Colored antiskid paving material as well as preparation method and application thereof

A paving material and anti-skid technology, applied in the direction of polyurea/polyurethane coatings, coatings, etc., can solve the problems of inability to achieve rapid pavement of colored anti-skid thin layers on the road, delamination and peeling, insufficient adhesion, etc. Practical value, excellent anti-skid performance, simple construction effect

Active Publication Date: 2020-04-17
CHONGQING POFUN TRAFFIC TECH
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although small molecular monomers can participate in the polymerization reaction, during the polymerization process, small molecular monomers can also be absorbed by the capillary pores of asphalt or cement concrete, resulting in insufficient adhesion between the material and the base surface after curing. Delamination and peeling after time
In the actual application process, in order to solve the above shortcomings, it is usually necessary to coat the base surface with epoxy primer. The advantages of rapid polymerization and curing at room temperature or low temperature, so that it is impossible to realize the rapid paving of colored anti-skid thin layers on the road surface

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Colored antiskid paving material as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] The preparation method of the colored non-slip paving material of the present embodiment may further comprise the steps:

[0040] 1) Add N,N-dimethylaniline to hydroxyethyl acrylate for dissolution;

[0041] 2) Mix liquid paraffin and 56# solid paraffin, heat and stir at 60°C until completely melted, then add the mixture prepared in step 1), stir well, and cool to room temperature;

[0042] 3) Mix and stir the 2-functionality urethane acrylate and 1,10-decanediol diacrylate evenly, then add the mixture prepared in step 2), and stir evenly;

[0043] 4) Add 600-mesh calcium carbonate and iron oxide red to the mixture prepared in step 3), stir well until the dispersion is uniform, and then grind with a sand mill to obtain a homogeneous and delicate glue;

[0044] 5) While stirring, add a mixture of 140-200 mesh silica and 1-2 mm red calcined ceramic aggregate into the glue, stir well, add tert-butyl peroxypivalate, and continue stirring for 1-2 mm. 2min, that is;

[004...

Embodiment 2

[0048] The preparation method of the colored non-slip paving material of the present embodiment may further comprise the steps:

[0049] 1) Add N,N-dimethyl-p-toluidine to hydroxypropyl acrylate for dissolution;

[0050] 2) Mix liquid paraffin and 54# solid paraffin, heat and stir at 60°C until completely melted, then add the mixture prepared in step 1), stir evenly, and cool to room temperature;

[0051]3) Mix and stir the 2-functionality urethane acrylate and 1,9-nonanediol diacrylate evenly, then add the mixture prepared in step 2), and stir evenly;

[0052] 4) Add 800-mesh calcium carbonate and chrome green to the mixture prepared in step 3), fully stir until the dispersion is uniform, and then grind with a sand mill to obtain a homogeneous and delicate glue;

[0053] 5) While stirring, add the mixture of 40-80 mesh silica and 1-3mm green calcined ceramic aggregate into the glue, stir well, add tert-butyl peroxyneodecanoate, and continue stirring for 1-3mm 2min, that is;...

Embodiment 3

[0057] The preparation method of the colored non-slip paving material of the present embodiment may further comprise the steps:

[0058] 1) adding N-methyl-N-hydroxyethyl p-toluidine to hydroxybutyl acrylate for dissolution;

[0059] 2) Mix liquid paraffin and 58# solid paraffin, heat and stir at 60°C until completely melted, then add the mixture prepared in step 1), stir evenly, and cool to room temperature;

[0060] 3) Mix and stir 3-functional polyurethane acrylate and 1,6-hexanediol diacrylate evenly, then add the mixture prepared in step 2), and stir evenly;

[0061] 4) Add 1000 meshes of calcium carbonate, iron oxide yellow, and iron oxide green to the mixture prepared in step 3), stir well until the mixture is evenly dispersed, and then grind with a sand mill to obtain a homogeneous and delicate glue;

[0062] 5) While stirring, add a mixture of 80-140 mesh silica and 1-2mm green calcined ceramic aggregate into the glue, stir well, add tert-butyl peroxy octanoate, and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
freezing pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a colored antiskid paving material as well as a preparation method and application thereof, and belongs to the technical field of road paving materials. The colored antiskid paving material is prepared from the components: polyurethane acrylate, dihydric alcohol diacrylate, aromatic tertiary amine, hydroxyl acrylate, liquid paraffin, solid paraffin, an inorganic calcium filler, an inorganic pigment, an inorganic siliceous filler, a calcined ceramic aggregate and a liquid peroxide initiator. The prepared colored anti-skid paving material does not contain soluble asphaltor micromolecular solvent type monomers permeating into a cement concrete pavement; the anti-skid material has the advantages of high bonding strength with the pavement, favorable high-temperature stability, favorable low-temperature crack resistance, high anti-skid coefficient, long service life, simple preparation technique, mild conditions, safety, environment friendliness, simple and quick construction and wide popularization and application value in road pavement.

Description

technical field [0001] The invention belongs to the technical field of road pavement materials, and in particular relates to a colored non-slip pavement material and its preparation method and application. Background technique [0002] On roads with steep slopes, roads around schools, urban non-motor vehicle lanes, tunnel entrances, park landscape roads and other roads, in order to prevent vehicle skidding due to high humidity or icing, the road surface is coated with various anti-skid pavement materials, Ensure the safety of vehicles and people driving or walking on these roads. [0003] In recent years, due to the rapid polymerization of methacrylate or acrylate at room temperature or low temperature through a redox initiation system, pavement colored anti-skid materials based on methacrylate or acrylate binders have been widely used. Patent CN201610863872 proposes a colored non-slip thin-layer paving material based on methacrylic resin MMA and its preparation process. H...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/14C09D7/61
CPCC08K2003/2272C08K2003/265C08L2201/02C08L2205/025C08L2205/03C09D175/14C09D7/61C08L91/06C08K3/26C08K3/22C08K3/36C08K3/00
Inventor 马志君
Owner CHONGQING POFUN TRAFFIC TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com