High-temperature-resistant antibacterial tipping paper gloss oil and preparation method thereof

A high-temperature resistant cigarette tipping paper technology, which is applied in paper, papermaking, paper coatings, etc., can solve the problems of affecting the content of antibacterial agents, the inability to guarantee the effective proportion of ink, and the inability to guarantee the antibacterial effect of tipping paper products, etc., to achieve stable effect

Pending Publication Date: 2020-08-07
QUJING KIRIN FUPAI PRINTING
View PDF11 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the disadvantage is that titanium dioxide and benzidine yellow are commonly used pigments and fillers in inks. Although nano-silica has certain bactericidal properties, due to the variability of the color of the tipping paper, the effectiveness of the ink in the color matching process cannot be guaranteed. ratio, so the final antibacterial effect of the finished tipping paper cannot be guaranteed
The disadvantage is that there are many components in the ink system, and the antibacterial agent is wrapped by other components in the ink, which affects the content of the antibacterial agent on the surface of the tipping paper, thus affecting the antibacterial effect of the tipping paper

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature-resistant antibacterial tipping paper gloss oil and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0050] According to yet another aspect of the present invention, the present invention also relates to the method for preparing the tipping paper for cigarettes as described above, comprising: coating the varnish layer on the surface layer of the tipping paper for cigarettes by printing, The pressure of the press roller during the printing process is 0.3MPa~0.5MPa, the drying temperature is 90℃~120℃, and the dry weight of ink is 0.5g / m 2 ~1.0g / m 2 .

[0051] The present invention also relates to a filter element, comprising a filter rod and a tipping paper for packaging the filter rod, and the tipping paper for cigarettes is the tipping paper for cigarettes as described above.

[0052] Primary functions of filter elements may include direct interception, inertial compaction, and diffusional settling.

[0053] The filter element may comprise a filter rod, the main component of which may be sponge.

[0054] The filter element optionally includes a filter rod of homogeneous filt...

Embodiment 1

[0060] The formula (parts by weight) of high temperature resistant antibacterial varnish is as follows in the present embodiment: 25 parts of polycarbonate resins, 4.5 parts of hydroxyethyl cellulose, 2.2 parts of ε-polylysine, 38 parts of ethanol, 30 parts of water, 0.2 parts of high-density polyethylene wax (average particle size of 8.5 μm), 0.1 parts of BYK-024.

[0061] The preparation method of described high temperature resistant antibacterial varnish is as follows:

[0062] (1) Mix ethanol and water and stir evenly to obtain a solution;

[0063] (2) Add polycarbonate resin and hydroxyethyl cellulose to the above solution, stir evenly to obtain an emulsion;

[0064] (3) Add ε-polylysine, high-density polyethylene wax, and BYK-024 to the above emulsion in sequence, and stir evenly to obtain a suspension;

[0065] (4) Obtain a high temperature resistant antibacterial varnish with a viscosity of 20s (25°C, British 2# Charn cup).

[0066] The preparation method of the tip...

Embodiment 2

[0069] In the present embodiment, the formula (parts by weight) of high temperature resistant antibacterial varnish is as follows: 10 parts of polyvinyl alcohol resin, 20 parts of hydroxypropyl methylcellulose, 8 parts of ε-polylysine, 38 parts of ethanol, 30 parts Water, 0.2 parts of high-density polyethylene wax (average particle size of 7.5 μm), 0.1 parts of BYK-024.

[0070] The preparation method of described high temperature resistant antibacterial varnish is as follows:

[0071] (1) Mix ethanol and water and stir evenly to obtain a solution;

[0072] (2) Add polyvinyl alcohol resin and hydroxypropyl methylcellulose to the above solution, stir evenly, and obtain an emulsion;

[0073] (3) Add ε-polylysine, high-density polyethylene wax, and BYK-024 to the above emulsion in sequence, and stir evenly to obtain a suspension;

[0074] (4) Obtain a high temperature resistant antibacterial varnish with a viscosity of 22s (25°C, British 2# Charn cup).

[0075] The preparation...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
The average particle sizeaaaaaaaaaa
The average particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of tipping paper, and especially relates to high-temperature-resistant antibacterial tipping paper gloss oil and a preparation method thereof. The tippingpaper gloss oil comprises main functional components, an assistant and a solvent; the main functional components comprise, by weight, 5 to 30 parts of first water-based resin, 1 to 25 parts of secondwater-based resin, 0.5 to 15 parts of epsilon-polylysine and 0.1 to 0.5 part of wax powder; the first water-based resin is selected from at least one of polycarbonate resin, polyurethane resin and polyvinyl alcohol resin; and the second water-based resin is cellulose resin. The high-temperature-resistant antibacterial tipping paper has high temperature resistance and an antibacterial effect, is stable in property in subsequent processing and production processes, and does not influence the quality of the tipping paper.

Description

technical field [0001] The invention relates to the technical field of tipping paper, in particular to a high-temperature resistant and antibacterial tipping paper varnish and a preparation method thereof. Background technique [0002] Cigarette tipping paper is an important tobacco auxiliary material in the cigarette manufacturing process. With the rapid development of cigarette products, cigarette tipping paper is not only used to connect cigarette filters and cigarette sticks. [0003] Cigarettes are easily infected with various bacteria during storage, transmission, and smoking, so these bacteria enter the human body from the oral cavity and respiratory tract, easily causing various diseases. Therefore, it is of great significance to prevent bacteria such as digestive tract infectious bacteria and respiratory tract infectious bacteria from spreading through cigarettes to carry out antibacterial treatment for cigarette tipping paper to make it have antibacterial propertie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D21H19/24D21H19/34D21H19/30D21H19/22D21H19/14D21H21/36D21H21/14A24D1/02
CPCD21H19/24D21H19/34D21H19/30D21H19/22D21H19/14D21H21/36D21H21/14A24D1/022
Inventor 徐善水赵荣艳杨二果曹萼郭曙光杨江涛王安余学良周琼英卫燕骆学松
Owner QUJING KIRIN FUPAI PRINTING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com