Treatment process method for reinforcing wet wicker for weaving

A treatment process and wicker technology, which is applied in the field of treatment technology for weaving with moist wicker reinforcement, can solve the problems of formaldehyde pollution, complex process, poor resin application effect, etc., and achieve the effect of heat resistance reinforcement

Pending Publication Date: 2021-12-14
阜南佳利工艺品股份有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese patent CN108789732A discloses a method for strengthening and modifying rattan materials. It is also common to use impregnation and modification of wood fibers such as wood by using an impregnation solution containing melamine-modified urea-formaldehyde resin rubber powder and cyclodextrin. , pressure impregnation, complex process, melamine-formaldehyde resin is insoluble in water, and there is a risk of formaldehyde pollution
Branch processing includes three items of peeling, drying and dyeing. Chinese patent CN108748502A discloses steam explosion treatment and pressure dipping treatment. The impregnating liquid enters the inside of the wicker or treats the inside of the wicker in order to combine with the lipophilic macromolecular resin, but because of the polarity difference and complex process and resin application effect is not good, with the rapid development of modern wicker craft products, traditional The wicker produced by the technology cannot meet the requirements of heat-resistant and high-strength performance, which seriously limits the scope and function of the wicker handicraft.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Qi Liu (Salirintegra Thunb), is a deciduous shrub of the Salicaceae Salix genus, also known as red-skinned willow, willow wicker, dustpan willow and so on. First of all, the two-year-old willow with big white skin in Huanggang Township, Funan, Fuyang was selected, and it was cut smoothly at 7 o'clock in the morning when the weather was sunny after the rain in the middle and late July (adjusted to a moisture content of 12%, and a density of 0.458kg / cm 3 , along the grain compressive strength 329.4kg / cm 2 , Bending strength 589.6.kg / cm 2 ), cut the freshly picked qi wicker with thick and thin ends, keep the complete wicker bark of the wet wicker, keep the cross-section of the wet wicker ends fresh, and place the wicker horizontally on the platform; secondly, static pressure replacement: water-soluble silicone enhancement solution It consists of potassium methyl silicate 13phr, phenyl sodium silicate 8phr, calcium chloride 0.2phr, calcium fluorosilicate 0.2phr, chromium p...

Embodiment 2

[0030] Dry willow (Salixmatsudana Koidz) has soft branches and a plump crown. It is a commonly used shade tree and street tree in the north. Dry willow wood is tough, beautiful in pattern, soft in color, simple and elegant. First of all, choose a 10-year-old, 12-meter-high, 25-cm steamed willow stick in Zhonggang, Funan, Fuyang, and cut freshly picked dry willow sticks (adjusted to a moisture content of 12% and a density of 0.598 kg / cm 3 , along the grain compressive strength 403.5kg / cm 2 , Bending strength 891.3kg / cm 2 ), keep the complete wicker skin of the wet wicker, keep the cross-sections of the wet wicker fresh, and place the wicker horizontally on the platform; secondly, static pressure replacement: the water-soluble organic silicon enhancement liquid is composed of potassium methyl silicate 15phr in parts by weight, Sodium phenylsilicate 11phr, calcium chloride 0.4phr, calcium fluorosilicate 0.3phr, potassium chromium sulfate 0.3phr, water 63, the water is heated to...

Embodiment 3

[0032] Weeping willow (Salixbabylonica) is a deciduous tree with slender, soft and drooping willow branches. It is a native tree species in my country, the earliest recorded artificial cultivation tree species in China, and one of the most widely distributed plants. It likes wetlands and grows rapidly. First, choose the asexual green-skinned weeping willow sticks with a height of 8m and a breast height of 15cm in Zhonggang, Funan, Fuyang, and cut freshly picked weeping willow sticks (adjusted to a water content of 12% and a density of 0.466g / cm 3 , but the compressive strength along the grain is 327.2kg / cm 2 , The bending strength is 789.4kg / cm 2 ), keep the complete wicker bark of the wet wicker, keep the cross section of the wet wicker both ends fresh, and place the wicker horizontally on the platform; secondly, static pressure replacement: the water-soluble organic silicon enhancement solution is composed of potassium methyl silicate 14 in parts by weight 9 parts, 9 parts ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Compressive strengthaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a treatment process method for reinforcing wet wickers for weaving, and belongs to the technical field of wickers. The wickers in the wet state, namely fresh wickers, are directly utilized, peeling, drying and liquid soaking are not needed in the reinforcing process, reinforcing liquid is directly injected in a reinforcing liquid injection and replacement mode, by means of the short-time biological characteristics of the cut wickers, the reinforcing liquid enters the wickers, the reinforcing effect is achieved through dry ice freezing and shaping storage, and in the process, molds can be adopted for shaping, and structures of different shapes are achieved. In the prior art, the shape of the wickers is changed by adopting fire-forced bending and box making, the method disclosed by the invention can also realize lower-requirement and more convenient wicker modeling, the weaving wickers have the effects of improving mechanical strength, increasing weight and preventing water after being subjected to enhanced liquid-liquid treatment, the wicker is not easy to deform, the treatment process is simple and convenient, and the obtained wet wickers has the advantages of high mechanical strength, high heat resistance, high corrosion resistance, high hardness and high specific gravity.

Description

technical field [0001] The invention belongs to the technical field of willow weaving, and in particular relates to a treatment method for reinforcing wet wicker for weaving. Background technique [0002] Wicker is a relatively light material with high mechanical strength, wide variety, wide distribution, low price, easy processing, good impact resistance and shock resistance, low thermal conductivity, small thermal expansion coefficient, and electric power in dry state. The green performance is very high, the connection and installation of parts and structures is simple, the disassembly is relatively easy, and it can resist weak corrosive media, so it has been used to prepare materials for a long time to meet the needs of various industrial production. Despite the advantages of natural wicker as described above, it also has a number of serious disadvantages. Such as: not resistant to strong corrosive media, hygroscopic, easy to crack after drying, flammability and limited ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B27K9/00B27K3/08B27K3/36B27K5/04B27K5/00
CPCB27K9/002B27K3/08B27K3/36B27K5/04B27K5/0005
Inventor 徐学进
Owner 阜南佳利工艺品股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products