Multi-color epoxy resin pure polyester molding powder

A technology of epoxy resin and polyester, applied in the field of pure polyester plastic powder, can solve the problems of cavity paint surface corrosion, increase repair cost, affect aesthetics, etc., achieve the effect of killing mold, increasing antibacterial effect, The effect of protecting the wall

Inactive Publication Date: 2020-12-18
四川省民和鑫新材料科技有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the prior art, during the long-term rainy season in the south, due to the high humidity and moderate temperature, it is suitable for the reproduction of fungi and other molds, so there will be spotted mold colonies on the wall, which not only affects the aesthetics, but also in the long-term process. It will cause the corrosion of the paint surface of the cavity, cause the wall to fall off, and increase the cost of repair

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Embodiment 1: The components of the powder coating and the parts by weight of each component are 100 parts of epoxy resin, 50 parts of polyester resin, 18 parts of curing agent, 8 parts of pigment, 8 parts of filler, 4 parts of barium sulfate, antibacterial 6 parts of agent and 6 parts of antifungal agent.

[0016] Among them, the antifungal agent is composed of quaternary ammonium salt derivatives, Cathone, surfactants and synergists, and acts on the cell wall and cell membrane system as well as on biochemical reaction enzymes or other active substances.

[0017] Preferably, the particle size of the barium sulfate powder is 0.03mm-0.08mm, and secondary drying is required when preparing the barium sulfate powder particles to avoid damage to the activity of other additives by the undried powder.

[0018] Further, the curing agent is composed of cement, slag, maleic acid, humacic acid, sodium carbonate, sodium fluoride, sodium hydroxide, potassium aluminum sulfate and tri...

Embodiment 2

[0022] Embodiment two: the components of the powder coating and the parts by weight of each component are 130 parts of epoxy resin, 80 parts of polyester resin, 16 parts of curing agent, 6 parts of pigment, 6 parts of filler, 3 parts of barium sulfate, antibacterial 5 parts of agent and 5 parts of antifungal agent.

[0023] Among them, the antifungal agent is composed of quaternary ammonium salt derivatives, Cathone, surfactants and synergists, and acts on the cell wall and cell membrane system as well as on biochemical reaction enzymes or other active substances.

[0024] Preferably, the particle size of the barium sulfate powder is 0.03mm-0.08mm, and secondary drying is required when preparing the barium sulfate powder particles to avoid damage to the activity of other additives by the undried powder.

[0025] Further, the curing agent is composed of cement, slag, maleic acid, humacic acid, sodium carbonate, sodium fluoride, sodium hydroxide, potassium aluminum sulfate and t...

Embodiment 3

[0029] Embodiment three: the components of the powder coating and the parts by weight of each component are 150 parts of epoxy resin, 100 parts of polyester resin, 18 parts of curing agent, 8 parts of pigment, 8 parts of filler, 4 parts of barium sulfate, 6 parts 6 parts and 6 parts of antifungal agent.

[0030] Among them, the antifungal agent is composed of quaternary ammonium salt derivatives, Cathone, surfactants and synergists, and acts on the cell wall and cell membrane system as well as on biochemical reaction enzymes or other active substances.

[0031] Preferably, the particle size of the barium sulfate powder is 0.03mm-0.08mm, and secondary drying is required when preparing the barium sulfate powder particles to avoid damage to the activity of other additives by the undried powder.

[0032] Further, the curing agent is composed of cement, slag, maleic acid, humacic acid, sodium carbonate, sodium fluoride, sodium hydroxide, potassium aluminum sulfate and triethanolami...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses multi-color epoxy resin pure polyester molding powder, which comprises the following components in parts by weight: 100-150 parts of epoxy resin, 50-100 parts of polyester resin, 15-18 parts of a curing agent, 4-8 parts of a pigment, 5-8 parts of a filler, 2-4 parts of barium sulfate, 3-6 parts of an antibacterial agent and 3-6 parts of a mildew preventive. The antibacterial agent and the mildew preventive are added into the components of the multi-color epoxy resin pure polyester molding powder, so that the antibacterial effect of the multi-color epoxy resin pure polyester molding powder can be improved, a wall body is prevented from generating much mildew in a long-term plum rain season, and the antibacterial agent and the mildew preventive can destroy the cell tissues of the generated mildew, mildew is effectively killed, the wall body is protected, and paint repair cost is reduced.

Description

technical field [0001] The invention relates to pure polyester plastic powder, in particular to multicolor epoxy resin pure polyester plastic powder, and belongs to the technical field of pure polyester plastic powder. Background technique [0002] Epoxy resin pure polyester plastic powder is commonly used as a raw material for coatings in the industry. Multi-color epoxy resin pure polyester plastic powder can be used as a home decoration coating, which can increase the plasticity of home decoration and has excellent wear resistance and protection properties. , with strong adhesion, good anti-rust and chemical resistance, comprehensive protection performance, high hardness, and can be dried at low temperature. [0003] In the prior art, during the long-term rainy season in the south, due to the high humidity and moderate temperature, it is suitable for the reproduction of fungi and other molds, so there will be spotted mold colonies on the wall, which not only affects the ae...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D167/00C09D7/61C09D5/03C09D5/14C09D5/29
CPCC08K2003/2241C08K2003/2296C08K2003/3045C09D5/033C09D5/035C09D5/14C09D5/29C09D163/00C08L67/00C08K13/04C08K7/12C08K3/30C08K5/46C08K5/0041C08K3/22C08K3/24C08K13/02C08K3/34
Inventor 王鑫
Owner 四川省民和鑫新材料科技有限公司