Firebrick dust-containing aerated building block and making method thereof

A technology for aerated blocks and refractory bricks, which is applied in the directions of climate sustainability, sustainable waste treatment, solid waste management, etc. The effect of improving fire resistance, thermal insulation and wide source of raw materials

Inactive Publication Date: 2016-01-27
MAANSHAN JIECHUANG PLASTIC TECH CO LTD
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the rapid development of my country's construction industry and the continuous improvement of people's living standards, the performance requirements for aerated blocks are getting higher and higher. However, the comprehensive performance of traditional aerated blocks is increasingly unable to meet market demand. Therefore, there is an urgent need for Development of an aerated block with excellent comprehensive performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] An aerated block added with refractory brick slag, made of the following raw materials in weight (kg): calcium silicate slag 17, refractory brick slag 29, Portland cement 33, coal gangue 26, anorthite 22, Porous ceramsite 26, flue ash 38, locust bean gum 9, boron slag 13, blast furnace water quenching slag 24, sodium tripolyphosphate 6, silicon aluminum alloy powder 3.5, sodium peroxide 1.5, appropriate amount of water;

[0016] The preparation method of described porous ceramsite is as follows: a, take manganese ore tailings, yellow phosphorus slag, broken glass by mass ratio 7:6:5, mix uniformly, pulverize, cross 500 mesh sieves; b, by mass ratio 9 :7:4 Weigh fly ash, cancryptite and magnesite, mix uniformly, pulverize, pass through a 300 mesh sieve, add water equivalent to 5 times the weight of the mixed powder, wet ball mill for 2.5h, and dry; c 1. Add 36% pulp waste liquid, 8% ammonium bicarbonate and 4.5% sodium bisulfate, which are equivalent to 36% of the weight...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
flame retardantaaaaaaaaaa
Login to View More

Abstract

The invention discloses a firebrick dust-containing aerated building block and a making method thereof. The aerated building block is made from, by weight, 12-23 parts of silicon-calcium slag, 24-37 parts of firebrick dusts, 26-39 parts of Portland cement, 19-35 parts of gangue, 14-26 parts of anorthite, 18-32 parts of porous ceramsite, 28-42 parts of flue dust, 6-12 parts of locust bean gum, 10-15 parts of boron slag, 16-28 parts of blast furnace water quenching slag, 4-8 parts of sodium tripolyphosphate, 3-4 parts of silicon-aluminum alloy powder, 1-2 parts of sodium peroxide and a proper amount of water. The firebrick dusts added in the invention cooperate with gangue, anorthite and silicon-calcium slag to improve the mechanical performances, the acid and alkali corrosion resistance and the weatherability of the aerated building block, and cooperate with the porous ceramsite, the boron slag and the blast furnace water quenching slag to improve the fire resistance and the heat insulation property of the aerated building block. The aerated building block made in the invention has the advantages of excellent comprehensive performances, excellent mechanical performances, excellent weatherability, excellent acid and alkali corrosion resistance, excellent ageing crack resistance, excellent heat insulation property and excellent fire resistance.

Description

technical field [0001] The invention relates to an aerated block added with refractory brick slag and a preparation method thereof, belonging to the field of building materials. Background technique [0002] Aerated block is a new type of wall material that saves energy, saves soil, and makes use of waste. It is widely used in various civil and public buildings because of its advantages such as the usable area of ​​buildings. With the rapid development of my country's construction industry and the continuous improvement of people's living standards, the performance requirements for aerated blocks are getting higher and higher. However, the comprehensive performance of traditional aerated blocks is increasingly unable to meet market demand. Therefore, there is an urgent need for To develop an aerated block with excellent comprehensive performance. Contents of the invention [0003] The object of the present invention is to provide an aerated block added with refractory bri...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B18/16C04B18/12C04B18/08C04B22/04
CPCY02W30/91
Inventor 吴传兴
Owner MAANSHAN JIECHUANG PLASTIC TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products