion-doped yttrium oxide-based transparent ceramics provided by the present invention first adopts the solid-phase method to prepare the precursor powder, and then adopts the dry pressing method to prepare the biscuit, and then performs isostatic in a cold isostatic press. Press molding, then sinter ceramics by vacuum sintering, and finally anneal in air atmosphere to remove residual stress and color centers, and obtain up-convers...
Embodiment 1~11
[0043] The chemical formulas of the up-conversion erbium ion-doped yttrium oxide-based transparent ceramics in Examples 1-11 are shown in Table 1.
[0044] The preparation method of the up-conversion erbium ion-doped yttrium oxide-based transparent ceramics of Examples 1-11 is as follows, and the specific raw materials and process conditions used are as shown in Table 1:
[0045] Step 1, according to the chemical formula (Y 1-x-y Er x m y ) 2 o 3 , Weigh the solid compound of Y element, Er element and M element according to the molar ratio, put it into a ball mill jar, and grind it mechanically for 24-60 hours to obtain the precursor powder;
[0046] Among them, the solid compound is preferably an oxide, a fluoride, a chloride or a salt containing corresponding elements;
[0047] Step 2, putting the precursor powder obtained in step 1 into a mold for dry pressing and molding, and putting the obtained green body into a cold isostatic pressing machine for isostatic pressing...
PUM
Property | Measurement | Unit |
---|---|---|
band gap | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com