Phosphorus removal material and preparation method thereof

A technology for raw materials and equipment, applied in the field of phosphorus removal materials and their preparation, to achieve the effects of improving adsorption performance, increasing stability and stable structure

Active Publication Date: 2021-11-02
神美科技有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there is no such foam material used in the application of water pollution treatment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Phosphorus removal material and preparation method thereof
  • Phosphorus removal material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Place natural microcrystalline graphite (average particle size of 50 μm), balls (diameter of 10-16 mm) and water in a zirconia ball mill tank at a mass ratio of 1:15:5, and grind the ball on a planetary ball mill at 500 r / min Rotate the ball mill for 24 hours, then take it out and dry it in an oven, pass through a 200-mesh sieve to obtain graphite powder.

[0033] Dissolve the obtained graphite powder in 15wt% copper sulfate solution according to the solid-to-liquid ratio of 1:8, and ultrasonically treat it at 100KHz for 5h, then filter and wash, and calcinate the obtained solid at 900°C for 2h at high temperature, and then cool it down to room temperature to give a solid product.

[0034] Mix the obtained solid product with polystyrene and polyvinyl chloride at a mass ratio of 1:1:1 and undergo a crosslinking reaction under the action of aluminum chloride. After the reaction is completed, the product is dried and placed in twin-screw extrusion Extrusion molding in the...

Embodiment 2

[0036] Put natural flake graphite (average particle size of 50 μm), grinding balls (diameter of 10-16 mm) and water in a zirconia ball mill tank at a mass ratio of 1:15:5, and rotate at 500 r / min on a planetary ball mill Ball mill for 24 hours, then take it out and dry it in an oven, pass through a 200-mesh sieve to obtain graphite powder.

[0037] Dissolve the obtained graphite powder in 15wt% copper sulfate solution according to the solid-to-liquid ratio of 1:5, and ultrasonically treat it at 100KHz for 5h, then filter and wash, and calcinate the obtained solid at 900°C for 2h, and then cool it down to room temperature to give a solid product.

[0038] Mix the obtained solid product with polystyrene and polyvinyl chloride at a mass ratio of 1:0.5:0.5 and undergo a crosslinking reaction under the action of aluminum chloride. After the reaction, the product is dried and placed in twin-screw extrusion Extrusion molding in the machine, the rotation speed of the twin-screw extru...

Embodiment 3

[0040] Put natural spherical graphite (average particle size of 50 μm), balls (diameter of 10-16 mm) and dodecane in a zirconia ball mill jar at a mass ratio of 1:15:5, and place them on a planetary ball mill at 500 r / Min speed ball milling for 24 hours, then take it out and dry it in an oven, pass through a 200-mesh sieve to obtain graphite powder.

[0041] Dissolve the obtained graphite powder in 15wt% copper sulfate solution according to the solid-to-liquid ratio of 1:10, and ultrasonically treat it at 100KHz for 5h, then filter and wash, and calcinate the obtained solid at 900°C for 2h at high temperature, and then cool it down to room temperature to give a solid product.

[0042] The obtained solid product is mixed with polystyrene and polyvinyl chloride at a mass ratio of 1:0.8:1 and cross-linked under the action of aluminum chloride. After the reaction is completed, the product is dried and placed in twin-screw extrusion Extrusion molding in the machine, the rotation sp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a phosphorus removal material, which is characterized by comprising the steps of 1) putting a graphite powder raw material, grinding balls and a ball milling medium into a ball milling tank according to a mass ratio of 1: (10-20): (4-6), carrying out ball milling on ball milling equipment for 24 hours at a rotating speed of 400-600r/min, then taking out, drying, and sieving with a 200-mesh sieve to obtain graphite powder; 2) dissolving the obtained graphite powder in a copper sulfate solution according to a solid-to-liquid ratio of 1: (5-10), carrying out ultrasonic treatment at 80-100KHz for 4-6 hours, then filtering and washing, carrying out high-temperature calcination on the obtained solid at the temperature of 800-1000 DEG C for 1-3 hours, and cooling to room temperature after the calcination is ended so as to obtain a solid product; and 3) mixing the obtained solid product with polystyrene and polyvinyl chloride according to a mass ratio of 1: (0.5-1): (0.5-1), carrying out a cross-linking reaction under the action of a catalyst, drying the product after the reaction is finished, and carrying out extrusion molding in a twin-screw extruder to obtain the phosphorus removal material. The material has an obvious removal effect on phosphorus and other pollutants in sewage.

Description

technical field [0001] The invention belongs to the technical field of sewage treatment, and in particular relates to a phosphorus removal material and a preparation method thereof. Background technique [0002] With the development of industry and agriculture and the growth of population, the production and consumption of chemical fertilizers, pesticides, and phosphorus-containing detergents have increased rapidly. Water eutrophication caused by water pollution has become increasingly serious. Water eutrophication has endangered agriculture, fishery, and tourism. It also poses a huge threat to drinking water sanitation and food safety. The main nutrients that cause water eutrophication include organic carbon, nitrogen, phosphorus, potassium, etc. Organic carbon in sewage can be basically removed after general biological treatment, and the content of other components other than nitrogen and phosphorus is relatively The demand in the process is extremely low and will not be ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/08C04B38/08C04B20/10C02F1/58C02F1/28C02F101/10C02F101/16C04B111/74
CPCC04B26/08C02F1/58C02F1/586C02F1/283C04B20/107C02F2101/105C02F2101/16C04B2111/74C04B14/024C04B24/2676C04B38/08C04B20/04
Inventor 柯建怡周继柱祖利朝张志平付雪玲
Owner 神美科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap