A resource recovery and red mud technology, applied in the direction of improving process efficiency, can solve problems such as low solubility, risk of dam collapse, release of alkaline substances to pollute the environment, and complexity
Pending Publication Date: 2020-12-01
何耀
View PDF2 Cites 6 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
Silicon-containing minerals are dissolved by dilute acid to form silicic acid. Due to the low solubility of silicic acid in water, it mainly exists in the pulp in the state of sol, and is easy to condense into silica gel, which makes it difficult to filter the leachate and separate and recover valuable metals. ; When the calcium in red mud reacts with sulfuric acid, the amount of calcium sulfate dihydrate slag produced is 4.3 times that of the calcium content in red mud. Due to the excessive amount of slag, it will have a serious adverse effect on the recovery of valuable metals
In order to overcome the above problems, the recycling process of red mud resources developed
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment
[0023] Such as figure 1 As shown, a method for efficient resource utilization of red mud of the present invention comprises the following steps:
[0024] 1. Dilute the concentrated hydrochloric acid to 1.5mol / L with lotion 1, and the initial liquid-solid ratio (ml / g) is 6. After reacting for 15 minutes, add red mud while adding concentrated hydrochloric acid until the total liquid-solid ratio is 4.5. The reaction temperature is 20-60° C., the reaction time is 1.0 h, and the final pH value of the solution is 1.0.
[0025] 2. The acidic pulp obtained in the first step above is separated by a thickener, and the upper overflow is used as a composite water purifier product, and the solid water purifier product is obtained after drying. Perform countercurrent washing with a five-stage thickener to obtain sedimentation 2 and washing solution 1 enriched in iron, titanium, scandium and vanadium.
[0026] 3. Sedimentary slag 2 uses a pulsating high-gradient magnetic separator to selec...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses an efficient resource utilization method of red mud. The red mud is leached out with diluted hydrochloric acid; the obtained ore pulp is separated with a thickener (or an ore washing tank); overflow (containing suspended solids, namely activated soil) at the upper part is used as a composite water purifying agent product; settling slag at the lower part is subjected to multi-stage thickener (or the ore washing tank) countercurrent washing with the diluted hydrochloric acid having a pH value of 0.5-1; washing liquid is used for diluting concentrated hydrochloric acid andthen used as leaching initial acid; iron ore concentrate products and titanium-rich slag are produced through magnetic separation of the settling slag of the last stage; the titanium-rich slag is circularly leached through sulfuric acid; titanium-rich liquid and sulfuric acid leaching slag are obtained; titanium, scandium and vanadium are recycled from the titanium-rich liquid; residual liquid isused for producing polymeric ferric sulfate aluminum products; and the sulfuric acid leaching slag serves as zirconium, tantalum and niobium extraction raw materials or building material raw materials. The method is simple in production process, low in energy consumption and good in production environment, no waste water or waste residues are discharged in the production process, red mud resources are completely consumed, and remarkable economic benefits can be obtained.
Description
technical field [0001] The invention belongs to the fields of hydrometallurgy and solid waste resource utilization, and in particular relates to a method for efficient resource utilization of red mud. Background technique [0002] Red mud is the solid waste residue produced when bauxite is eluted with high temperature, high pressure and strong alkali, and the solid and liquid are separated. The main components are iron, aluminum, silicon, calcium, sodium, titanium, oxygen and a small amount of scandium, zirconium, vanadium, tantalum , niobium and other rare metals. The mineral components contained in red mud are complex, among which: hematite (α-Fe 2 o 3 ), hydrated garnet [Ca 3 AlFe(SiO 4 )(OH) 8 ], sodium silicate (Na 2 O·Al 2 o 3 1.68SiO2 2 1.73H 2 O), calcium aluminate (Ca(AlO 2 ) 2 ), perovskite (CaTiO 3 ) and other new minerals, as well as goethite (α-FeOOH), diaspore (Al 2 o 3 ·H 2 O), gibbsite (Al 2 o 3 ·3H 2 O), Hydroxysite (Ca(OH) 2 ), calcium c...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.