A kind of battery diaphragm and preparation method thereof

A battery diaphragm and diaphragm technology, applied in the field of power battery diaphragm and its preparation, can solve the problem of high closed cell temperature, poor piercing tensile strength, battery diaphragm air permeability, high temperature membrane rupture of polyvinylidene fluoride non-woven diaphragm Problems such as unsatisfactory temperature

Active Publication Date: 2015-09-30
BYD CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the technical problems of unsatisfactory air permeability and high-temperature membrane rupture temperature of the existing battery diaphragm, excessively high closed cell temperature of the polyvinylidene fluoride non-woven diaphragm, and poor piercing tensile strength, the present invention provides a battery with high air permeability, closed cell Novel battery separator with better performance in terms of pore temperature, high temperature rupture temperature and tensile strength, and preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0024] The present invention also provides a method for preparing a battery diaphragm, comprising the following steps:

[0025] (a) mixing ultra-high molecular weight polyethylene and linear low-density polyethylene, placing them in a second solvent after mixing, heating and stirring to dissolve, and obtaining a mixed solution;

[0026] (b) Coating the mixed solution on both sides of the polyvinylidene fluoride nonwoven fabric to obtain a coated membrane;

[0027] (c) Stretching the coated membrane to obtain a stretched membrane;

[0028] (d) heat-setting the stretched membrane to obtain a separator;

[0029] The second solvent is a good solvent for polyolefin, which refers to a solvent close to the polarity of polyolefin, preferably, selected from decahydronaphthalene, kerosene, benzene, toluene, chloroform, ether, trichloroethylene, paraffin or liquid paraffin one or more.

[0030] In the preparation method of the battery separator provided by the present invention, prefe...

Embodiment 1

[0053] The diaphragm in this example is made through the following steps:

[0054] (s1) 4kg, weight average molecular weight is 3.7×10 5 1. Mix polyvinylidene fluoride with a molecular weight distribution of 2.4, 32kg N,N-dimethylformamide, and 4kg acetone, add it to a stirring tank, heat up to 60°C at a stirring rate of 50r / min, heat and stir for 1h, and ultrasonically Degassing and standing for 2h to obtain polyvinylidene fluoride spinning solution;

[0055] (s2) Inject the spinning liquid obtained in (s1) into the tee pipe in the high-voltage electrospinning device, connect the spinneret to the anode output end of the high-voltage power supply, connect the cathode output end to the metal receiving plate, and turn on the high-voltage power supply 13KV , preheat for 30min, adjust the spinning voltage and the distance between the spinneret and the metal receiving plate to 15cm, start spinning to form fiber aggregates similar to non-woven fabrics, and then reinforce and compac...

Embodiment 2

[0064] The difference from Example 1 is that in step (s2), the high-voltage power supply is 20KV, and the thickness of the prepared non-woven fabric is 26 μm. The obtained separator is designated as S2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

A battery separator and a method for preparing the same are provided. The battery separator comprises: a substrate which is a polyvinylidene fluoride non-woven fabric; and a coating layer formed on each surface of the substrate, in which the material of the coating layer comprises an ultra-high molecular weight polyethylene and a linear low density polyethylene.

Description

technical field [0001] The invention relates to a battery separator, in particular to a separator for a power battery and a preparation method thereof. Background technique [0002] Lithium ion secondary battery is a kind of battery with extremely high energy density, but there is a danger of explosion due to short circuit. In lithium-ion secondary batteries, the separator is mainly used for the conduction of lithium ions, and separates the positive and negative electrodes inside the battery from each other, so as to prevent battery self-discharge and short-circuit of the two poles, and play a certain role in safety protection. The thermal stability, permeability, porosity, and film thickness of the separator all have an important impact on the performance of the battery. [0003] In recent years, the application of lithium-ion secondary batteries has been extended to fields such as hybrid electric vehicles, and the thermal stability requirements for separators are becoming...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M2/16B32B27/08B32B27/30B32B27/32H01M50/417H01M50/426H01M50/454H01M50/457H01M50/489H01M50/491
CPCH01M2/1653H01M10/0525Y02T10/7011H01M2/1686H01M2/162Y02E60/10H01M50/417H01M50/454H01M50/457H01M50/491H01M50/489H01M50/426H01M50/44
Inventor 林妙云尤臻于伟成罗明俊刘会权
Owner BYD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com