Environment-friendly polycarbonate/polyester composite material and preparation method and application thereof

A technology of polyester composite material and polycarbonate, which is applied in the field of intelligent irrigation control well room, which can solve the problem of unsatisfactory mechanical strength, chemical corrosion resistance and aging resistance, low safety of intelligent irrigation control well room, glass fiber reinforced plastic and cast iron The materials are not environmentally friendly and the environment can avoid anti-aging and flame-retardant properties, improve interfacial compatibility, and improve comprehensive mechanical properties.

Active Publication Date: 2019-05-21
定州旭邦新材料科技有限公司
View PDF14 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the deficiency of prior art, provide a kind of polycarbonate / polyester composite material and preparation method thereof, to solve existing polycarbonate / polyester composite material existing mechanical strength, chemical corrosion resistance, aging resistance Technical problems such as unsatisfactory performance
[0006] In addition, the purpose of the present invention is to provide an intelligent irrigation control machine well house to solve the problems caused by the unsatisfactory performance of existing fiberglass and cast iron materials, such as environmental pollution, non-recyclable, non-corrosion resistance, and relatively bulky. Technical problems with low housing security

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly polycarbonate/polyester composite material and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] Prescription: 30 parts by weight of polycarbonate (PC), 30 parts by weight of polybutylene terephthalate (PBT) as polyester, 20 parts by weight of glass fiber, 2 parts by weight of triethyl phosphate as transesterification inhibitor Parts, 5 parts by weight of polyethylene grafted maleic anhydride (Shanghai Rizhisheng Company) as a compatibilizer, ethylene-methyl acrylate-glycidyl methacrylate copolymer (available from France Ake Ma company) 2 parts by weight, 15 parts by weight of melamine aluminum polyphosphate (purchasing Clariant company) as flame retardant, 0.3 parts by weight of anti-UV agent (UV360), 0.15 parts by weight of antioxidant (1098), coupling agent ( KH570) 0.15 parts by weight, silicone powder 0.2 parts by weight as a lubricant.

[0046] Preparation:

[0047] 1) Put the formulated amount of PC, polyester and toughener into a high-speed mixer for pre-mixing for 1-3 minutes, then add the formulated amount of coupling agent and mix for 2-4 minutes to ful...

Embodiment 2

[0054] Prescription: 30 parts by weight of polycarbonate (PC), 30 parts by weight of polyethylene terephthalate (PET) as polyester, 20 parts by weight of glass fiber, 2 parts by weight of triethyl phosphate as transesterification inhibitor Parts, 5 parts by weight of polyethylene grafted maleic anhydride (Shanghai Rizhisheng Company) as compatibilizer, 2 parts by weight of n-butyl acrylate-glycidyl ester copolymer (Akema Company of France) as toughening agent , 15 parts by weight of aluminum hypophosphite (purchase Clariant company) as flame retardant, 0.3 parts by weight of anti-UV agent (UV360), 0.15 parts by weight of antioxidant (1098), 0.15 parts by weight of coupling agent (KH570), lubricated agent (silicone powder) 0.2 parts by weight.

[0055] The preparation method is the same as in Example 1.

Embodiment 3

[0057] Prescription: 30 parts by weight of polycarbonate (PC), 30 parts by weight of poly(butylene terephthalate-co-butylene adipate) (PBAT) as polyester, 20 parts by weight of glass fiber, as 2 parts by weight of triethyl phosphate of transesterification inhibitor, 5 parts by weight of polyethylene graft maleic anhydride (Shanghai Rizhisheng Company) as compatibilizer, n-butyl acrylate-glycidyl ester as toughening agent 2 parts by weight of copolymer (DuPont), 15 parts by weight of aluminum hypophosphite (purchasing Clariant Company) as flame retardant, 0.3 parts by weight of anti-UV agent (UV360), 0.15 parts by weight of antioxidant (1098), coupling Agent (KH570) 0.15 parts by weight, lubricant (silicone powder) 0.2 parts by weight.

[0058] The preparation method is the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides an environment-friendly polycarbonate / polyester composite material and a preparation method and application thereof. The environment-friendly polycarbonate / polyester composite material is prepared from the following components in parts by weight: 30-80 parts of polyester, 20-60 parts of polycarbonate, 5-30 parts of glass fibers, 1-5 parts of an ester exchange inhibitor, 1-5parts of a flexibilizer, 0.5-10 parts of a compatilizer, 1-20 parts of a flame retardant, 0.1-1 part of an antioxidant, 0.1-1 part of an anti-UL agent, 0.1-1 part of a lubricating agent and 0.1-0.5 part of a coupling agent. The environment-friendly polycarbonate / polyester composite material provided by the invention has excellent mechanical properties, flame retardance and ageing resistance, the preparation method of the environment-friendly polycarbonate / polyester composite material is simple in process, and the production cost of the environment-friendly polycarbonate / polyester composite material is lowered.

Description

technical field [0001] The invention relates to an environment-friendly polycarbonate (PC) / polyester composite material, its preparation method and application, and an intelligent irrigation control well house prepared by the composite material. Background technique [0002] Polycarbonate is a non-crystalline polymer material with excellent impact resistance, dimensional stability, thermal stability, high gloss and excellent mechanical properties, electrical insulation and flame retardancy. However, its molecular rigidity and steric hindrance are large, its melting temperature is high, and molding processing is difficult. More importantly, its products have large residual stress, are prone to stress cracking, and have poor solvent resistance. In addition, the disadvantages of high cost limit the use of polycarbonate. practical application. [0003] Polyester materials such as polybutylene terephthalate (PBT), polyethylene terephthalate (PET), and poly(butylene terephthalate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L69/00C08L67/02C08L51/06C08L23/08C08L33/08C08K13/04C08K7/14C08K5/521C08K5/3492C08K3/32
Inventor 王国利陈亚宁曲振党伟荣潘小君
Owner 定州旭邦新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com