Full biological degradable composition and its preparing method and use

A biodegradable and fully biological technology, applied in the field of fully biodegradable compositions and their preparation and application, can solve the problems of high production cost, low starch content, large investment in equipment, etc., and achieve good biodegradability and complete biodegradability , the effect of excellent mechanical properties

Inactive Publication Date: 2005-10-19
CHENDU NEW KELI CHEM SCI CO LTD
View PDF4 Cites 47 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] In addition, due to the use of single-component polyester or low starch content in it, large investment in equipment, high production costs, long flow of materials in the traditional screw extruder, high energy consumption, and the adaptability of processed materials The limited performance makes the cost of raw materials of products much higher than that of ordinary plastic products of the same kind, and limits the performance of fully biodegradable plastics, which is unsatisfactory.
These have seriously restricted the large-scale production and application of fully biodegradable plastics.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] The weight composition of each component raw material:

[0045] Modified corn starch 80.0 parts

[0046] Polycaprolactone 20.0 parts

[0047] Calcium carbonate (50nm) 5.5 parts

[0048] Glycerin 6.0 parts

[0049] Stearic acid amide 4.0 parts

[0050] Dodecyl maleic anhydride 2.5 parts

[0051] Vinyltrimethoxysilane 1.0 parts

[0052]Linoleic acid / modified starch composition (10 / 60) 1.8 parts

[0053] Steps:

[0054] The cornstarch was dried at normal temperature and pressure to a moisture content of 1.5%. Add 1.0% (weight) modifier calcium stearate to the dried cornstarch, mix well and refine to 2200 mesh. Then take modified cornstarch and glycerin according to the above ratio and mix them evenly in a high-speed mixer at a speed of 1000r / min for 15 minutes, then add the biodegradable polymer polycaprolactone and stearic acid amide in sequence according to the above ratio ,well mixed. The rotating speed is 1200r / min, the time is 12 minutes, and the temperature...

Embodiment 2

[0061] The weight composition of each component:

[0062] Modified tapioca starch 75.0 parts

[0063] Polylactic acid 60 parts

[0064] Clay (60nm) 3.6 parts

[0065] Butanediol 8.0 parts

[0066] 2.4 parts of methylene bis stearamide

[0067] Maleic anhydride grafted polycaprolactone 0.8 parts

[0068] Cyclohexyldimethoxysilane 1.5 parts

[0069] Linolenic acid / tapioca starch composition (25 / 80) 2.0 parts

[0070] Tapioca starch was dried under reduced pressure (-0.06MPa) at 50°C to a moisture content of 5%. Add 2.5% (weight) modifying agent stearic acid in the tapioca starch after drying, refine to 2500 orders after mixing. Then take the modified tapioca starch and butanediol according to the above ratio and mix them evenly in a high-speed mixer at a speed of 1500r / min for 10 minutes, then add the biodegradable polymer polylactic acid and methylene bishard in sequence according to the above ratio. Fatty amide, mix well. The rotating speed is 1500r / min, the time is 1...

Embodiment 3

[0077] The weight composition of each component:

[0078] Modified pea starch 20 parts

[0079] 50 parts polyvinyl alcohol

[0080] Montmorillonite (30nm) 3.0 parts

[0081] Sorbitol 5.5 parts

[0082] Ethylene bis stearamide 6.0 parts

[0083] Hydroxyl-modified polyethylene terephthalate (PET) 0.5 part

[0084] Epoxy silane 3.0 parts

[0085] Phosphite / modified starch composition (40 / 90) 2.5 parts

[0086] Pea starch was dried at 150°C and reduced pressure (-0.002MPa) to a moisture content of 10%. Add 4.0% (weight) modifier sodium stearate to the dried pea starch, mix well and refine to 3000 mesh. Then take the modified pea starch and sorbitol according to the above ratio and mix them evenly in a high-speed mixer at a speed of 3000r / min for 5 minutes, then add the biodegradable polymer polyvinyl alcohol and ethylene bisstearate in sequence according to the above ratio amide, mix well. The rotating speed is 2000r / min, the time is 10 minutes, and the temperature is 30°...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Tensile strengthaaaaaaaaaa
Tensile strengthaaaaaaaaaa
Tensile modulus of elasticityaaaaaaaaaa
Login to View More

Abstract

The fully biodegradable composition consists of modified starch, biodegradable polymer, nanometer reinforcer, plasticizer, lubricant, reactive bulking agent, crosslinking agent and biodegradation promoter. The preparation process includes drying starch and fining modification and plasticizing treatment, mixing with supplementary material, and extrusion and pelletizing in reciprocating single-screw extruder and electric mixer. The composition is completely biodegradable, has high adaptability, easy use, wide use range and low cost, and may be used directly as resin or mixed with other resin.

Description

Technical field [0001] The present invention relates to a completely biodegradable composition, as well as a preparation method and use of the composition. Specifically, it is a fully biodegradable composition using starch and biodegradable polymers as basic and main raw materials and its preparation method and use. Background technique [0002] In the current increasingly widespread use of plastic materials and products, as well as the environmental protection problems caused by the traditional plastic industry and the resource shortage problems based on the petroleum industry, out of considerations of environmental protection and the search for alternative resources and resource recycling, research and The application of biodegradable materials has become an inevitable trend and focus in the development of the plastics industry. [0003] The development of degradable plastics has generally gone through two stages: the first stage is the stage of photodegradable plastics a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08K5/54C08L3/02C08L29/04C08L67/04C08L75/04
Inventor 陈庆郭林陈兵杨欣宇
Owner CHENDU NEW KELI CHEM SCI CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More