Biological nano plastic

A technology of bio-nano and biodegradable plastics, applied in the field of bio-nano-plastics, can solve the problems of weak two-phase interface affinity, application limitations of composite materials, and decline in mechanical properties. The effect of high production efficiency

Active Publication Date: 2014-01-29
SUZHOU XIANGYUAN SPEICAL FINE CHEM
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Talc powder filled PP composite materials have been widely used in the production of automotive parts and daily necessities. Compared with PP without talc powder, its products have good appearance quality, low shrinkage and higher heat distortion temperature. However, due to The affinity of the two-phase interface is not strong, and the direct filling of talc powder often leads to the decline of some mechanical properties, which limits the application of composite materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A biodegradable plastic, characterized in that: its raw material components and parts by weight are respectively:

[0039] Vegetable fiber starch 45-60,

[0040] Glycerin 4-6

[0041] Polyethylene 40

[0042] Polylactic acid 20-40

[0043]Synthetic resin 60-80

[0044] Auxiliary 10-15

[0045] Pullulan 5-8

[0046] Antioxidant 2-4

[0047] UV absorber 1-1.5

[0048] Nano Flame Retardant Compound 25

[0049] The preparation method of described nano flame retardant composite agent is:

[0050] (1) The silicon hydroxyapatite, red phosphorus, attapulgite, hydrotalcite, montmorillonite, titanium dioxide, calcite, kaolin according to 25-35: 15-20: 10-15: 10-15: 8-10: 8-10: 7-8: 5-7 parts by mass, mixed, added to a mixed solution of 200 parts of dimethyl sulfoxide (DMSO) and 50 parts of methanol, stirred at 65°C for 60 hours, filtered, and used 60 Wash with hot ethanol at ℃ for 3 times to remove excess dimethylsulfoxide (DMSO), put it in a vacuum drying oven, dry at ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses a biological nano plastic, which is characterized in that the plastic comprises the following raw material components in parts by weight: 45-60 parts of plant fiber starch, 4-6 parts of glycerine, 40 parts of polyethylene, 20-40 parts of a polylactic acid, 60-80 parts of synthetic resin, 10-15 parts of additives, 5-8 parts of Pulullan, 2-4 parts of an antioxidant, 1-1.5 parts of an ultraviolet light absorber, and the like.

Description

technical field [0001] The invention relates to a plastic film, in particular to a bionano plastic. Background technique [0002] As a general-purpose plastic, polypropylene has many excellent properties, but due to defects such as low mechanical strength, poor heat resistance, large shrinkage deformation, and poor creep resistance, its application, especially as a structural material, is greatly restricted. It cannot be used as a high-performance engineering plastic. Therefore, modifying polypropylene and engineering it has become an important research topic. [0003] Talc powder is a mineral composed of layered silicate crystals, PP filled with talc powder has good heat resistance, low shrinkage, good dimensional stability and high hardness. Talc powder filled PP composite materials have been widely used in the production of automotive parts and daily necessities. Compared with PP without talc powder, its products have good appearance quality, low shrinkage and higher he...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L3/02C08L23/06C08L67/04C08L101/00C08L5/00C08K13/06C08K3/34C08K3/02C08K3/22C08K5/053
Inventor 周建颜玉荣
Owner SUZHOU XIANGYUAN SPEICAL FINE CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com