A technology of microcrystalline cellulose and crop straw, applied in the field of resources and environment, can solve the problems of unfavorable large-scale deep processing and transformation and utilization, corrosiveness and large amount of waste liquid, and high post-treatment cost, so as to reduce environmental pollution and equipment. Corrosion, easy recovery, and small damage to solid acid

Active Publication Date: 2021-01-19
WUHAN POLYTECHNIC UNIVERSITY
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the most widely used organic solvent is ethanol. Since ethanol and water form an azeotrope, it takes a lot of energy to recover ethanol; and ethanol has a lower boiling point and is more volatile during the process.
In addition, α-cellulose is usually partially hydrolyzed under the homogeneous catalysis of strong inorganic acids such as hydrochloric acid and sulfuric acid. The corrosiveness and waste liquid volume are relatively large and the pollution is serious. The above factors will lead to high post-treatment costs and are not conducive to further processing. It is necessary to find a method for cleanly utilizing crop straw cellulose to prepare microcrystalline cellulose

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] Add the mixed solvent of wheat straw powder, N-methylpyrrolidone and water (the volume ratio of N-methylpyrrolidone and water is 1:2), sulfuric acid (so that the concentration in the solution is 0.05M) into the autoclave , wherein the weight ratio of wheat straw powder and mixed solvent is 1:6, heated to 180°C, stirred for 4h, cooled to room temperature, centrifuged and suction filtered to obtain filtrate and solid product. The solid product was washed with the same above-mentioned mixed solvent, the washing liquid and the filtrate were combined, the filtrate was extracted with chloroform, and the organic solvent was recovered. The solid product is wheat straw crude cellulose with a purity of 75.3%. Put the wheat straw crude cellulose into the round bottom flask, and then add the prepared mixed solution containing 4wt% sodium carbonate and 2wt% hydrogen peroxide. The weight ratio of the wheat straw crude cellulose to the mixed solution is 1:7.5.70 Heat and stir at ℃ fo...

Embodiment 2

[0038]Add the mixed solvent of wheat straw powder, N-methylpyrrolidone and water (the volume ratio of N-methylpyrrolidone and water is 1:1), sulfuric acid (so that the concentration in the solution is 0.03M) into the autoclave , wherein the weight ratio of wheat straw powder and mixed solvent is 1:8, heated to 190°C, stirred for 6h, cooled to room temperature, centrifuged, and suction filtered to obtain filtrate and solid product. The solid product was washed with the same above-mentioned mixed solvent, the washing liquid and the filtrate were combined, the filtrate was extracted with chloroform, and the organic solvent was recovered. The solid product is wheat straw crude cellulose with a purity of 79.7%. Put the wheat straw crude cellulose into the round bottom flask, and then add the prepared mixed solution containing 4wt% sodium carbonate and 2wt% hydrogen peroxide. The weight ratio of the wheat straw crude cellulose to the mixed solution is 1:7.5.70 Heat and stir at ℃ fo...

Embodiment 3

[0040] Add the mixed solvent of wheat straw powder, N-methylpyrrolidone and water (the volume ratio of N-methylpyrrolidone and water is 1:1), sulfuric acid (so that the concentration in the solution is 0.03M) into the autoclave , wherein the weight ratio of wheat straw powder and mixed solvent is 1:8, heated to 190°C, stirred for 6h, cooled to room temperature, centrifuged, and suction filtered to obtain filtrate and solid product. The solid product was washed with the same above-mentioned mixed solvent, the washing liquid and the filtrate were combined, the filtrate was extracted with chloroform, and the organic solvent was recovered. The solid product is wheat straw crude cellulose with a purity of 79.7%. Put the wheat straw crude cellulose into the round bottom flask, and then add the prepared mixed solution containing 6wt% sodium carbonate and 1wt% hydrogen peroxide. The weight ratio of the wheat straw crude cellulose to the mixed solution is 1:7.5.60 Heat and stir at ℃ f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle diameteraaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to view more

Abstract

The invention discloses a microcrystalline cellulose and a method for preparing the microcrystalline cellulose by using crop straws. Separation and extraction of straw crude cellulose with a high boiling point organic solvent, the obtained crude cellulose is partially hydrolyzed under the action of a spherical solid acid catalyst, and the resulting hydrolyzed mixture is left to stand, filtered, solid is collected, and dried to obtain a spherical solid acid catalyst and micro The solid mixture of crystalline cellulose is further sieved to recover the solid catalyst and obtain microcrystalline cellulose with a degree of polymerization ranging from 156 to 402. The microcrystalline cellulose prepared by the present invention has high purity and moderate degree of polymerization, and can be used as a fine chemical raw material. The high boiling point solvent used has low volatility and good thermal stability and can be recovered through simple extraction operations. The solid acid catalyst has high catalytic activity and is easy to separate and recover, which overcomes the problems of pollution and corrosion caused by the low boiling point solvent volatilization and the use of strong inorganic acid in traditional methods.

Description

technical field [0001] The invention belongs to the field of resources and environment, and specifically relates to the high-value utilization of agricultural waste resources, and more specifically, to a microcrystalline cellulose and a method for preparing microcrystalline cellulose by using crop straws. Background technique [0002] Crop straw is a valuable renewable biomass resource. According to the report of the United Nations Environment Programme, the crops planted in the world can provide about 2 billion tons of various straws every year. China's straw output ranks first in the world, with an annual production of about 700 million tons of straw, and my country's straw output alone can be converted into 353 million tons of standard coal. With the continuous deterioration of the environment and the increasing scarcity of fossil resources and wood resources, the development of comprehensive utilization of renewable resources has become one of the effective ways to deal ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D21C5/00
CPCD21C5/00
Inventor 范国枝王悦昕胡宗潇宋光森李建芬闫俊涛
Owner WUHAN POLYTECHNIC UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap