Preparation method of co1-xs-mos2-nitrogen-doped carbon her/oer bifunctional catalyst

A bifunctional catalyst, nitrogen-doped carbon technology, applied in physical/chemical process catalysts, chemical instruments and methods, chemical/physical processes, etc., can solve the problem of underreporting

Active Publication Date: 2022-03-08
CHINA THREE GORGES UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the hexagonal Co 1-x S is rarely reported

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of co1-xs-mos2-nitrogen-doped carbon her/oer bifunctional catalyst
  • Preparation method of co1-xs-mos2-nitrogen-doped carbon her/oer bifunctional catalyst
  • Preparation method of co1-xs-mos2-nitrogen-doped carbon her/oer bifunctional catalyst

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] CoCl 2 ·6H 2 O and urea were dissolved in 40 mL of deionized water at room temperature, in which CoCl 2 The concentration of urea is 0.15M, and the mass fraction of urea is 6.25wt.%. Take the hydrophilic carbon paper and immerse it in the solution, and then keep it at 90°C for 2 hours. After cooling to room temperature, take out the carbon paper and rinse it with deionized water three times. , dry for later use. Then pre-oxidize in the air at 400°C for 0.5h, and then sinter at 600°C in S atmosphere for 2h to obtain Co 9 S 8 array of nanorods. Dissolve 0.492g of molybdenum chloride and 100mg of bipyridine in 2.85ml of N,N dimethylformamide and 0.15ml of Tx-100 solution, stir and dissolve to obtain a 600mM molybdenum chloride nitrogen carbon solution. The above grown Co 9 S 8 The carbon paper of the nanorod array was soaked in the molybdenum chloride nitrogen carbon solution at room temperature for 1 min, and then dried on a hot stage at 80°C for 10 min to obtain C...

Embodiment 2

[0048] The preparation steps are the same as in Example 1, only the quality of molybdenum chloride is 0.164g, and the molybdenum chloride nitrogen carbon solution of 300mM is obtained, and Co 1-x S-MoS 2 - Nitrogen doped carbon (NC) in situ electrodes.

[0049] figure 2 Electrode prepared for Example 2 (a) HER linear voltammetry (LSV) diagram and (b) OER LSV diagram. It can be seen from figure (a) that when the current density of the electrode is 10mA / cm 2 , the overpotential required for HER reaction to produce hydrogen in alkaline aqueous solution is only 80mV; when the current density is 100mA / cm 2 When the corresponding overpotential is only 143mV; when the current density is 400mA / cm 2 , the corresponding overpotential is only 248mV. This reflects the excellent catalytic hydrogen evolution performance of the material. It can be seen from the figure (b) that when the current density of the electrode is 10mA / cm 2 , the overpotential corresponding to OER reaction oxyge...

Embodiment 3

[0051] The preparation steps are the same as in Example 1, only the quality of molybdenum chloride is 0.328g, and the molybdenum chloride nitrogen carbon solution of 400mM is obtained, and Co 1-x S-MoS 2 - Nitrogen doped carbon (NC) in situ electrodes.

[0052] image 3 Electrodes prepared for Example 3 (a) HER linear voltammetry (LSV) diagram and (b) OER LSV diagram. It can be seen from figure (a) that when the current density of the electrode is 10mA / cm 2 , the overpotential required for HER reaction to produce hydrogen in alkaline aqueous solution is only 70mV; when the current density is 100mA / cm 2 When the corresponding overpotential is only 142mV; when the current density is 400mA / cm 2 , the corresponding overpotential is only 212mV. This reflects the excellent catalytic hydrogen evolution performance of the material. It can be seen from the figure (b) that when the current density of the electrode is 10mA / cm 2 , the overpotential corresponding to OER reaction oxy...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention provides a dual-functional Co 1‑x S-MoS 2 ‑Nitrogen-doped carbon ternary composite material preparation method. Cobalt precursor arrays grown on carbon paper substrates were first obtained by chemical bath deposition, followed by oxidation and sulfidation to obtain cubic phase Co 9 S 8 array of nanorods. Dissolve molybdenum salt, bipyridine or o-phenanthroline, and carbon source in N,N-dimethylformamide solution to obtain Mo 5+ ‑N‑C precursor solution, and then apply the precursor solution until the growth of Co 9 S 8 On the substrate of the array structure and dry; with argon or nitrogen as the protective gas and carrier gas, and the liter S elemental powder as the solid evaporation source, the chemical vapor deposition reaction can obtain the hexagonal phase Co 1‑x S and MoS 2 and NC complex arrays. The product obtained by the technical scheme of the present invention has many advantages such as low equipment requirements, low cost of required raw materials, easy control of reaction conditions, simple production process, good consistency of formed products, and low environmental pollution, and can be used in multiple applications of HER and OER. Functional electrocatalysts.

Description

technical field [0001] The invention relates to the preparation of multi-component multifunctional materials, and its application belongs to the field of electrocatalysis and energy conversion materials and devices. Background technique [0002] In the 21st century, the environmental problems caused by the greenhouse effect are intensifying. The glaciers are receding, the climate zone is moving northward, the frequency of extremely hot weather is increasing, and the incidence of respiratory diseases is increasing. The large-scale emergence of these environmental problems has begun to make people seek a clean and sustainable new energy alternative to fossil fuels. Among them, hydrogen has the characteristics of high combustion calorific value, which is 3 times that of gasoline, 3.9 times that of alcohol, and 4.5 times that of coke. Moreover, the product of its combustion is water, which will not cause any harm to the environment. It is rich in resources, sustainable develop...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J27/24
CPCB01J27/24B01J35/0033
Inventor 黄妞骆禅杨柳李佳乐
Owner CHINA THREE GORGES UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More